Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g...Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .展开更多
Si3N4/TiC nanocomposite ceramics have been fabricated by hot pressing technique with Al2O3 and Y2O3 as additives. The results showed that well dispersed composite powder was carried out by adding dispersant and adjust...Si3N4/TiC nanocomposite ceramics have been fabricated by hot pressing technique with Al2O3 and Y2O3 as additives. The results showed that well dispersed composite powder was carried out by adding dispersant and adjusting pH values of suspensions. Remarkable increase in flexural strength at room temperatures was obtained by adding nanoparticles in Si3N4 matrix with 10% （wt pct） of nano-Si3N4 and 15% of nano-TiC. The flexural strength, fracture toughness and hardness were 1025 MPa, 7.5 MPa.m^1/2 and 15.6 GPa, respectively. The microstructures of materials were analyzed by scanning electron microscopy （SEM） and transmission electron microscopy （TEM）, which indicated that TiC nanoparticles distribute in the matrix and at the grain boundaries. According to the fracture form, low contents of nano particles could refine matrix grains and lead to the crack deflection as well as crack pinning. The multiplex microstructure was formed by mixing nano-Si3N4 particles. The crack trajectories exhibited crack deflection, rod-like grain bridging and pull-out.展开更多
基金Funded by the National Science Foundation of China ( No.50375037)
文摘Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .
基金supported by the National Natural Sci ence Foundation of China(No.50105011)the Foundation for the author by the National Excellent Doctoral Disserta tion of China(200231)+2 种基金the Natural Science Foundation of Shandong Province(Y2004F14)the SRF for ROCS([2002]247),MOE,Chinathe SRF for ROCS(2002[247]),SEM.
文摘Si3N4/TiC nanocomposite ceramics have been fabricated by hot pressing technique with Al2O3 and Y2O3 as additives. The results showed that well dispersed composite powder was carried out by adding dispersant and adjusting pH values of suspensions. Remarkable increase in flexural strength at room temperatures was obtained by adding nanoparticles in Si3N4 matrix with 10% （wt pct） of nano-Si3N4 and 15% of nano-TiC. The flexural strength, fracture toughness and hardness were 1025 MPa, 7.5 MPa.m^1/2 and 15.6 GPa, respectively. The microstructures of materials were analyzed by scanning electron microscopy （SEM） and transmission electron microscopy （TEM）, which indicated that TiC nanoparticles distribute in the matrix and at the grain boundaries. According to the fracture form, low contents of nano particles could refine matrix grains and lead to the crack deflection as well as crack pinning. The multiplex microstructure was formed by mixing nano-Si3N4 particles. The crack trajectories exhibited crack deflection, rod-like grain bridging and pull-out.