Soil microbial communities are pivotal in permafrost biogeochemical cycles,yet the variations of abundant and rare microbial taxa and their impacts on greenhouse gas emissions in different seasons,remain elusive,espec...Soil microbial communities are pivotal in permafrost biogeochemical cycles,yet the variations of abundant and rare microbial taxa and their impacts on greenhouse gas emissions in different seasons,remain elusive,especially in the case of soil archaea.Here,we conducted a study on soil abundant and rare archaeal taxa during the growing and non-growing seasons in the active layer of alpine permafrost in the Qinghai-Tibetan Plateau.The results suggested that,for the archaeal communities in the sub-layer,abundant taxa exhibited higher diversity,while rare taxa maintained a more stable composition from the growing to non-growing season.Water soluble organic carbon and soil porosity were the most significant environmental variables affecting the compositions of abundant and rare taxa,respectively.Stochastic and deterministic processes dominated the assemblies of rare and abundant taxa,respectively.The archaeal ecological network influenced N_(2)O flux through different modules.Rare taxa performed an essential role in stabilizing the network and exerting important effects on N_(2)O flux.Our study provides a pioneering and comprehensive investigation aimed at unravelling the mechanisms by which archaea or other microorganisms influence greenhouse gas emissions in the alpine permafrost.展开更多
The morphology and the formation of Y2BaCuO5 phase in powder melting processed YBa2Cu3O7-x superconductors were investigated. The experimental results show the heat treatment can not change the shape of Y2BaCuO5 parti...The morphology and the formation of Y2BaCuO5 phase in powder melting processed YBa2Cu3O7-x superconductors were investigated. The experimental results show the heat treatment can not change the shape of Y2BaCuO5 particles in powder melting processed samples. The formation of round Y2BaCuO5 phase is due to relative content of each constitution of precursor powders in powder melting process. For powder melting process, the excessive liquid phase is eliminated, which restrains the preferred growth of Y2BaCuO5 particles.展开更多
The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymeri...The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.展开更多
YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respect...YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respectively. The effect of the Ag content on superconducting crictical transition temperature of YBa2Cu3O7-δ-Agx was not evident as long as YBa2Cu3O7-δ-Agx can form continuous network. But Ag can increase superconduction crictical current and density of the composite superconductors. The normal state (i.e. non-superconducting state at room temperature) resistivity shows a percolation threshold at 20%-30% Ag, whereas the superconducting net-work shows a percolationthreshold at 70% -80% Ag.展开更多
In-situ HVEM observation on phase transition of the YBa_2Cu_3O_(7-x) superconducting compound in pro- cess of heating was carried out,and high temperature X-ray diffraction analysis in air and X-ray diffraction phase ...In-situ HVEM observation on phase transition of the YBa_2Cu_3O_(7-x) superconducting compound in pro- cess of heating was carried out,and high temperature X-ray diffraction analysis in air and X-ray diffraction phase analysis for the sample treated in vacuum condition were made.The results showed that the temperature of phase transition is related to oxygen content in the sample and in general,is 100℃ to 120℃ lower in vacu- um condition than in air.At 320℃ to 350℃ twin bands begin to disappear,and some Cu_2O are formed on the surface of the sample and transit from orthorhombic YBa_2Cu_3O_(7-x) to arthorhombic Y_2BaCuO_5 compound. This transition was completed at about 500℃.Above 900℃,this compound consists of the Y_2BaCuO_5, BaCuO_2,Y_2O_3 and some other minor compounds.No phase transition was observed during cooling the sample.展开更多
The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The r...The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.展开更多
The layered Li[Ni1/3Mn1/3Co1/3]O2 was separately synthesized by pretreatment process of ball mill method and solution phase route, using [Ni1/3Co1/3Mn1/3]3O4 and lithium hydroxide as raw materials. The physical and el...The layered Li[Ni1/3Mn1/3Co1/3]O2 was separately synthesized by pretreatment process of ball mill method and solution phase route, using [Ni1/3Co1/3Mn1/3]3O4 and lithium hydroxide as raw materials. The physical and electrochemical behaviors of Li[Ni1/3Mn1/3Co1/3]O2 were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, field emission scanning electron microscopy （FESEM） and electrochemical charge/discharge cycling tests. The results show that the difference in pretreatment process results in the difference in compound Li[Ni1/3Co1/3Mn1/3]O2 structure, morphology and the electrochemical characteristics. The Li[Ni1/3Mn1/3Co1/3]O2 prepared by solution phase route maintains the uniform spherical morphology of the [Ni1/3Co1/3Mn1/3]3O4, and it exhibits a higher capacity retention and better rate capability than that prepared by ball mill method. The initial discharge capacity of this sample reaches 178 mA-h/g and the capacity retention after 50 cycles is 98.7% at a current density of 20 mA/g. Moreover, it delivers high discharge capacity of 135 mA-h/g at a current density of 1 000 mA/g.展开更多
基金This work was supported by Gansu Provincial Science and Technology Program(22ZD6FA005)"Light of the West"Cross-team Project of the Chinese Academy of Sciences(xbzgzdsys-202214)+1 种基金the National Natural Science Foundation of China(41871064)Qinghai Province High-level Innovative"Thousand Talents"Program.
文摘Soil microbial communities are pivotal in permafrost biogeochemical cycles,yet the variations of abundant and rare microbial taxa and their impacts on greenhouse gas emissions in different seasons,remain elusive,especially in the case of soil archaea.Here,we conducted a study on soil abundant and rare archaeal taxa during the growing and non-growing seasons in the active layer of alpine permafrost in the Qinghai-Tibetan Plateau.The results suggested that,for the archaeal communities in the sub-layer,abundant taxa exhibited higher diversity,while rare taxa maintained a more stable composition from the growing to non-growing season.Water soluble organic carbon and soil porosity were the most significant environmental variables affecting the compositions of abundant and rare taxa,respectively.Stochastic and deterministic processes dominated the assemblies of rare and abundant taxa,respectively.The archaeal ecological network influenced N_(2)O flux through different modules.Rare taxa performed an essential role in stabilizing the network and exerting important effects on N_(2)O flux.Our study provides a pioneering and comprehensive investigation aimed at unravelling the mechanisms by which archaea or other microorganisms influence greenhouse gas emissions in the alpine permafrost.
基金Funded by the National Natural Science Foundation of China (50432050)the National High Technology Research and Development Program of China(2007AA03Z241)
文摘The morphology and the formation of Y2BaCuO5 phase in powder melting processed YBa2Cu3O7-x superconductors were investigated. The experimental results show the heat treatment can not change the shape of Y2BaCuO5 particles in powder melting processed samples. The formation of round Y2BaCuO5 phase is due to relative content of each constitution of precursor powders in powder melting process. For powder melting process, the excessive liquid phase is eliminated, which restrains the preferred growth of Y2BaCuO5 particles.
文摘The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.
文摘YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respectively. The effect of the Ag content on superconducting crictical transition temperature of YBa2Cu3O7-δ-Agx was not evident as long as YBa2Cu3O7-δ-Agx can form continuous network. But Ag can increase superconduction crictical current and density of the composite superconductors. The normal state (i.e. non-superconducting state at room temperature) resistivity shows a percolation threshold at 20%-30% Ag, whereas the superconducting net-work shows a percolationthreshold at 70% -80% Ag.
文摘In-situ HVEM observation on phase transition of the YBa_2Cu_3O_(7-x) superconducting compound in pro- cess of heating was carried out,and high temperature X-ray diffraction analysis in air and X-ray diffraction phase analysis for the sample treated in vacuum condition were made.The results showed that the temperature of phase transition is related to oxygen content in the sample and in general,is 100℃ to 120℃ lower in vacu- um condition than in air.At 320℃ to 350℃ twin bands begin to disappear,and some Cu_2O are formed on the surface of the sample and transit from orthorhombic YBa_2Cu_3O_(7-x) to arthorhombic Y_2BaCuO_5 compound. This transition was completed at about 500℃.Above 900℃,this compound consists of the Y_2BaCuO_5, BaCuO_2,Y_2O_3 and some other minor compounds.No phase transition was observed during cooling the sample.
基金Project(2012AA030311)supported by the National High-tech Research and Development Program of ChinaProject(2010BB4074)supported by the Natural Science Foundation of Chongqing Municipality,ChinaProject(2010ZD-02)supported by the State Key Laboratory for Advanced Metals and Materials,China
文摘The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.
基金Project(20871101)supported by the National Natural Science Foundation of ChinaProject(2009WK2007)supported by Key Project of Science and Technology Department of Hunan Province,ChinaProject(CX2009B133)supported by Colleges and Universities in Hunan Province Plans to Graduate Research and Innovation,China
文摘The layered Li[Ni1/3Mn1/3Co1/3]O2 was separately synthesized by pretreatment process of ball mill method and solution phase route, using [Ni1/3Co1/3Mn1/3]3O4 and lithium hydroxide as raw materials. The physical and electrochemical behaviors of Li[Ni1/3Mn1/3Co1/3]O2 were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, field emission scanning electron microscopy （FESEM） and electrochemical charge/discharge cycling tests. The results show that the difference in pretreatment process results in the difference in compound Li[Ni1/3Co1/3Mn1/3]O2 structure, morphology and the electrochemical characteristics. The Li[Ni1/3Mn1/3Co1/3]O2 prepared by solution phase route maintains the uniform spherical morphology of the [Ni1/3Co1/3Mn1/3]3O4, and it exhibits a higher capacity retention and better rate capability than that prepared by ball mill method. The initial discharge capacity of this sample reaches 178 mA-h/g and the capacity retention after 50 cycles is 98.7% at a current density of 20 mA/g. Moreover, it delivers high discharge capacity of 135 mA-h/g at a current density of 1 000 mA/g.