Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g...Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .展开更多
The effect of hot-forging process was investigated on microstructural and mechanical properties of AZ31 B alloy and AZ31 B/1.5 vol.%Al2 O3 nanocomposite under static and cycling loading. The as-cast alloy and composit...The effect of hot-forging process was investigated on microstructural and mechanical properties of AZ31 B alloy and AZ31 B/1.5 vol.%Al2 O3 nanocomposite under static and cycling loading. The as-cast alloy and composite were firstly subjected to a homogenization heat treatment at 450 ℃ and then an open-die forging at 450 ℃. The results indicated that the presence of reinforcing particles led to grain refinement and improvement of dynamic recrystallization. The forging process was more effective to eliminate the porosity in the cast alloy workpiece. Microhardness of the forged composite was increased by up to 80% and 16%, in comparison with those of the cast and forged alloy samples, respectively. Ultimate tensile strength and maximum tensile strain of the composite were improved by up to 45% and 23%, compared with those of the forged alloy in similar regions. These enhancements were respectively 50% and 37% in the compression test. The composite exhibited a fatigue life improvement in the region with low applied strain;however, a degradation was observed in the high applied strain region. Unlike AZ31 B samples, tensile, compressive and high cycle fatigue behaviors of the composite showed less sensitivity to the applied strain, which can be attributed to the amount of porosity in the samples before and after the hot-forging.展开更多
The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface...The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface dispersed ceria species and crystalline CeO\-2 shows a significant enhancement on the activity. The effect of ceria species is contributed to their promoting the reduction of copper oxide species.展开更多
The selective catalytic reduction(SCR) of NOx using MnOx and CeO2 supported on viscose-based active carbon fibers(ACF) at 120 ℃～270 ℃ relatively lower than the temperature when using V2O5/TiO2-anatase catalyst was ...The selective catalytic reduction(SCR) of NOx using MnOx and CeO2 supported on viscose-based active carbon fibers(ACF) at 120 ℃～270 ℃ relatively lower than the temperature when using V2O5/TiO2-anatase catalyst was studied.As a result,CeO2/ACF shows a better catalysis than MNOx/ACF,which is not affected by the reaction temperature. NO conversion of 85% is reached with the 10%-CeO2/ACF catalyst at the whole temperature window.Furthermore,a series of MnOx-CeO2/ACF composite catalysts were studied.The results show that the loading method of catalyst affects its activity.展开更多
Three kinds of REO modified CeO 2 ZrO 2 solid solutions were prepared by co precipitate method.TPR and XRD measurements have been used to characterize the effect of REO on the thermal stability and oxygen storage prop...Three kinds of REO modified CeO 2 ZrO 2 solid solutions were prepared by co precipitate method.TPR and XRD measurements have been used to characterize the effect of REO on the thermal stability and oxygen storage properties of CeO 2 ZrO 2 solid solutions,comparison being made with unmodified CeO 2 ZrO 2 solid solutions.The results indicated that the addition of REO to CeO 2 ZrO 2 solid solutions obviously improved the oxygen storage properties of the three kinds of solid solutions calcinated at 773K.Except for Zr rich solid solutions,the modified CeO 2 ZrO 2 solid soltuions calcinated at 1173K show higher thermal stability and oxygen storage properties than unmodified solid solutions.展开更多
基金Funded by the National Science Foundation of China ( No.50375037)
文摘Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .
文摘The effect of hot-forging process was investigated on microstructural and mechanical properties of AZ31 B alloy and AZ31 B/1.5 vol.%Al2 O3 nanocomposite under static and cycling loading. The as-cast alloy and composite were firstly subjected to a homogenization heat treatment at 450 ℃ and then an open-die forging at 450 ℃. The results indicated that the presence of reinforcing particles led to grain refinement and improvement of dynamic recrystallization. The forging process was more effective to eliminate the porosity in the cast alloy workpiece. Microhardness of the forged composite was increased by up to 80% and 16%, in comparison with those of the cast and forged alloy samples, respectively. Ultimate tensile strength and maximum tensile strain of the composite were improved by up to 45% and 23%, compared with those of the forged alloy in similar regions. These enhancements were respectively 50% and 37% in the compression test. The composite exhibited a fatigue life improvement in the region with low applied strain;however, a degradation was observed in the high applied strain region. Unlike AZ31 B samples, tensile, compressive and high cycle fatigue behaviors of the composite showed less sensitivity to the applied strain, which can be attributed to the amount of porosity in the samples before and after the hot-forging.
文摘The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface dispersed ceria species and crystalline CeO\-2 shows a significant enhancement on the activity. The effect of ceria species is contributed to their promoting the reduction of copper oxide species.
文摘The selective catalytic reduction(SCR) of NOx using MnOx and CeO2 supported on viscose-based active carbon fibers(ACF) at 120 ℃～270 ℃ relatively lower than the temperature when using V2O5/TiO2-anatase catalyst was studied.As a result,CeO2/ACF shows a better catalysis than MNOx/ACF,which is not affected by the reaction temperature. NO conversion of 85% is reached with the 10%-CeO2/ACF catalyst at the whole temperature window.Furthermore,a series of MnOx-CeO2/ACF composite catalysts were studied.The results show that the loading method of catalyst affects its activity.
文摘Three kinds of REO modified CeO 2 ZrO 2 solid solutions were prepared by co precipitate method.TPR and XRD measurements have been used to characterize the effect of REO on the thermal stability and oxygen storage properties of CeO 2 ZrO 2 solid solutions,comparison being made with unmodified CeO 2 ZrO 2 solid solutions.The results indicated that the addition of REO to CeO 2 ZrO 2 solid solutions obviously improved the oxygen storage properties of the three kinds of solid solutions calcinated at 773K.Except for Zr rich solid solutions,the modified CeO 2 ZrO 2 solid soltuions calcinated at 1173K show higher thermal stability and oxygen storage properties than unmodified solid solutions.