Cyanoacrylate adhesive and its composites have been widely used in industry and dentistry. According to literature survey done by the authors, there are few papers concentrated on role of nano-sized particles on wear ...Cyanoacrylate adhesive and its composites have been widely used in industry and dentistry. According to literature survey done by the authors, there are few papers concentrated on role of nano-sized particles on wear behavior of cyanoacrylate glue. Thus the main goal of current research focused on clarifying the role of nano-sized SiO2 on wear behavior of cyanoacrylate. Pin-on-disk wear test, SEM imaging and microhardness test was utilized to investigate wear performance of cyanoacrylate and its nanocomposites with SiO2. The results indicated that SiO2 nano powders can reduce wear rate of cyanoacrylate and change its wear mechanism. It was also shown that surface hardness of cyanoacrylate is increased by addition of nano-sized SiO2.展开更多
Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g...Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .展开更多
文摘Cyanoacrylate adhesive and its composites have been widely used in industry and dentistry. According to literature survey done by the authors, there are few papers concentrated on role of nano-sized particles on wear behavior of cyanoacrylate glue. Thus the main goal of current research focused on clarifying the role of nano-sized SiO2 on wear behavior of cyanoacrylate. Pin-on-disk wear test, SEM imaging and microhardness test was utilized to investigate wear performance of cyanoacrylate and its nanocomposites with SiO2. The results indicated that SiO2 nano powders can reduce wear rate of cyanoacrylate and change its wear mechanism. It was also shown that surface hardness of cyanoacrylate is increased by addition of nano-sized SiO2.
文摘以N,N-二甲基丙烯酰胺(DMAA)及甲基丙烯酸甲酯(MMA)为单体,Irgacure 2959为光引发剂,N,N′-二甲基双丙烯酰胺(Bis)为交联剂,利用紫外光引发自由基聚合制备了聚N,N′-二甲基丙烯酰胺(PDMAA)及P(DMAA-co-MMA)水凝胶,并通过加入少量表面改性后的纳米SiO2对该水凝胶进行改性,制得了P(DMAA-co-MMA)/纳米SiO2复合水凝胶,用FT-IR和SEM对产物进行了表征,同时研究该复合凝胶的溶胀动力学、消溶胀动力学、pH值响应性、离子强度等.该方法简便、快捷,大大缩短了聚合时间,合成过程仅需2—3 min.
基金Funded by the National Science Foundation of China ( No.50375037)
文摘Si3N4-Si2N2O composites were fabricated with amorphous nano-sized silicon nitride powders by the liquid phase sintering （ LPS ）. The Si2 N2O phase was generated by an in-situ reaction 2 Si3 N4 （ s ） ＋ 1.5 02 （ g ） = 3 Si2 N2O （ s ） ＋ N2 （ g ） . The content of Si2 N2 O phase up to 60% in the volume was obtained at a sintering temperature of 1 650℃ and reduced when the sintering temperature increased or decreased, indicating the reaction is reversible. The mass loss, relative density and average grain size increased with increasing the sintering temperature. The average grain size was less than 500 nm when the sintering temperature was below 1 700 ℃. The sintering procedure contains a complex crystallization and a phase transition ： amorphous silicon nitride→equiaxial α- Si3 N4→ equiaxial β- Si3 N4→ rod- like Si2 N2O→ needle- like β- Si3N4 . Small round-shaped β→ Si3 N4 particles were entrapped in the Si2 N2O grains and a high density of staking faults was situated in the middle of Si2 N2O grains at a sintering temperature of 1 650 ℃. The toughness inereased from 3.5 MPa·m^1/2 at 1 600 ℃ to 7.2 MPa· m^1/2 at 1 800 ℃ . The hardness was as high as 21.5 GPa （Vickers） at 1 600 ℃ .