Quantitative research on the heat affected zone of weave bead welding for Invar alloy

Quantitative research on the heat affected zone （ HAZ） o f weave bead welding （ WBW） joint fo r Invar alloy is carried out in this paper. Based on the morphology and related data analysis of the weld seam, the width difference o f each layer and the forming mechanism are analyzed. Results show that the bottom layer （ Layer 1 ） has the widest HAZ and the smallest fluctuation, which reaches 1 200 ｜jLm. HAZ width o f layer 2 to 5 is relatively narrower which is basically below 600 jjim, while the amplitude fluctuation is greater. The main reason lies in the welding path. The long straight welding without weave causes the base metal near the groove fully melts which causes by the long straight welding without weave, while welding with weave leads to the uneven and inadequate melting of metal near groove.

船体厚板高效气电立焊焊接技术的研究

针对集装箱船设计与建造关键技术研究的厚板焊接技术焊接状况,研制开发高效气电立焊焊接技术及自动化焊接设备,实现了EH36级δ=60mm厚板立缝的一次焊接成形技术,对提高我国集装箱船设计与建造及各种钢结构厚板焊接制造施工工艺,提高焊接质量和生产率,减轻工人劳动强度具有重要意义。

厚板Invar钢多层多道焊与多层摆动焊效率与接头质量对比分析

对19 mm厚Invar钢板进行多层多道焊和多层摆动焊对接试验,计算分析了这两种工艺的功耗和效率,并通过观察和测量Invar钢焊件的金相组织和显微硬度以比较两种焊接方法的焊接接头质量。结果表明,在连接厚板Invar钢时,由于多层摆动焊焊道数少于多层多道焊焊道数,多层摆动焊所用焊接时间较少、效率更高、功耗更少;多层摆动焊的层间重熔区熔合良好,而多层多道焊接接头处观察到明显的未熔合缺陷;多层摆动焊的热影响区宽度远小于多层多道焊;多层摆动焊的平均晶粒尺寸及显微硬度均略大于多层多道焊。

Invar钢多层摆动焊接过程的数值模拟

以19. 05 mm厚Invar钢板作为研究对象,通过研究Invar钢的多层摆动焊接,得到多层摆动MIG焊焊缝。利用建模软件建立和实际焊缝一致的有限元模型并进行分析计算,得出焊接过程中温度场的变化过程,对瞬时温度场和焊接热循环曲线进行分析,得出焊接过程中试样整体温度场的变化过程。结果表明,焊接时间越长,焊接速度越慢,熔池尺寸越大;热循环曲线的斜率代表该点温度变化的速率,斜率越大,温度变化速率越快,相对的,热循环曲线随着热源靠近发生剧烈地变化,远离热源变化平缓;直线焊接的热循环曲线为一条平滑的曲线,摆动焊接的热循环曲线为一系列均匀摆动的折线,折线摆动的频率与焊枪摆动的频率一致。