Microstructure and Contact Fatigue Behavior of Nano-SiO_2/Ni Coating Prepared by Electro-Brush Plating

The composite coating nano SiO 2/Ni was prepared by co depositing nano SiO 2 particles with pure nickel through electro brush plating. By taking into account the effect of microstructure, heat treatment and load on the contact fatigue life, the anti contact fatigue behavior of the composite coating was examined and compared with that of nickel coating. As a result, the contact fatigue life decreased with the increasing of load. The contact fatigue lives of nano SiO 2/Ni coating were 16.5% and 45.2% higher than those of nickel coating respectively under the loads of 60 N and 140 N, and 326.3% higher than its counterpart of nickel coating after annealed under the load of 140 N. From the SEM image of fatigue fracture, it has been observed that the fatigue fracture of the composite coating initiated in the sub surface as well as at the track surface due to the huddling of units, and propagated along the interface between grain units.

Effects of Surfactants SDS and CTAB on Ni-SiC Deposition

The influences of surfactant type and concentration on the content and uniformity of SiC particles in Ni-SiC deposit were studied in this paper. The electrochemical behavior of preparing Ni-SiC composite coating was investigated using the cyclic voltammetry method. Then the impact of surfactants on the deposition potential of Ni-SiC coating was analyzed. Electrochemical studies showed that the cathode overvoltage increases gradually with increasing SDS（Sodium dodecyl sulfate） concentration. The CV curve showed the shift towards a lower current at a given potential with increasing SDS concentration. Ni-SiC composite coatings were prepared by electrodeposition. The experimental results show that the dispersion of 40 nm SiC in Ni-SiC coating obtained in the electrolyte containing SDS is superior that containing CTAB（cetyltrimethyl ammonium bromide）. CTAB increases the content of 40 nm SiC particles in the Ni-SiC coating, but the uniformity of 40 nm SiC particles in Ni-SiC composite coating is poor. SiC particles are still agglomerated. Compared with the anionic surfactant SDS and the cationic surfactant CTAB, surfactant SDS makes the particles better dispersed. But the contribution of surfactant SDS for co-deposition amount of SiC particles is negligible. The cationic surfactant CTAB can effectively improve the suspension performance of SiC particles and promote the co-deposition of SiC particles and metallic nickel. But there is still some reunion of SiC.