Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g...Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .展开更多
Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. T...Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. The product was characterized by IR,XRD,TEM,Vibrating Sample Magnetometer (VSM),TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe3O4 nanoparticles is also suggested.展开更多
基金Funded by the National Science Foundation of China ( No.50375037)
文摘Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .
文摘Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. The product was characterized by IR,XRD,TEM,Vibrating Sample Magnetometer (VSM),TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe3O4 nanoparticles is also suggested.