Ordered Co/Cu multilayer nanowire arrays have been fabricated into anodic aluminium oxide templates with Ag and Cu substrate by direct current electrodeposition. This paper studies the morphology, structure and magnet...Ordered Co/Cu multilayer nanowire arrays have been fabricated into anodic aluminium oxide templates with Ag and Cu substrate by direct current electrodeposition. This paper studies the morphology, structure and magnetic properties by transmission electron microscopy, selective area electron diffraction, x-ray diffraction, and vibrating sample magnetometer. X-ray diffraction patterns reveal that both as-deposited nanowire arrays films exhibit face-centred cubic structure. Magnetic measurements indicate that the easy magnetization direction of Co/Cu multilayer nanowire arrays films on Ag substrate is perpendicular to the long axis of nanowire, whereas the easy magnetization direction of the sample with Cu substrate is parallel to the long axis of nanowire. The change of easy magnetization direction attributed to different substrates, and the magnetic properties of the nanowire arrays are discussed.展开更多
Ni-Fe/Cu/Co/Cu multilayered nanowire arrays were electrodeposited into anodic aluminum oxide template by using dual-bath method at room temperature. Scanning electron microscopy and transmission electron microscopy we...Ni-Fe/Cu/Co/Cu multilayered nanowire arrays were electrodeposited into anodic aluminum oxide template by using dual-bath method at room temperature. Scanning electron microscopy and transmission electron microscopy were used to characterize the morphology and structure of the multilayered nanowire arrays. Vibrating sample magnetometer and physical property measurement system were used to measure their magnetic and giant magnetoresistance （GMR） properties. The effect of sub-layer thickness on the magnetic and GMR properties was investigated. The results indicate that magnetic properties of electmdeposited nanowires are not affected obviously by Cu layer thickness, while magnetic layers （Ni-Fe and Co layers） have significant influence. In addition, GMR ratio presents an oscillatory behavior as Cu layer thickness changes. The magnetic and GMR properties of the multilayered nanowire arrays are optimum at room temperature for the material structure of Ni-Fe （25 nm）/Cu （15 nm）/Co （25 nm）/Cu （15 nm） with 30 deposition cycles.展开更多
We compare the electrical, optical, and surface properties of the PEDOT：PSS/Cu nanowires （Cu NWs）/PEDOT： PSS （PCP） multilayer for organic solar cells. It is demonstrated that the electrical and optical propertie...We compare the electrical, optical, and surface properties of the PEDOT：PSS/Cu nanowires （Cu NWs）/PEDOT： PSS （PCP） multilayer for organic solar cells. It is demonstrated that the electrical and optical properties of the PEDOT could be improved by the insertion of a Cu NW layer due to its very low resistivity and surface morphology. The organic bulk heterojunction solar cell fabricated on the multil^yer exhibits a higher power conversion ef^ciency than devices based on the PEDOT：PSS or PEDOT：PSS/Cu NWs layer. Moreover, the PCP multilayer can improve cell-performances such as a fill factor and the internal resistance in the device due to horizontally well-aligned Cu NWs. The results suggest that the PCP multilayer is a promising low-cost and low-temperature processing buffer layer candidate for low-cost organic photovoltaics.展开更多
基金supported by the National Natural Science Foundation of China (Grant Nos 10404011 and 50401018)the Program for New Century Excellent Talents (NCET) in University
文摘Ordered Co/Cu multilayer nanowire arrays have been fabricated into anodic aluminium oxide templates with Ag and Cu substrate by direct current electrodeposition. This paper studies the morphology, structure and magnetic properties by transmission electron microscopy, selective area electron diffraction, x-ray diffraction, and vibrating sample magnetometer. X-ray diffraction patterns reveal that both as-deposited nanowire arrays films exhibit face-centred cubic structure. Magnetic measurements indicate that the easy magnetization direction of Co/Cu multilayer nanowire arrays films on Ag substrate is perpendicular to the long axis of nanowire, whereas the easy magnetization direction of the sample with Cu substrate is parallel to the long axis of nanowire. The change of easy magnetization direction attributed to different substrates, and the magnetic properties of the nanowire arrays are discussed.
基金Supported by the Natural Science Foundation of Tianjin,China(08JCZDJC17400)
文摘Ni-Fe/Cu/Co/Cu multilayered nanowire arrays were electrodeposited into anodic aluminum oxide template by using dual-bath method at room temperature. Scanning electron microscopy and transmission electron microscopy were used to characterize the morphology and structure of the multilayered nanowire arrays. Vibrating sample magnetometer and physical property measurement system were used to measure their magnetic and giant magnetoresistance （GMR） properties. The effect of sub-layer thickness on the magnetic and GMR properties was investigated. The results indicate that magnetic properties of electmdeposited nanowires are not affected obviously by Cu layer thickness, while magnetic layers （Ni-Fe and Co layers） have significant influence. In addition, GMR ratio presents an oscillatory behavior as Cu layer thickness changes. The magnetic and GMR properties of the multilayered nanowire arrays are optimum at room temperature for the material structure of Ni-Fe （25 nm）/Cu （15 nm）/Co （25 nm）/Cu （15 nm） with 30 deposition cycles.
基金Supported by the Tianjin Natural Science Foundation under Grant Nos 13JCYBJC18900,12JCQNJC01300 and13JCZDJC26700the Ministry of Science and Technology of China under Grant No 2013AA014201the Tianjin Key Discipline of Material Physics and Chemistry
文摘We compare the electrical, optical, and surface properties of the PEDOT：PSS/Cu nanowires （Cu NWs）/PEDOT： PSS （PCP） multilayer for organic solar cells. It is demonstrated that the electrical and optical properties of the PEDOT could be improved by the insertion of a Cu NW layer due to its very low resistivity and surface morphology. The organic bulk heterojunction solar cell fabricated on the multil^yer exhibits a higher power conversion ef^ciency than devices based on the PEDOT：PSS or PEDOT：PSS/Cu NWs layer. Moreover, the PCP multilayer can improve cell-performances such as a fill factor and the internal resistance in the device due to horizontally well-aligned Cu NWs. The results suggest that the PCP multilayer is a promising low-cost and low-temperature processing buffer layer candidate for low-cost organic photovoltaics.