This study focuses on the preparation of nanostructured holmium oxide via the decomposition of holmium acetate precursor utilizing the non-isothermal strategy. Thermogravimetric analysis(TGA) was used to follow up the...This study focuses on the preparation of nanostructured holmium oxide via the decomposition of holmium acetate precursor utilizing the non-isothermal strategy. Thermogravimetric analysis(TGA) was used to follow up the various thermal events involved in the decomposition process. Dehydration completes approximately at 150℃, which is followed by the decomposition of the anhydrous acetate leading to the formation of holmium oxide. Based on the TGA results the acetate precursor was heated non-isothermally at the temperature range of 150 e700℃. The obtained solids were characterized using powder X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), Fourier transform infrared spectroscopy(FT-IR), field-emission scanning electron microscopy(FE-SEM) and transmission electron microscopy(TEM). It is found that nanocrystalline Ho_2 O_3 starts to form at 500℃ and presents the only phase detected at the 500 e700℃ range. The electrical conductivity of the solids that form at the temperature range of 300 e700℃ was investigated. The obtained values were correlated with the observed structural modifications accompanying the heat treatment. The electrical conductivity of the Ho_2 O_3 samples prepared at 500, 600 and 700℃ reaches the values of 1.92 × 10^(-7), 1.61 × 10^(-7) and 8.33 × 10^(-8) Ω^(-1)cm^(-1) at a measuring temperature of 500℃, respectively. These values are potentially advantageous for high-resistivity devices.展开更多
文摘This study focuses on the preparation of nanostructured holmium oxide via the decomposition of holmium acetate precursor utilizing the non-isothermal strategy. Thermogravimetric analysis(TGA) was used to follow up the various thermal events involved in the decomposition process. Dehydration completes approximately at 150℃, which is followed by the decomposition of the anhydrous acetate leading to the formation of holmium oxide. Based on the TGA results the acetate precursor was heated non-isothermally at the temperature range of 150 e700℃. The obtained solids were characterized using powder X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), Fourier transform infrared spectroscopy(FT-IR), field-emission scanning electron microscopy(FE-SEM) and transmission electron microscopy(TEM). It is found that nanocrystalline Ho_2 O_3 starts to form at 500℃ and presents the only phase detected at the 500 e700℃ range. The electrical conductivity of the solids that form at the temperature range of 300 e700℃ was investigated. The obtained values were correlated with the observed structural modifications accompanying the heat treatment. The electrical conductivity of the Ho_2 O_3 samples prepared at 500, 600 and 700℃ reaches the values of 1.92 × 10^(-7), 1.61 × 10^(-7) and 8.33 × 10^(-8) Ω^(-1)cm^(-1) at a measuring temperature of 500℃, respectively. These values are potentially advantageous for high-resistivity devices.