Microstructural evolution and strengthening mechanisms of Mg-3Sn-1Ca based alloys with additions of different amounts of Al N nanoparticles were investigated.It was found that with increasing the amount of AlN nano-pa...Microstructural evolution and strengthening mechanisms of Mg-3Sn-1Ca based alloys with additions of different amounts of Al N nanoparticles were investigated.It was found that with increasing the amount of AlN nano-particles the grain size decreases obviously.The existence of AlN nano-particles could refine the primary crystal phases CaMgSn,which provided more heterogeneous nucleation sites for the formation of magnesium.Moreover,such nano-particles could also restrict the grain growth during solidification.After adding AlN nano-particles,both the tensile properties at room temperature and high temperature 250℃and the hardness are largely improved.The improvement of strength is attributed to grain refinement and second phase refinement.展开更多
Nano-particles which can largely improve the microstructure and oxidation resistance of materials are often used as a strengthening component in metal matrix composites. However, few studies were reported on its appli...Nano-particles which can largely improve the microstructure and oxidation resistance of materials are often used as a strengthening component in metal matrix composites. However, few studies were reported on its application in the bond coat of duplex structure thermal barrier coating(TBC). Three kinds of NiCoCrAlY coatings strengthened by different nano-particles with the same addition (1%, mass fraction) were prepared by the laser cladding technique on Ni-based superalloy substrates, aiming to study the effects of the nano-particles on microstructure and oxidation resistance of NiCoCrAlY coatings (the bond coat of the duplex structure thermal barrier coatings). Scanning electron microscope (SEM), X-ray diffractometer(XRD) and thermogravimetry were employed to investigate their morphologies, phases and cyclic oxidation behaviors in atmosphere at 1 050℃, compared with the coating without nano-particles. With the addition of nano-particles, the growth pattern of the grains at the interface changed from epitaxial growth to non-epitaxial growth or part-epitaxial growth; slender dendrites were broken and cellularized; cracks and pores were restrained; and the oxidation weight-gain and the stripping resistance of the oxide scale were improved as well. Among the three kinds of nano-particles, the SiC nano-particles showed the most improvement on microstructure, while the CeO2 nano-particles were insufficient, but its effects on the oxidation resistance are the same as those of the SiC nano-particles. Based on the discussions of the influence mechanism, it is believed that CeO2 nano-particles would show better improvement than SiC nano-particles if the proper amount is added and the proper preparation technique of micro-nanometer composite powders is adopted, with the synergistic action of nanometer effect and reactive element effect.展开更多
Effects of nano-particle size on hydrocarbon production rates and distributions for precipitated Fe/Cu/La catalysts in Fischer-Tropsch synthesis were investigated.Nano-structured iron catalyst was prepared by micro-em...Effects of nano-particle size on hydrocarbon production rates and distributions for precipitated Fe/Cu/La catalysts in Fischer-Tropsch synthesis were investigated.Nano-structured iron catalyst was prepared by micro-emulsion method.The concept of two superimposed AndersonSchulz-Flory (ASF) distributions has been applied for the representation of the effects of reaction conditions and nano-particles size on kinetics parameters and product distributions.These results reveal that by reducing the particle size of catalyst,the break in ASF distributions was decreased.Also useful different kinetics equations for synthesis of C3 to C9 and C10 to C22 were determined by using α1 and α2 chain growth probabilities.展开更多
In order to investigate the effect of additives and nano-particle on the surface tensions of lithium bromide(Li Br) aqueous solution/ammonia, many experiments were carried out based on Wilhelmy plate method. Firstly, ...In order to investigate the effect of additives and nano-particle on the surface tensions of lithium bromide(Li Br) aqueous solution/ammonia, many experiments were carried out based on Wilhelmy plate method. Firstly, the surface tension of Li Br aqueous solution with 1-octanol was measured and then the comparison between the measured results and previous experimental results was given to verify the measuring accuracy. Some new additives, such as cationic surfactants cetyltrimethyl ammonium chloride(CTAC), and cetyltrimethyl ammonium bromide(CTAB) were chosen in the experiments. The experimental results show that CTAC and CTAB can obviously reduce the surface tension of Li Br aqueous solution/ammonia. In addition, it is found that nano-particles cannot remarkably decrease the surface tension of Li Br aqueous solution/ammonia. However, the mixed addition of additives and nano-particles can remarkably affect the surface tension of Li Br aqueous solution/ammonia. That is to say, additives play more important role in reducing the surface tension of Li Br aqueous solution/ammonia. But nano-particles may enhance the heat transfer in the absorption refrigeration process.展开更多
Direct measurement of slip length is based on the measured fluid velocity near solid boundary. However, previous micro particle image velocimetry/particle tracking velocimetry (microPIV/PTV) measurements have report...Direct measurement of slip length is based on the measured fluid velocity near solid boundary. However, previous micro particle image velocimetry/particle tracking velocimetry (microPIV/PTV) measurements have reported surprisingly large measured near-wall velocities of pressure-driven flow in apparent contradiction with the no-slip hy-pothesis and experimental results from other techniques. To better interpret the measured results of the microPIV/PTV, we performed velocity profile measurements near a hy-drophilic wall (z = 0.25-1.5 μm) with two sizes of tracer particles (φ 50 nm and φ200 nm). The experimental results indicate that, at less than 1 μm from the wall, the deviations between the measured velocities and no-slip theoretical values obviously decrease from 93% of φ200 nm particles to 48% of φ50 nm particles. The Boltzmann-like exponential measured particle concentrations near wall were found. Based on the non linear Boltzmann distribution of particle concentration and the effective focus plane thickness, we illustrated the reason of the apparent velocity increase near wall and proposed a method to correct the measured velocity profile. By this method, the deviations between the corrected measured velocities and the no-slip theoretical velocity decrease from 45.8% to 10%, and the measured slip length on hy-drophilic glass is revised from 75 nm to 16 nm. These results indicated that the particle size and the biased particle concentration distribution can significantly affect near wall velocity measurement via microPIV/PTV, and result in larger measured velocity and slip length close to wall.展开更多
The brittle-ductile transition is a very important phenomenon for polymer toughening. Polypropylene (PP) is often toughened by using rubbers, e.g., ethylene-propylene diene monomer (EPDM) has often been used as a ...The brittle-ductile transition is a very important phenomenon for polymer toughening. Polypropylene (PP) is often toughened by using rubbers, e.g., ethylene-propylene diene monomer (EPDM) has often been used as a modifier. In this article, the toughening of PP by using a new kind of rubber, known as elastomeric nano-particle (ENP), and the brittleductile transition of PP/EPDM/ENP was studied. Compared to PP/EPDM binary blends, the brittle-ductile transition of PP/EPDM/ENP ternary blends occurred at lower EPDM contents. SEM experiment was carried out to investigate the etched and impact-fractured surfaces. ENP alone had no effect on the impact strength of PP, however, with the same EPDM content, PP/EPDM/ENP ternary blends had smaller particle size, better dispersion and smaller interparticle distance in contrary to PP/EPDM binary blends, which promoted the brittle-ductile transition to occur earlier.展开更多
Composites formed by adding nano-scale particles to a polymer matrix results in improving electrical, mechanical, and thermal properties of the composite. Good tribological properties can be obtained for polymers fill...Composites formed by adding nano-scale particles to a polymer matrix results in improving electrical, mechanical, and thermal properties of the composite. Good tribological properties can be obtained for polymers filled with nano-scale fillers compared to that filled with micro-scale particles. The friction and wear resistance of these composites is found to increase with increasing filler concentration. It is also possible to use multi-functional fillers to develop high performance composites which cannot be achieved by using a single filler.展开更多
Particles can be removed from a silicon surface by means of irradiation and a laser plasma shock wave.The particles and silicon are heated by the irradiation and they will expand differently due to their different exp...Particles can be removed from a silicon surface by means of irradiation and a laser plasma shock wave.The particles and silicon are heated by the irradiation and they will expand differently due to their different expansion coefficients,making the particles easier to be removed.Laser plasma can ionize and even vaporize particles more significantly than an incident laser and,therefore,it can remove the particles more efficiently.The laser plasma shock wave plays a dominant role in removing particles,which is attributed to its strong burst force.The pressure of the laser plasma shock wave is determined by the laser pulse energy and the gap between the focus of laser and substrate surface.In order to obtain the working conditions for particle removal,the removal mechanism,as well as the temporal and spatial characteristics of velocity,propagation distance and pressure of shock wave have been researched.On the basis of our results,the conditions for nano-particle removal are achieved.展开更多
The change of conductivity and transparency of silver nanowire (AgNW) films by adding silver nano-particles (AgNPs) onto their surface is studied. The results show that the conductivity of the AgNW film is greatly...The change of conductivity and transparency of silver nanowire (AgNW) films by adding silver nano-particles (AgNPs) onto their surface is studied. The results show that the conductivity of the AgNW film is greatly improved with its sheet resistance reduced about 78. 7% to 51.9Ω/sq, and there is no obvious reduction of the transmittance. Further studies show that there is a self-assembling process pushing the AgNPs to concentrate at the intersecting points between AgNWs to weld them, which would reduce the intersection resistance between the AgNWs. This self-assembling behavior is led by the surface interactivities among the dispersing liquid of AgNPs, the surface of the substrate and AgNWs when the dispersing liquid is drying.展开更多
γ-Fe nano-particles with size of 20-40 nm were produced by SF6-sensitized CW CO2 laser-induced gaseous pyrolysis of Fe(Co) 5, The γ-Fe stabte in reaction zone at above 910℃ was formed.The rapid quenching prevents f...γ-Fe nano-particles with size of 20-40 nm were produced by SF6-sensitized CW CO2 laser-induced gaseous pyrolysis of Fe(Co) 5, The γ-Fe stabte in reaction zone at above 910℃ was formed.The rapid quenching prevents from the γ-Fe transforming to α-Fe as rapidly cooling from high temperature to room temperature, The characteristics of the particles were examined at room temperature by TEM. electron diffraction and XRD. It was proved that about 70% of γ-Fe phase in the particles was present. In addition. the lattice constant of the γ-Fe was 0.364 nm in place of 0.360 nm展开更多
The tribological properties of Sialon sliding against AISI52100 steel ball under the lubrication of solid particle additives, as micro-borate particle and nano-PbS particle, were evaluated by a SRV ball-on-disc test r...The tribological properties of Sialon sliding against AISI52100 steel ball under the lubrication of solid particle additives, as micro-borate particle and nano-PbS particle, were evaluated by a SRV ball-on-disc test rig. The chemical composition of the worn surface was characterized by X-ray photoelectron spectroscopy (XPS). The morphologies of the worn surfaces of Sialon were analyzed by scanning electron microscopy (SEM). The results show that the particles can reduce the friction coefficient of the pairs and the wear volume of Sialon significantly. The wear resistance of micro-borate is superior to that of nano-PbS while the friction-reducing ability of PbS is better than that of borate. According to the XPS and SEM results, the wear resistance of PbS is mainly depended on the tribochemical film mainly composed of PbSO 4, which deposited on the worn surface with good bonding strength. No tribochemical reaction or deposited film was detected or observed on the worn surface of Sialon under the lubrication of borate, indicating that the possible physically deposited film generated from micro particle can also greatly reduce the wear volume of Sialon, though the friction reducing ability of which is inferior to that of nano PbS particle.展开更多
To improve the hydrophilicity and anti-fouling performance in water treatment,both entrapped method and deposited method were used to modify polyvinylidene fluoride(PVDF)porous membrane with composite Al2O3/TiO2 nano-...To improve the hydrophilicity and anti-fouling performance in water treatment,both entrapped method and deposited method were used to modify polyvinylidene fluoride(PVDF)porous membrane with composite Al2O3/TiO2 nano-particles.Neat PVDF membrane was prepared and its property was also compared with that of the modified membranes.Membrane permeation flux and anti-fouling performance were measured using a membrane cell.The contact angle between water and membrane surface was detected in order to denote the membrane hydrophilicity.Membrane morphology and surface structure were examined by atomic-force microscopy(AFM)and scanning electron microscopy(SEM).Experimental results showed that modified membranes had higher permeation fluxes than that of the neat PVDF membrane.The addition of nano-particles altered membrane surface morphology and increased surface roughness.Due to the hydrophilicity of nano-particles,however,the membrane anti-fouling performance was improved instead of worsened.The entrapped membrane exhibited better anti-fouling performance than the deposited membrane and the neat membrane.展开更多
We have observed the thermodynamic properties of metallic superconductive nano-particles in the grand canonical ensemble; and the level distribution and the level correlation between the discrete electronic energy lev...We have observed the thermodynamic properties of metallic superconductive nano-particles in the grand canonical ensemble; and the level distribution and the level correlation between the discrete electronic energy levels are considered in the calculation of the electronic spin susceptibility of the ensemble numerically. The quantum effect, even-odd effect and other special effects existing in the metallic nano-particles are also studied in this article.展开更多
Rutile phase exhibits higher refractive index and h id ing power, good chemical stability, and is becoming a candidate material for the high-temperature separation and catalysis applications. The thermodynamically sta...Rutile phase exhibits higher refractive index and h id ing power, good chemical stability, and is becoming a candidate material for the high-temperature separation and catalysis applications. The thermodynamically stable feature of rutile among the three polymorphs of TiO 2 usually hinders ob taining nano-sized rutile phase by a conventional calcining way. However, acid peptization of amorphous TiO 2 is favorable to the formation of rutile phase. I n this work, well-crystallized and well-dispersed rod-like rutile particles w ith specific surface areas of 49.1 and 35.0 m 2/g were prepared by hydrothermal ly treating the acid peptized TiO 2 amorphous sols at relatively low temperatur es of 200 ℃ or 240 ℃, respectively. The formation of non-touching rutile part icles is attributed to high long-range electrostatic forces between particles i n the presence of the high concentration of the peptizer. The acid peptization w ould easily break the ≡Ti-O-Ti≡ bonds to form ≡Ti-OH or HO-Ti-OH species depending on the amount of acid, and create conditions for the formation of rut ile nuclei after structural rearrangements.展开更多
Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,w...Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,we deeply investigated the optical,electrical and the thermal stability of PEDOT nanoparticles.The main results are as follows: the small-sized PEDOT nanoparticles were prepared and utilized by different methods,such as ultraviolet/visible (UV-Vis) spectroscopy,Fourier-transform infrared (FT- IR) spectrum,scanning electron microscopy(SEM) and so on.The results show that the amount of oxidizer,ultrasonic treatment,polymerizing temperature and doping degree can influent morphology,electrical ability and gas sensitivity of PEDOT nanoparticles.The Bragg peaks of nanoparticles at 6.7°,12.7°,25° were observed by XRD and the better orientation of molecular chain was attributed to the effective doping of toluene-p-sulfonic acid,which also resulted in an enhancement of thermal stability of nanoparticles than conventional PEDOT.展开更多
CdS particles were generated in the mixed sodium 10- undecenoate--decyltrmethylammonium bromide vesicle dispersions.Depending on the condition and method of preparation. CdSsemi conductor absorption edges were found...CdS particles were generated in the mixed sodium 10- undecenoate--decyltrmethylammonium bromide vesicle dispersions.Depending on the condition and method of preparation. CdSsemi conductor absorption edges were found to range from 526 to 448 nm, corresponding to particle diameter between >5. 0 and 2. 7 nm.展开更多
The paper presents the results of studies surface microrelief, frequency-temperature characteristics of the imaginary part of the dielectric permittivity and dielectric loss of PE+TlInSe2 composite materials in 25。C ...The paper presents the results of studies surface microrelief, frequency-temperature characteristics of the imaginary part of the dielectric permittivity and dielectric loss of PE+TlInSe2 composite materials in 25。C - 150。C temperature and 25 Hz - 1 MHz frequency range before and after application of the aluminum nano-particles with a size of 50 nm. The change in the amount of semicon-ductor filler TlInSe2 and aluminum nano-particles changes the state of the surface and the frequency-temperature characteristics of composite materials PE+xvol.%TlInSe2, which allows to obtain composites with the desired dielectric permittivity and dielectric loss.展开更多
Pure and doped Polyvinylidene difluoride (PVDF) films, for the detection of infrared radiation, have been well documented using the mechanism of pyroelectricity. Alternatively, the electrical properties of films made ...Pure and doped Polyvinylidene difluoride (PVDF) films, for the detection of infrared radiation, have been well documented using the mechanism of pyroelectricity. Alternatively, the electrical properties of films made from Polyvinyl Alcohol (PVA) have received considerable attention in recent years. The investigation of surface resistivities of both such films, to this point, has received far less consideration in comparison to pyroelectric effects. In this research, we report temperature dependent surface resistivity measurements of commercial, and of multiwall carbon nanotubes (MWCNT), or Ag-nanoparticle doped PVA films. Without any variation in the temperature range from 22°C to 40°C with controlled humidity, we found that the surface resistivity decreases initially, reaches a minimum, but rises steadily as the temperature continues to increase. This research was conducted with the combined instrumentation of the Keithley Model 6517 Electrometer and Keithley Model 8009 resistivity test fixture using both commercial and in-house produced organic thin films. With the objective to quantify the suitability of PVDF and PVA films as IR detector materials, when using the surface resistivity phenomenon, instead of or in addition to the pyroelectricity, surface resistivity measurements are reported when considering bolometry. We found that the surface resistivity measurements on PVA films were readily implemented.展开更多
Catalytic direct decomposition of NO by perovskite-type catalysts has attracted much attention for the various possible components and the unique structure. LaCoO_3 nanoparticles were precipitated on a-Al_2O_3 micro p...Catalytic direct decomposition of NO by perovskite-type catalysts has attracted much attention for the various possible components and the unique structure. LaCoO_3 nanoparticles were precipitated on a-Al_2O_3 micro powders by rotary chemical vapor deposition(rotary CVD) and its catalytic performance for the decomposition of NO was investigated. LaCoO_3 nano-particles with 100 nm in average diameter and 1.5% in mass were uniformly dispersed on a-Al_2O_3 powder. The conversion of NO increased with increasing temperature from 400 to 950 ℃, and reached 28.7% at 950 ℃. The gas velocity of transformed NO on LaCoO_3 nano-particles catalyst per mass unit was 7.7 mL/(g min), showing a good catalytic activity over the calculated results of pure catalysts. After five times of aging performance experiments, the NO conversion kept the same value, showing a good aging performance and thermal stability.展开更多
Bacterial pathogens produced resistance against the existing antimicrobial applications. Scientist trending towards the potent novel eco-friendly and cost effective antimicrobial approaches and fabricating bio-based n...Bacterial pathogens produced resistance against the existing antimicrobial applications. Scientist trending towards the potent novel eco-friendly and cost effective antimicrobial approaches and fabricating bio-based nano-particles. In this regard, several bio-materials have been investigated, such as, bacteria, fungi, algae, lichens and green plants. Lichens are introduced as an emerging source to synthesis bio-based nano-particles. The lichen-based metal nano-materials, especially fabricated by applying green chemistry strategies, have resulted significant alternates to traditional antimicrobial applications. Several studies break out and revealed that lichen-based nano-particle showed strong antimicrobial efficacy, as the lichens are biologically compatible. Current review summarizes an overview of lichen-based nano-materials, their fabrication, their applications, and their molecular action mechanism. As it emerged a broad spectrum antimicrobial agent for pharmaceutical and agricultural applications.展开更多
基金financially supported by the Study Abroad Program by the Government of Shandong Province(201802005)Linyi Industrial Technology Research Institute and Shandong Yinguang Yuyuan Light Metal Precise Forming Co.,Ltd。
文摘Microstructural evolution and strengthening mechanisms of Mg-3Sn-1Ca based alloys with additions of different amounts of Al N nanoparticles were investigated.It was found that with increasing the amount of AlN nano-particles the grain size decreases obviously.The existence of AlN nano-particles could refine the primary crystal phases CaMgSn,which provided more heterogeneous nucleation sites for the formation of magnesium.Moreover,such nano-particles could also restrict the grain growth during solidification.After adding AlN nano-particles,both the tensile properties at room temperature and high temperature 250℃and the hardness are largely improved.The improvement of strength is attributed to grain refinement and second phase refinement.
基金supported by Specialized Research Fund for Doctoral Program of Higher Education of China (Grant No. 20060287019)Opening Research Fund of Jiangsu Provincial Key Laboratory of Tribology of China (Grant No. kjsmcx07001)Jiangsu Provincial Graduate Innovation Foundation of China (Grant No. CX08B-039Z)
文摘Nano-particles which can largely improve the microstructure and oxidation resistance of materials are often used as a strengthening component in metal matrix composites. However, few studies were reported on its application in the bond coat of duplex structure thermal barrier coating(TBC). Three kinds of NiCoCrAlY coatings strengthened by different nano-particles with the same addition (1%, mass fraction) were prepared by the laser cladding technique on Ni-based superalloy substrates, aiming to study the effects of the nano-particles on microstructure and oxidation resistance of NiCoCrAlY coatings (the bond coat of the duplex structure thermal barrier coatings). Scanning electron microscope (SEM), X-ray diffractometer(XRD) and thermogravimetry were employed to investigate their morphologies, phases and cyclic oxidation behaviors in atmosphere at 1 050℃, compared with the coating without nano-particles. With the addition of nano-particles, the growth pattern of the grains at the interface changed from epitaxial growth to non-epitaxial growth or part-epitaxial growth; slender dendrites were broken and cellularized; cracks and pores were restrained; and the oxidation weight-gain and the stripping resistance of the oxide scale were improved as well. Among the three kinds of nano-particles, the SiC nano-particles showed the most improvement on microstructure, while the CeO2 nano-particles were insufficient, but its effects on the oxidation resistance are the same as those of the SiC nano-particles. Based on the discussions of the influence mechanism, it is believed that CeO2 nano-particles would show better improvement than SiC nano-particles if the proper amount is added and the proper preparation technique of micro-nanometer composite powders is adopted, with the synergistic action of nanometer effect and reactive element effect.
文摘Effects of nano-particle size on hydrocarbon production rates and distributions for precipitated Fe/Cu/La catalysts in Fischer-Tropsch synthesis were investigated.Nano-structured iron catalyst was prepared by micro-emulsion method.The concept of two superimposed AndersonSchulz-Flory (ASF) distributions has been applied for the representation of the effects of reaction conditions and nano-particles size on kinetics parameters and product distributions.These results reveal that by reducing the particle size of catalyst,the break in ASF distributions was decreased.Also useful different kinetics equations for synthesis of C3 to C9 and C10 to C22 were determined by using α1 and α2 chain growth probabilities.
基金Project(51206033)supported by the National Natural Science Foundation of ChinaProjects(2011M500652,2013T60354)supported by the China Postdoctoral Science FoundationProject(2011LBH-Z11139)supported by the Heilongjiang Postdoctoral Science Foundation,China
文摘In order to investigate the effect of additives and nano-particle on the surface tensions of lithium bromide(Li Br) aqueous solution/ammonia, many experiments were carried out based on Wilhelmy plate method. Firstly, the surface tension of Li Br aqueous solution with 1-octanol was measured and then the comparison between the measured results and previous experimental results was given to verify the measuring accuracy. Some new additives, such as cationic surfactants cetyltrimethyl ammonium chloride(CTAC), and cetyltrimethyl ammonium bromide(CTAB) were chosen in the experiments. The experimental results show that CTAC and CTAB can obviously reduce the surface tension of Li Br aqueous solution/ammonia. In addition, it is found that nano-particles cannot remarkably decrease the surface tension of Li Br aqueous solution/ammonia. However, the mixed addition of additives and nano-particles can remarkably affect the surface tension of Li Br aqueous solution/ammonia. That is to say, additives play more important role in reducing the surface tension of Li Br aqueous solution/ammonia. But nano-particles may enhance the heat transfer in the absorption refrigeration process.
基金supported by the National Natural Science Foundation of China (10872203)the National Basic Research Program(2007AC744701)the CAS Research and Development Program of China (KSCX2-YW-H18)
文摘Direct measurement of slip length is based on the measured fluid velocity near solid boundary. However, previous micro particle image velocimetry/particle tracking velocimetry (microPIV/PTV) measurements have reported surprisingly large measured near-wall velocities of pressure-driven flow in apparent contradiction with the no-slip hy-pothesis and experimental results from other techniques. To better interpret the measured results of the microPIV/PTV, we performed velocity profile measurements near a hy-drophilic wall (z = 0.25-1.5 μm) with two sizes of tracer particles (φ 50 nm and φ200 nm). The experimental results indicate that, at less than 1 μm from the wall, the deviations between the measured velocities and no-slip theoretical values obviously decrease from 93% of φ200 nm particles to 48% of φ50 nm particles. The Boltzmann-like exponential measured particle concentrations near wall were found. Based on the non linear Boltzmann distribution of particle concentration and the effective focus plane thickness, we illustrated the reason of the apparent velocity increase near wall and proposed a method to correct the measured velocity profile. By this method, the deviations between the corrected measured velocities and the no-slip theoretical velocity decrease from 45.8% to 10%, and the measured slip length on hy-drophilic glass is revised from 75 nm to 16 nm. These results indicated that the particle size and the biased particle concentration distribution can significantly affect near wall velocity measurement via microPIV/PTV, and result in larger measured velocity and slip length close to wall.
基金This work was financially supported by the National Natural Science Foundation of China (Nos. 20404008, 50373030 and 20490220) the Special Funds for Major State Basic Research Projects of China (No. 2003CB615600) the Ministry of Education of China as a Key Project (No. 104154).
文摘The brittle-ductile transition is a very important phenomenon for polymer toughening. Polypropylene (PP) is often toughened by using rubbers, e.g., ethylene-propylene diene monomer (EPDM) has often been used as a modifier. In this article, the toughening of PP by using a new kind of rubber, known as elastomeric nano-particle (ENP), and the brittleductile transition of PP/EPDM/ENP was studied. Compared to PP/EPDM binary blends, the brittle-ductile transition of PP/EPDM/ENP ternary blends occurred at lower EPDM contents. SEM experiment was carried out to investigate the etched and impact-fractured surfaces. ENP alone had no effect on the impact strength of PP, however, with the same EPDM content, PP/EPDM/ENP ternary blends had smaller particle size, better dispersion and smaller interparticle distance in contrary to PP/EPDM binary blends, which promoted the brittle-ductile transition to occur earlier.
文摘Composites formed by adding nano-scale particles to a polymer matrix results in improving electrical, mechanical, and thermal properties of the composite. Good tribological properties can be obtained for polymers filled with nano-scale fillers compared to that filled with micro-scale particles. The friction and wear resistance of these composites is found to increase with increasing filler concentration. It is also possible to use multi-functional fillers to develop high performance composites which cannot be achieved by using a single filler.
基金Project supported by the National Natural Science Foundation of China(Grant No.11574221)
文摘Particles can be removed from a silicon surface by means of irradiation and a laser plasma shock wave.The particles and silicon are heated by the irradiation and they will expand differently due to their different expansion coefficients,making the particles easier to be removed.Laser plasma can ionize and even vaporize particles more significantly than an incident laser and,therefore,it can remove the particles more efficiently.The laser plasma shock wave plays a dominant role in removing particles,which is attributed to its strong burst force.The pressure of the laser plasma shock wave is determined by the laser pulse energy and the gap between the focus of laser and substrate surface.In order to obtain the working conditions for particle removal,the removal mechanism,as well as the temporal and spatial characteristics of velocity,propagation distance and pressure of shock wave have been researched.On the basis of our results,the conditions for nano-particle removal are achieved.
文摘The change of conductivity and transparency of silver nanowire (AgNW) films by adding silver nano-particles (AgNPs) onto their surface is studied. The results show that the conductivity of the AgNW film is greatly improved with its sheet resistance reduced about 78. 7% to 51.9Ω/sq, and there is no obvious reduction of the transmittance. Further studies show that there is a self-assembling process pushing the AgNPs to concentrate at the intersecting points between AgNWs to weld them, which would reduce the intersection resistance between the AgNWs. This self-assembling behavior is led by the surface interactivities among the dispersing liquid of AgNPs, the surface of the substrate and AgNWs when the dispersing liquid is drying.
文摘γ-Fe nano-particles with size of 20-40 nm were produced by SF6-sensitized CW CO2 laser-induced gaseous pyrolysis of Fe(Co) 5, The γ-Fe stabte in reaction zone at above 910℃ was formed.The rapid quenching prevents from the γ-Fe transforming to α-Fe as rapidly cooling from high temperature to room temperature, The characteristics of the particles were examined at room temperature by TEM. electron diffraction and XRD. It was proved that about 70% of γ-Fe phase in the particles was present. In addition. the lattice constant of the γ-Fe was 0.364 nm in place of 0.360 nm
基金FundedbytheNationalNaturalScienceFoundationofChi na (No .30 30 0 0 78)
文摘The tribological properties of Sialon sliding against AISI52100 steel ball under the lubrication of solid particle additives, as micro-borate particle and nano-PbS particle, were evaluated by a SRV ball-on-disc test rig. The chemical composition of the worn surface was characterized by X-ray photoelectron spectroscopy (XPS). The morphologies of the worn surfaces of Sialon were analyzed by scanning electron microscopy (SEM). The results show that the particles can reduce the friction coefficient of the pairs and the wear volume of Sialon significantly. The wear resistance of micro-borate is superior to that of nano-PbS while the friction-reducing ability of PbS is better than that of borate. According to the XPS and SEM results, the wear resistance of PbS is mainly depended on the tribochemical film mainly composed of PbSO 4, which deposited on the worn surface with good bonding strength. No tribochemical reaction or deposited film was detected or observed on the worn surface of Sialon under the lubrication of borate, indicating that the possible physically deposited film generated from micro particle can also greatly reduce the wear volume of Sialon, though the friction reducing ability of which is inferior to that of nano PbS particle.
基金Sponsored by the National High Technology Research and Development Program of China(863 Program)(Grant No.2006AA06Z303)the National Natural Science Foundation of China(Grant No.50778050)+2 种基金the Key Projects in the National Science & Technology Pillar Program in the Eleventh Five-year Plan Period(Grant No.2006BAJ08B09)the National Creative Research Groups(Grant No.50821002)the Key Scientific and Technological Project of Heilongjiang Province(Grant No.GB06C20403)
文摘To improve the hydrophilicity and anti-fouling performance in water treatment,both entrapped method and deposited method were used to modify polyvinylidene fluoride(PVDF)porous membrane with composite Al2O3/TiO2 nano-particles.Neat PVDF membrane was prepared and its property was also compared with that of the modified membranes.Membrane permeation flux and anti-fouling performance were measured using a membrane cell.The contact angle between water and membrane surface was detected in order to denote the membrane hydrophilicity.Membrane morphology and surface structure were examined by atomic-force microscopy(AFM)and scanning electron microscopy(SEM).Experimental results showed that modified membranes had higher permeation fluxes than that of the neat PVDF membrane.The addition of nano-particles altered membrane surface morphology and increased surface roughness.Due to the hydrophilicity of nano-particles,however,the membrane anti-fouling performance was improved instead of worsened.The entrapped membrane exhibited better anti-fouling performance than the deposited membrane and the neat membrane.
基金Project supported by the National Natural Science Foundation of China (Grant No 10147207).
文摘We have observed the thermodynamic properties of metallic superconductive nano-particles in the grand canonical ensemble; and the level distribution and the level correlation between the discrete electronic energy levels are considered in the calculation of the electronic spin susceptibility of the ensemble numerically. The quantum effect, even-odd effect and other special effects existing in the metallic nano-particles are also studied in this article.
文摘Rutile phase exhibits higher refractive index and h id ing power, good chemical stability, and is becoming a candidate material for the high-temperature separation and catalysis applications. The thermodynamically stable feature of rutile among the three polymorphs of TiO 2 usually hinders ob taining nano-sized rutile phase by a conventional calcining way. However, acid peptization of amorphous TiO 2 is favorable to the formation of rutile phase. I n this work, well-crystallized and well-dispersed rod-like rutile particles w ith specific surface areas of 49.1 and 35.0 m 2/g were prepared by hydrothermal ly treating the acid peptized TiO 2 amorphous sols at relatively low temperatur es of 200 ℃ or 240 ℃, respectively. The formation of non-touching rutile part icles is attributed to high long-range electrostatic forces between particles i n the presence of the high concentration of the peptizer. The acid peptization w ould easily break the ≡Ti-O-Ti≡ bonds to form ≡Ti-OH or HO-Ti-OH species depending on the amount of acid, and create conditions for the formation of rut ile nuclei after structural rearrangements.
基金Funded by the National Natural Science Foundation of China (No. 60372002)
文摘Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,we deeply investigated the optical,electrical and the thermal stability of PEDOT nanoparticles.The main results are as follows: the small-sized PEDOT nanoparticles were prepared and utilized by different methods,such as ultraviolet/visible (UV-Vis) spectroscopy,Fourier-transform infrared (FT- IR) spectrum,scanning electron microscopy(SEM) and so on.The results show that the amount of oxidizer,ultrasonic treatment,polymerizing temperature and doping degree can influent morphology,electrical ability and gas sensitivity of PEDOT nanoparticles.The Bragg peaks of nanoparticles at 6.7°,12.7°,25° were observed by XRD and the better orientation of molecular chain was attributed to the effective doping of toluene-p-sulfonic acid,which also resulted in an enhancement of thermal stability of nanoparticles than conventional PEDOT.
文摘CdS particles were generated in the mixed sodium 10- undecenoate--decyltrmethylammonium bromide vesicle dispersions.Depending on the condition and method of preparation. CdSsemi conductor absorption edges were found to range from 526 to 448 nm, corresponding to particle diameter between >5. 0 and 2. 7 nm.
文摘The paper presents the results of studies surface microrelief, frequency-temperature characteristics of the imaginary part of the dielectric permittivity and dielectric loss of PE+TlInSe2 composite materials in 25。C - 150。C temperature and 25 Hz - 1 MHz frequency range before and after application of the aluminum nano-particles with a size of 50 nm. The change in the amount of semicon-ductor filler TlInSe2 and aluminum nano-particles changes the state of the surface and the frequency-temperature characteristics of composite materials PE+xvol.%TlInSe2, which allows to obtain composites with the desired dielectric permittivity and dielectric loss.
文摘Pure and doped Polyvinylidene difluoride (PVDF) films, for the detection of infrared radiation, have been well documented using the mechanism of pyroelectricity. Alternatively, the electrical properties of films made from Polyvinyl Alcohol (PVA) have received considerable attention in recent years. The investigation of surface resistivities of both such films, to this point, has received far less consideration in comparison to pyroelectric effects. In this research, we report temperature dependent surface resistivity measurements of commercial, and of multiwall carbon nanotubes (MWCNT), or Ag-nanoparticle doped PVA films. Without any variation in the temperature range from 22°C to 40°C with controlled humidity, we found that the surface resistivity decreases initially, reaches a minimum, but rises steadily as the temperature continues to increase. This research was conducted with the combined instrumentation of the Keithley Model 6517 Electrometer and Keithley Model 8009 resistivity test fixture using both commercial and in-house produced organic thin films. With the objective to quantify the suitability of PVDF and PVA films as IR detector materials, when using the surface resistivity phenomenon, instead of or in addition to the pyroelectricity, surface resistivity measurements are reported when considering bolometry. We found that the surface resistivity measurements on PVA films were readily implemented.
基金Funded by the National Natural Science Foundation of China(Nos.51372188 and 51521001)the 111 Project(B13035)+3 种基金the International Science&Technology Cooperation Program of China(2014DFA53090)the Natural Science Foundation of Hubei Province,China(2016CFA006)the National Key Research and Development Program of China(2017YFB0310400)the Fundamental Research Funds for the Central Universities(WUT:2017II43GX,2017III032)
文摘Catalytic direct decomposition of NO by perovskite-type catalysts has attracted much attention for the various possible components and the unique structure. LaCoO_3 nanoparticles were precipitated on a-Al_2O_3 micro powders by rotary chemical vapor deposition(rotary CVD) and its catalytic performance for the decomposition of NO was investigated. LaCoO_3 nano-particles with 100 nm in average diameter and 1.5% in mass were uniformly dispersed on a-Al_2O_3 powder. The conversion of NO increased with increasing temperature from 400 to 950 ℃, and reached 28.7% at 950 ℃. The gas velocity of transformed NO on LaCoO_3 nano-particles catalyst per mass unit was 7.7 mL/(g min), showing a good catalytic activity over the calculated results of pure catalysts. After five times of aging performance experiments, the NO conversion kept the same value, showing a good aging performance and thermal stability.
文摘Bacterial pathogens produced resistance against the existing antimicrobial applications. Scientist trending towards the potent novel eco-friendly and cost effective antimicrobial approaches and fabricating bio-based nano-particles. In this regard, several bio-materials have been investigated, such as, bacteria, fungi, algae, lichens and green plants. Lichens are introduced as an emerging source to synthesis bio-based nano-particles. The lichen-based metal nano-materials, especially fabricated by applying green chemistry strategies, have resulted significant alternates to traditional antimicrobial applications. Several studies break out and revealed that lichen-based nano-particle showed strong antimicrobial efficacy, as the lichens are biologically compatible. Current review summarizes an overview of lichen-based nano-materials, their fabrication, their applications, and their molecular action mechanism. As it emerged a broad spectrum antimicrobial agent for pharmaceutical and agricultural applications.