The influence of fluorine on the structure of CaO Si（）e-Al2Oa Na2O-CaF2 continuous-casting-type slag was measured by Raman spectroscopy, and the degree of polymerization of mould flux and the structural behavior of ...The influence of fluorine on the structure of CaO Si（）e-Al2Oa Na2O-CaF2 continuous-casting-type slag was measured by Raman spectroscopy, and the degree of polymerization of mould flux and the structural behavior of F- in the melt were investigated by classifying and quantifying the structural species of F ions. The results exhibit that the main structural units of Si O tetrahedra are Q1, Q1 and Q2, and the actual measured number of non bridging oxygen ions in the [SiO4 ]-tetrahedra （denoted by NBO/T） in creases from 2. 73 to 3.44 with increasing the molar ratio of F to （F＋O） （denoted by XF/X（F-O ） from 0.06 to 0. 19. It means that the degree of polymerization o1 meh structure decreases with an increase in XE/X（F＋O）. In addition, most of F- ions were distributed in Si-O tetrahedra and Al-O tetrahedra. With increasing XF/X（F＋O）, the complex structural units Al-Otetrahedra are gradually replaced hy discrete structural units A1F4 because of the breakage of Al-O bonds in Al-Otetrahedra by F ions, and the SiO （bridging oxygen） bonds of SiO tetrahedra are broken to form [SiOnF1-n]-tetrahedra by F ions coordinating with Si4 ＋ .展开更多
基金the National Natural Science Foundation of China for providing financial support(Nos.51374060 and 51374059)
文摘The influence of fluorine on the structure of CaO Si（）e-Al2Oa Na2O-CaF2 continuous-casting-type slag was measured by Raman spectroscopy, and the degree of polymerization of mould flux and the structural behavior of F- in the melt were investigated by classifying and quantifying the structural species of F ions. The results exhibit that the main structural units of Si O tetrahedra are Q1, Q1 and Q2, and the actual measured number of non bridging oxygen ions in the [SiO4 ]-tetrahedra （denoted by NBO/T） in creases from 2. 73 to 3.44 with increasing the molar ratio of F to （F＋O） （denoted by XF/X（F-O ） from 0.06 to 0. 19. It means that the degree of polymerization o1 meh structure decreases with an increase in XE/X（F＋O）. In addition, most of F- ions were distributed in Si-O tetrahedra and Al-O tetrahedra. With increasing XF/X（F＋O）, the complex structural units Al-Otetrahedra are gradually replaced hy discrete structural units A1F4 because of the breakage of Al-O bonds in Al-Otetrahedra by F ions, and the SiO （bridging oxygen） bonds of SiO tetrahedra are broken to form [SiOnF1-n]-tetrahedra by F ions coordinating with Si4 ＋ .