This paper reports the preparation of nano-TiO2 (about 10 nm) powder by the method of precipitation. In detail, some breparation conditions were investigated in order to find out how to control the grain size and redu...This paper reports the preparation of nano-TiO2 (about 10 nm) powder by the method of precipitation. In detail, some breparation conditions were investigated in order to find out how to control the grain size and reduce the agglomeration of powders. Also, the reflex spectra of nano-scale powders with different grain size were studied. It tvas found that the wave length and width of reflex spectra are connected with the grain size of nano-TiO2 powders展开更多
TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of p...TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of pure Al matrix by 71.5% and 134% respectively However, the elongation is 20.36%, slightly lower than that of the Al matrix.展开更多
TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction (XRD) measurements indicate that the Mn-TiO...TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction (XRD) measurements indicate that the Mn-TiO2 nano powders with Mn concentration of 1 at% and 2 at% annealed at 500 and 800 ℃ are of pure anatase and rutile, respectively. The scanning electron microscope (SEM) observations reveal that the crystal grain size increases with the annealing temperature, and the high resolution transmission electron microscopy (HRTEM) investigations further indicate that the samples are well crystallized, confirming that Mn has doped into the TiO2 crystal lattice effectively. The room temperature ferromagnetism, which could be explained within the scope of the bound magnetic polaron (BMP) theory, is detected in the Mn-TiO2 samples with Mn concentration of 2 at%, and the magnetization of the powders annealed at 500 ℃ is stronger than that of the sample treated at 800 ℃. The UV-VIS diffuse reflectance spectra results demonstrate that the absorption of the TiO2 powders could be enlarged by the enhanced trapped electron absorption caused by Mn doping.展开更多
The comparative study of the tensile plastic deformation of nano(n)-TiO2 ceramic prepared byphysical gas condensation (P) and chemical hydrolysis precipitation (C) methods was conductedby a gas pressure forming techni...The comparative study of the tensile plastic deformation of nano(n)-TiO2 ceramic prepared byphysical gas condensation (P) and chemical hydrolysis precipitation (C) methods was conductedby a gas pressure forming technique at 750~800℃. The results show that n-TiO2 (P) possessesexcellent property of tensile pIastic deformation comparing with n-TiO2(C). The reason for thisis attributed to the surface cleanness and soft agglomeration of n-TiO2 (P) particfe prepared inreIatively cIean vacuum condition.展开更多
纳米 Ti O2 具有独特的光催化性、优异的颜色效应以及紫外线屏蔽等功能 ,在光催化剂、化妆品、抗紫外线吸收剂、功能陶瓷、气敏传感器件等方面具有广阔的应用前景 ,国内外文献对纳米 Ti O2 的性质、应用及其制备方法进行了大量的研究报...纳米 Ti O2 具有独特的光催化性、优异的颜色效应以及紫外线屏蔽等功能 ,在光催化剂、化妆品、抗紫外线吸收剂、功能陶瓷、气敏传感器件等方面具有广阔的应用前景 ,国内外文献对纳米 Ti O2 的性质、应用及其制备方法进行了大量的研究报道。本工作对有关纳米 Ti O2的性能。展开更多
文摘This paper reports the preparation of nano-TiO2 (about 10 nm) powder by the method of precipitation. In detail, some breparation conditions were investigated in order to find out how to control the grain size and reduce the agglomeration of powders. Also, the reflex spectra of nano-scale powders with different grain size were studied. It tvas found that the wave length and width of reflex spectra are connected with the grain size of nano-TiO2 powders
文摘TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of pure Al matrix by 71.5% and 134% respectively However, the elongation is 20.36%, slightly lower than that of the Al matrix.
基金Project supported by the Innovation Foundation of BUAA for PhD Graduates (Grant No. 292122)Equipment Research Foundation of China
文摘TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction (XRD) measurements indicate that the Mn-TiO2 nano powders with Mn concentration of 1 at% and 2 at% annealed at 500 and 800 ℃ are of pure anatase and rutile, respectively. The scanning electron microscope (SEM) observations reveal that the crystal grain size increases with the annealing temperature, and the high resolution transmission electron microscopy (HRTEM) investigations further indicate that the samples are well crystallized, confirming that Mn has doped into the TiO2 crystal lattice effectively. The room temperature ferromagnetism, which could be explained within the scope of the bound magnetic polaron (BMP) theory, is detected in the Mn-TiO2 samples with Mn concentration of 2 at%, and the magnetization of the powders annealed at 500 ℃ is stronger than that of the sample treated at 800 ℃. The UV-VIS diffuse reflectance spectra results demonstrate that the absorption of the TiO2 powders could be enlarged by the enhanced trapped electron absorption caused by Mn doping.
文摘The comparative study of the tensile plastic deformation of nano(n)-TiO2 ceramic prepared byphysical gas condensation (P) and chemical hydrolysis precipitation (C) methods was conductedby a gas pressure forming technique at 750~800℃. The results show that n-TiO2 (P) possessesexcellent property of tensile pIastic deformation comparing with n-TiO2(C). The reason for thisis attributed to the surface cleanness and soft agglomeration of n-TiO2 (P) particfe prepared inreIatively cIean vacuum condition.