Nanocrystalline titanium dioxide powder is characterized for phase analysis as well as particle size and its distribution by x-ray diffraction and small angle neutron scattering measurements. Analysis of the SANS data...Nanocrystalline titanium dioxide powder is characterized for phase analysis as well as particle size and its distribution by x-ray diffraction and small angle neutron scattering measurements. Analysis of the SANS data in the momentum transfer range q = 0.1 - 1.8 nm–1 reveals an average particle size of 24.82 nm in good agreement with the particle size determined earlier by transmission electron microscopy. XRD measurement proves co-existence of rutile and anatase phases in this commercial TiO2 nanocrystalline powder.展开更多
Titanium dioxide thin films with a rutile crystallinite size around 20 nm were fabri- cated by pulsed laser deposition （PLD） aided with an electron cyclotron resonance （ECR） plasma. With annealing treatment, the c...Titanium dioxide thin films with a rutile crystallinite size around 20 nm were fabri- cated by pulsed laser deposition （PLD） aided with an electron cyclotron resonance （ECR） plasma. With annealing treatment, the crystal size of the rutile crystallinite increased to 100 nm. The apatite-forming ability of the films as deposited and after annealing was investigated in a kind of simulated body fluid with ion concentrations nearly equal to those of human blood plasma. The results indicate that ECR aided PLD is an effective way both to fabricate bioactive titanium dioxide thin films and to optimize the bioactivity of titanium dioxide, with both crystal size and defects of the film taken into account.展开更多
Titanium dioxide is a photocatalytically active substance used as a white pigment for cosmetics.In sunlight,titanium dioxide catalyzes decomposition of a certain amount of sebum on the skin by ultraviolet radiation.He...Titanium dioxide is a photocatalytically active substance used as a white pigment for cosmetics.In sunlight,titanium dioxide catalyzes decomposition of a certain amount of sebum on the skin by ultraviolet radiation.Herein,a novel white pigment for use in cosmetics was developed from titanium dioxide and phosphoric acid at pH=4 with and without glycerin,sodium lactate,lactic acid,and urea.The chemical composition,powder properties,photocatalytic activity,color phase,and smoothness of the samples were studied.Addition of glycerin led to a decline in the intensity of the X-ray diffraction(XRD)peak of TiO_(2) relative to that of the other samples.The particle size of the materials prepared with and without additives was 0.3μm;however,extensive aggregation was observed in the obtained materials.The photocatalytic activity of TiO_(2) was inhibited by phosphoric acid treatment.The materials prepared with sodium lactate,lactic acid,and glycerin exhibited higher photocatalytic activity than that prepared without additives.The obtained materials showed a high reflectance in the range of visible light,and the L^(*)values in L^(*)a^(*)b^(*) color space were high(where L^(*)defines lightness,a^(*) denotes the red/green value,and b^(*) the yellow/blue value).These results indicate that the samples prepared in this work are suitable for use as white pigments.展开更多
文摘Nanocrystalline titanium dioxide powder is characterized for phase analysis as well as particle size and its distribution by x-ray diffraction and small angle neutron scattering measurements. Analysis of the SANS data in the momentum transfer range q = 0.1 - 1.8 nm–1 reveals an average particle size of 24.82 nm in good agreement with the particle size determined earlier by transmission electron microscopy. XRD measurement proves co-existence of rutile and anatase phases in this commercial TiO2 nanocrystalline powder.
基金supported by Shanghai Science and Technology Committee (09ZR1414600)
文摘Titanium dioxide thin films with a rutile crystallinite size around 20 nm were fabri- cated by pulsed laser deposition （PLD） aided with an electron cyclotron resonance （ECR） plasma. With annealing treatment, the crystal size of the rutile crystallinite increased to 100 nm. The apatite-forming ability of the films as deposited and after annealing was investigated in a kind of simulated body fluid with ion concentrations nearly equal to those of human blood plasma. The results indicate that ECR aided PLD is an effective way both to fabricate bioactive titanium dioxide thin films and to optimize the bioactivity of titanium dioxide, with both crystal size and defects of the film taken into account.
文摘Titanium dioxide is a photocatalytically active substance used as a white pigment for cosmetics.In sunlight,titanium dioxide catalyzes decomposition of a certain amount of sebum on the skin by ultraviolet radiation.Herein,a novel white pigment for use in cosmetics was developed from titanium dioxide and phosphoric acid at pH=4 with and without glycerin,sodium lactate,lactic acid,and urea.The chemical composition,powder properties,photocatalytic activity,color phase,and smoothness of the samples were studied.Addition of glycerin led to a decline in the intensity of the X-ray diffraction(XRD)peak of TiO_(2) relative to that of the other samples.The particle size of the materials prepared with and without additives was 0.3μm;however,extensive aggregation was observed in the obtained materials.The photocatalytic activity of TiO_(2) was inhibited by phosphoric acid treatment.The materials prepared with sodium lactate,lactic acid,and glycerin exhibited higher photocatalytic activity than that prepared without additives.The obtained materials showed a high reflectance in the range of visible light,and the L^(*)values in L^(*)a^(*)b^(*) color space were high(where L^(*)defines lightness,a^(*) denotes the red/green value,and b^(*) the yellow/blue value).These results indicate that the samples prepared in this work are suitable for use as white pigments.