Synthesis,characterization and gas-sensing properties of Pd-doped SnO_2 nano particles

SnO2 nano particles with various Pd-doping concentrations were prepared using a template-free hydrothermal method.The effects of Pd doping on the crystal structure,morphology,microstructure,thermal stability and surface chemistry of these nano particles were characterized by transmission electron microscope,X-ray diffractometer and X-ray photoelectron spectroscope respectively.It was observed that Pd-doping had little effect on the grain sizes of the obtained SnO2 nano particles during the hydrothermal route.During thermal annealing,Pd-doping could restrain the growth of grain sizes below 500℃ while the grain growth was promoted when the temperature increased to above 700℃.XPS results revealed that Pd existed in three chemical states in the as-synthesized sample as Pd^0,Pd^2＋ and Pd^4＋,respectively.Pd^4＋ was the main state which was responsible for improving the gas-sensing property.The optimal Pd-doping concentration for better gas-sensing property and thermal stability was 2.0%-2.5% （mole fraction）.

Modification of Nano-α-Al2O3 and Its Influence on the Surface Properties of Waterborne Polyurethane Resin Composite Passivation Films

Silane coupling agent KH560 was used to modify the surface of nano-α-Al2O3 in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al2O3 was determined by nano-particle size analyzer, and the effects of nano-α-Al2O3 content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al2O3 were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al2O3 dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al2O3 increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al2O3.

Production and mechanical properties of nano SiC particle reinforced Ti-6Al-4V matrix composite

Different mass fractions （0, 5%, 10%, and 15%） of the synthesized nano SiC particles reinforced Ti-6Al-4V （Ti64） alloy metal matrix composites （MMCs） were successfully fabricated by the powder metallurgy method. The effects of addition of SiC particle on the mechanical properties of the composites such as hardness and compressive strength were investigated. The optimum density （93.33%） was obtained at the compaction pressure of 6.035 MPa. Scanning electron microscopic （SEM） observations of the microstructures revealed that the wettability and the bonding force were improved in Ti64 alloy/5% nano SiCp composites. The effect of nano SiCp content in Ti64 alloy/SiCp matrix composite on phase formation was investigated by X-ray diffraction. The correlation between mechanical parameter and phase formation was analyzed. The new phase of brittle interfaced reaction formed in the 10% and 15% SiCp composite specimens and resulted in no beneficial effect on the strength and hardness. The compressive strength and hardness of Ti64 alloy/5% nano SiCp MMCs showed higher values. Hence, 5% SiCp can be considered to be the optimal replacement content for the composite.

Creep-Recovery and Relaxation Behavior of High Density Polyethylene/Hydroxyapatite Nano Particles for Bone Substitutes: Effects of Gamma Radiation

The following article has been retracted due to the fact that it cannot be accepted by the author as a journal publication. The Editorial Board takes a very strong respect to the author’s situation on this matter. This paper published in Journal of Biosciences and Medicines Vol.2 No.2, April 2014, has been removed from this site.

STRUCTURAL DETERMINATION OF TITANIUM-OXIDE NANOPARTICLES BY X-RAY ABSORPTION SPECTROSCOPY

As a potential application of titanium-oxide nanoparticles, it is extremely important to investigate a detailed picture of the surface and interior structural properties of nanocrystalline materials, such as rutile and anatase with diameters 7.0 and 4.5nm, respectively. X-ray absorption spectroscopy has been used to identify the local Ti environment and related electronic structure. We combine the experimental results at the Ti edge in both bulk and nano-crystals to determine the lattice distortion in terms of differently characteristic preedge features and the variation in the multiple-scattering region of X-ray absorption near-edge structure (XANES) spectra. The relationship between the transition peaks and the surface-to volume ratio is also discussed.

Effect of Drying on Particle Size and Sensitivities of Nano hexahydro-1,3,5-trinitro-1,3,5-triazine

Nano hexahydro-1,3,5-trinitro-1,3,5-triazine(RDX) was prepared using a bi-directional rotation mill and dried under different conditions(liquid, temperature and drying). It shows that the samples cake seriously and the particles grow up obviously by ordinary drying in different liquids at 70 C, which occurs again after vacuum drying. With the increase of temperature, the degrees of caking and aggregation are enhanced.Well dispersed sample maintaining constant particle size is extracted by supercritical drying, especially freeze drying. Furthermore, the mechanical sensitivities of I-RDX, O-RDX and F-RDX, of which the average sizes are 88.03 mm, 15.32 mm and 0.16 mm, respectively, are evaluated. Compared with I-RDX, the friction, impact and shock sensitivities of O-RDX are slightly lower. However, the friction, impact and shock sensitivities of F-RDX are reduced by 30%, 99.0% and 59.9%, respectively.

Effect of Zn Substitution on the Magnetic Properties of Cobalt Ferrite Nano Particles Prepared Via Sol-Gel Route

Zinc substituted cobalt ferrite nanoparticles (CoxZn1-xFe2O4, with x = 0.0, 0.2, 0.4, 0.8 and 1.0) were prepared via sol-gel route and the effect of zinc concentration on saturation magnetization and lattice parameter were investigated. The particle sizes of the as obtained samples were found to be ~10 nm which increases upto ~92 nm on annealing at 1000oC. The frequency bands near 564-588 cm-1 and 425-442 cm-1 are assigned to the tetrahedral and octahedral clusters which confirm the presence of M-O stretching band in ferrites. The unit cell parameter ‘a’ increases linearly with increasing concentration of zinc due to larger ionic radii of Zn2+ ion . It was found that this substitution allows tunable changes in the magnetic properties of cobalt ferrite. Interestingly, saturation magnetization first increases upto x = 0.4 and then decreases for higher Zn substitution, thus tunable changes in magnetic properties of cobalt ferrite are possible. Source of such behaviour could be the variation of exchange interaction between the tetrahedral and the octahedral sites.

Microstructure and Oxidation Behaviors of Nano-particles Strengthened NiCoCrAlY Cladded Coatings on Superalloys

Nano-particles which can largely improve the microstructure and oxidation resistance of materials are often used as a strengthening component in metal matrix composites. However, few studies were reported on its application in the bond coat of duplex structure thermal barrier coating（TBC）. Three kinds of NiCoCrAlY coatings strengthened by different nano-particles with the same addition （1%, mass fraction） were prepared by the laser cladding technique on Ni-based superalloy substrates, aiming to study the effects of the nano-particles on microstructure and oxidation resistance of NiCoCrAlY coatings （the bond coat of the duplex structure thermal barrier coatings）. Scanning electron microscope （SEM）, X-ray diffractometer（XRD） and thermogravimetry were employed to investigate their morphologies, phases and cyclic oxidation behaviors in atmosphere at 1 050℃, compared with the coating without nano-particles. With the addition of nano-particles, the growth pattern of the grains at the interface changed from epitaxial growth to non-epitaxial growth or part-epitaxial growth; slender dendrites were broken and cellularized; cracks and pores were restrained; and the oxidation weight-gain and the stripping resistance of the oxide scale were improved as well. Among the three kinds of nano-particles, the SiC nano-particles showed the most improvement on microstructure, while the CeO2 nano-particles were insufficient, but its effects on the oxidation resistance are the same as those of the SiC nano-particles. Based on the discussions of the influence mechanism, it is believed that CeO2 nano-particles would show better improvement than SiC nano-particles if the proper amount is added and the proper preparation technique of micro-nanometer composite powders is adopted, with the synergistic action of nanometer effect and reactive element effect.

Research on anti-contact fatigue performance of grease containing nano SbSbS_4 particles

Effects of nano SbSbS4particles on contact fatigue life of a steel ball were evaluated on a self-made ball-rod contact fatigue tester. The anti-fatigue mechanisms of SbSbS4 additive were analyzed by means of SEM and EDAX. It was shown that, when the grease contained SbSbS4, contact fatigue life was improved compared with that of base grease. Nanoparticle absorption action, nanoparticle infiltration action, and extreme pressure and anti-friction performance, explained why SbSbS4 increased the contact fatigue life of the steel ball tested.

MORPHOLOGY EVOLUTION OF POLY(St-co-BuA)/SILICA NANOCOMPOSITE PARTICLES SYNTHESIZED BY EMULSION POLYMERIZATION

Poly（St-co-BuA）/silica nanocomposite latexes were synthesized via conventional emulsion polymerization in the presence of 3-（trimethoxysilyl）propyl methacrylate modified colloidal nano-silica. The effects of surface property, particle size and content of colloidal nano-silica as well as the concentrations of monomer and surfactant on the morphology of nanocomposite latex particles were investigated by transmission electron microscope （TEM） and scanning electron microscope （SEM） in detail. Various interesting morphologies such as grape-like, Chinese gooseberry-like, pomegranate-like and normal core-shell structures were observed. Droplet nucleation mechanism competing with micelle nucleation mechanism was proposed to explain the morphological evolution of the nanocomposite particles.

Preparation and drug releasing property of magnetic chitosan-5-fluorouracil nano-particles

In order to synthesize the targeting drug carrier system,magnetic chitosan-5-fluorouracil nano-particles were prepared by using 5-fluorouracil(5-Fu)as model drug,Fe3O4 nano-particles as kernel,chitosan as enveloping material and glutaraldehyde as cross linking agent through ultrasonic technique.The morphology of the magnetic chitosan-5-Fu nano-particles was observed with a transmission electron microscope(TEM).The results showed that magnetic chitosan-5-Fu nano-particles were prepared in spherical structure with a size range of 50-60 nm.The delivering capacity and drug releasing properties of magnetic chitosan-5-Fu nano-particles were investigated by UV-vis spectrum analysis.The results showed that the loading capacity was 13.4%and the cumulative release percentage in the phosphate buffer(pH=7.2)solutions was 68%in 30 h.These data indicate that the wrapped drug of magnetic chitosan-5-Fu nano-particles was slowly-released.The magnetic response of magnetic chitosan-5-Fu nano-particles was studied by UV-vis spectrometer to detect the changes of solution absorbance.Without external magnetic field,the nano-particle deposition rate was slow.When being subjected to 8 mT magnetic field,the particle sedimentation rate was increased rapidly.The results showed that magnetic chitosan-5-Fu nano-particles have a magnetic stability and strong targeting characteristics.

Surface tension of lithium bromide aqueous solution/ammonia with additives and nano-particles

In order to investigate the effect of additives and nano-particle on the surface tensions of lithium bromide(Li Br) aqueous solution/ammonia, many experiments were carried out based on Wilhelmy plate method. Firstly, the surface tension of Li Br aqueous solution with 1-octanol was measured and then the comparison between the measured results and previous experimental results was given to verify the measuring accuracy. Some new additives, such as cationic surfactants cetyltrimethyl ammonium chloride(CTAC), and cetyltrimethyl ammonium bromide(CTAB) were chosen in the experiments. The experimental results show that CTAC and CTAB can obviously reduce the surface tension of Li Br aqueous solution/ammonia. In addition, it is found that nano-particles cannot remarkably decrease the surface tension of Li Br aqueous solution/ammonia. However, the mixed addition of additives and nano-particles can remarkably affect the surface tension of Li Br aqueous solution/ammonia. That is to say, additives play more important role in reducing the surface tension of Li Br aqueous solution/ammonia. But nano-particles may enhance the heat transfer in the absorption refrigeration process.

Preparation and Characterization of Fe3O4 Magnetic Nano-particles by ^（60）Co γ-ray Irradiation

By using a new method, ^60Co γ-ray irradiation, Fe3O4 magnetic nano-particles were successfully synthesized at room temperature under ambient pressure. The structure, morphology and magnetic properties of these nanoparticles were characterized by X-ray diffraction （XRD）, transmission electron microscope （TEM） and vibrating sample magnetometer （VSM）, respectively. The radiation formation mechanism was also discussed. The results show that the absorbed dose can greatly influence the structure, morphology and magnetic properties of the products. XRD and TEM studies show that the product prepared by γ-ray irradiation （10 kGy） is pure FesO4 phase and the mean diameter of these nano-particles is about 21 nm. The Fe3O4 nano-particles synthesized by γ-ray irradiation （10 kGy） are mainly in small cubic shape and the size uniformity of these particles is good.

Effect of nano-particle size on product distribution and kinetic parameters of Fe/Cu/La catalyst in Fischer-Tropsch synthesis

Effects of nano-particle size on hydrocarbon production rates and distributions for precipitated Fe/Cu/La catalysts in Fischer-Tropsch synthesis were investigated.Nano-structured iron catalyst was prepared by micro-emulsion method.The concept of two superimposed AndersonSchulz-Flory （ASF） distributions has been applied for the representation of the effects of reaction conditions and nano-particles size on kinetics parameters and product distributions.These results reveal that by reducing the particle size of catalyst,the break in ASF distributions was decreased.Also useful different kinetics equations for synthesis of C3 to C9 and C10 to C22 were determined by using α1 and α2 chain growth probabilities.

The influence of nano-particle tracers on the slip length measurements by microPTV

Direct measurement of slip length is based on the measured fluid velocity near solid boundary. However, previous micro particle image velocimetry/particle tracking velocimetry （microPIV/PTV） measurements have reported surprisingly large measured near-wall velocities of pressure-driven flow in apparent contradiction with the no-slip hy-pothesis and experimental results from other techniques. To better interpret the measured results of the microPIV/PTV, we performed velocity profile measurements near a hy-drophilic wall （z = 0.25-1.5 μm） with two sizes of tracer particles （φ 50 nm and φ200 nm）. The experimental results indicate that, at less than 1 μm from the wall, the deviations between the measured velocities and no-slip theoretical values obviously decrease from 93% of φ200 nm particles to 48% of φ50 nm particles. The Boltzmann-like exponential measured particle concentrations near wall were found. Based on the non linear Boltzmann distribution of particle concentration and the effective focus plane thickness, we illustrated the reason of the apparent velocity increase near wall and proposed a method to correct the measured velocity profile. By this method, the deviations between the corrected measured velocities and the no-slip theoretical velocity decrease from 45.8% to 10%, and the measured slip length on hy-drophilic glass is revised from 75 nm to 16 nm. These results indicated that the particle size and the biased particle concentration distribution can significantly affect near wall velocity measurement via microPIV/PTV, and result in larger measured velocity and slip length close to wall.

Pressure-Induced Structural Transitions of the Zinc Sulfide Nano-particles with Different Sizes

ZnS nano-particles with average sizes of 10 nm and 5 nm were fabricated by sol-gel method, and their pressure-induced phase transformations were in-situ examined in a diamond anvil cell by energy dispersive X-ray diffraction （EDXD） from ambient pressure to 35.0 GPa. From the obtained interplanar spacing data,the volume compression ratios were derived at different pressures, and then the bulk modulus and its pressure derivative were obtained by fitting to the Murnaghan equation. It is found that both ZnS nano-particles initially in the zinc-blende phase transformed to cubic NaCl structure in the presence of pressure and the transition was reversible when the pressure was released. Moreover, it is suggested that a smaller particle size will induce a larger transition pressure.

BRITTLE-DUCTILE TRANSITION OF PP/EPDM/ELASTOMERIC NANO-PARTICLE TERNARY BLENDS

The brittle-ductile transition is a very important phenomenon for polymer toughening. Polypropylene （PP） is often toughened by using rubbers, e.g., ethylene-propylene diene monomer （EPDM） has often been used as a modifier. In this article, the toughening of PP by using a new kind of rubber, known as elastomeric nano-particle （ENP）, and the brittleductile transition of PP/EPDM/ENP was studied. Compared to PP/EPDM binary blends, the brittle-ductile transition of PP/EPDM/ENP ternary blends occurred at lower EPDM contents. SEM experiment was carried out to investigate the etched and impact-fractured surfaces. ENP alone had no effect on the impact strength of PP, however, with the same EPDM content, PP/EPDM/ENP ternary blends had smaller particle size, better dispersion and smaller interparticle distance in contrary to PP/EPDM binary blends, which promoted the brittle-ductile transition to occur earlier.

Synthesis of nano-CaCO_3 composite particles and their application

Nano-calcium carbonate composite particles were synthesized by the soapless emulsion polymerization technique of double monomers. The composite particles formation mechanism was investigated. The effects of composite particles on the mechanical properties of nano-CaCO3-ABS （acrylonitrile-butadiene-styrene copolymer） composite material were studied. It was validated that the composite particles are made up of the nano-calcium carbonate cores and the shells of alternating copolymers of butyl acrylate （BA） and styrene （St）. The shells are chemically grafted and physically wrapped on the surface of nano-calcium carbonate particles. When the composite particles were filled in ABS matrix, the CaCO3 particles are homogeneously dispersed in the composite material as nanoscales. The impact strength of the composite material is obviously enhanced after filling appropriate amounts of composite particles. It can be concluded that the soapless emulsion polymerization of double monomers is an effective method for nano-CaCO3 surface treatment. 2008 University of Science and Technology Beijing. All rights reserved.

Friction and Wear of Polymer Composites Filled by Nano-Particles: A Review

Composites formed by adding nano-scale particles to a polymer matrix results in improving electrical, mechanical, and thermal properties of the composite. Good tribological properties can be obtained for polymers filled with nano-scale fillers compared to that filled with micro-scale particles. The friction and wear resistance of these composites is found to increase with increasing filler concentration. It is also possible to use multi-functional fillers to develop high performance composites which cannot be achieved by using a single filler.

Factors Affecting the Reductive Properties of the Core-Shell SiO2-Coated Iron Nanoparticles

In this study, novel core-shell SiO2-coated iron nanoparticles (SiO2-nZVI) were synthesized using a one-step Stoeber method. The Malachite green degradation abilities of the nanoparticles were investigated. The effects of ethanol/distilled water volume ratio, presence and absence of PEG, tetraethyl orthosilicate (TEOS) dosage, and hydrolysis time used in the nanoparticles preparation process were investigated. The results indicated that the SiO2-coated iron nanoparticles had the highest reduction activity when the particles synthesized with ethanol/H2O ratio of 2:1, PEG of 0.15 ml, TEOS of 0.5 ml and the reaction time was 4 h. The SiO2-nZVI nanoparticles were characterized using Transmission Electron Microscopy (TEM), Energy Dispersive Spectrometry (EDS) and powder X-Ray Diffraction (XRD). The results showed that the average particles diameter of the SiO2-nZVI was 20 - 30 nm. The thickness of the outside SiO2 film is consistent and approximately 10 nm. The results indicated that the nanoparticles coated completely with a transparent SiO2-film. Such nanoparticles could have wide applications in dye decolorization.