Synthesis of Neodymium-Doped Yttrium Aluminum Garnet (Nd∶YAG) Nano-Sized Powders by Low Temperature Combustion

The homogeneously dispersed, less agglomerated (Nd0.01Y0.99)3Al5O12 nano-sized powders were synthesized by the low temperature combustion (LCS), using Nd2O3, Y2O3, Al(NO3)3·9H2O, ammonia water and citric acid as starting materials. This method effectively solves the problems caused by solid-state reaction at high temperature and hard agglomerates brought by the chemical precipitation method. The powders were characterized by TG-DTA, XRD, FT-IR, TEM respectively and the photoluminescence (PL) spectra of (Nd0.01Y0.99)3Al5O12 green and sintered ceramic disks were measured. The results show that the forming temperature of YAG crystal phase is 850 ℃ and YAP crystal phase appearing during the calcinations transforms to pure YAG at 1050 ℃. The particle size of the powders synthesized by the LCS is in a range of 20～50 nm depending on the thermal treatment temperatures. The effectively induced cross section (σin) with the value 4.03×10-19 cm2 of (Nd0.01Y0.99)3Al5O12 ceramics is about 44% higher than that of single crystal.

Synthesis and Characterization of Nano-sized Boron Powder Prepared by Plasma Torch

Hydrogen thermal plasma jet was employed to prepare nano-sized boron powder with hydrogen reduction of BCI3. The maximum yield of nano-sized boron powders was about 50% with the operational conditions of H2/BCl3 of 4.5：1, total feed of 4.9 m3/h, and plasma power of 25 kW. The samples were analyzed by X-ray diffraction （XRD）, field emission scanning electron microscopy （FE-SEM）, and inductively coupled plasma - mass spectrometry （ICP-MS）, inductively coupled plasma - atomic emission spectrometry （ICP-AES）, inductive combustion infrared absorption （ICIA） and infrared thermal conductivity of oxygen and nitrogen analyzer （ITCA）. The results show that the boron powders have different crystal structures with higher dispersion and purity. The average diameter is about 50 nm, and the purity is 90.29% or so. This new technology can use simple process to produce high quality boron powders, and is feasible for industrial production.

Preparation of ultrafine silver powders with controllable size and morphology

The ultrafine silver powders were prepared by liquid reduction method using Arabic gum as dispersant.The effects of different dispersants,pH values,and temperature on the morphology and particle size of silver powders were investigated.It is found that Arabic gum can better adsorb on silver particles via chemical adsorption,and it shows the best dispersive effect among all the selected dispersants.The particle size of silver powders can be finely tuned from 0.34 to 4.09μm by adjusting pH values,while the morphology of silver powders can be tuned by changing the temperature.The silver powders with high tap density higher than 4.0 g/cm3 were successfully prepared in a wide temperature range of 21.8-70°C.Especially,the tap density is higher than 5.0 g/cm3 when the temperature is optimized to be 50°C.The facile process and high silver concentration of this method make it a promising way to prepare high quality silver powders for electronic paste.

Corrosion resistance of waterborne epoxy coating pigmented by nano-sized aluminium powder on steel

A novel kind of waterborne epoxy coating pigmented by nano-sized aluminium powders on high strength steel was formulated. Several coatings with different pigment volume content (PVC) were prepared. The coating morphology was observed using scanning electron microscopy (SEM), and the electrochemical properties were investigated by electrochemical impedance spectroscopy (EIS). Immersion test and neutral salt spray test were also conducted to investigate the corrosion resistance of the coating. It is demonstrated that the critical pigment volume content (CPVC) value is between 30% and 40%. The coating with PVC of 30% exhibits good corrosion resistance in 3.5% (mass fraction) NaCl solution.

Micro-aluminum powder with bi-or tri-component alloy coating as a promising catalyst:Boosting pyrolysis and combustion of ammonium perchlorate

A novel design of micro-aluminum(μAl)powder coated with bi-/tri-component alloy layer,such as:Ni-P and Ni-P-Cu(namely,Al@Ni-P,Al@Ni-P-Cu,respectively),as combustion catalysts,were introduced to release its huge energy inside Al-core and promote rapid pyrolysis of ammonium perchlorate(AP)at a lower temperature in aluminized propellants.The microstructure of Al@Ni-P-Cu demonstrates that a three-layer Ni-P-Cu shell,with the thickness of~100 nm,is uniformly supported byμAl carrier(fuel unit),which has an amorphous surface with a thickness of~2.3 nm(catalytic unit).The peak temperature of AP with the addition of Al@Ni-P-Cu(3.5%)could significantly drop to 316.2℃ at high-temperature thermal decomposition,reduced by 124.3℃,in comparison to that of pure AP with 440.5℃.It illustrated that the introduction of Al@Ni-P-Cu could weaken or even eliminate the obstacle of AP pyrolysis due to its reduction of activation energy with 118.28 kJ/mol.The laser ignition results showed that the ignition delay time of Al@Ni-P-Cu/AP mixture with 78 ms in air is shorter than that of Al@Ni-P/AP(118 ms),decreased by 33.90%.Those astonishing breakthroughs were attributed to the synergistic effects of adequate active sites on amorphous surface and oxidation exothermic reactions(7597.7 J/g)of Al@Ni-P-Cu,resulting in accelerated mass and/or heat transfer rate to catalyze AP pyrolysis and combustion.Moreover,it is believed to provide an alternative Al-based combustion catalyst for propellant designer,to promote the development the propellants toward a higher energy.

Preparation and Sinterability of Mn-Zn Ferrite Powders by Sol-Gel Method

Mn-Zn spinel ferrites were synthesized by sol-gel method. Effects of calcined temperature on structure and particle size of MnZnFe2O4 were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). XRD patterns indicate that the ultra fine Mn-Zn ferrite exhibits a spinel crystal structure. SEM images show that the powder fired at 900℃for 2 h has an average diameter of 60 ~ 90 nm. The particle size becomes larger with the increasing of calcined temperature and the distribution of particle becomes even more homogeneous. Sintering behaviors of synthesized ferrite powders depend on the powder characteristics and high temperatures have induced the good crystallization of particles.

Preparation of micro-sized and uniform spherical Ag powders by novel wet-chemical method

A novel wet-chemical method was presented for the preparation of the micro-sized and uniform spherical Ag powders on a mass-production scale.The well-defined particles were synthesized by mixing the iron(II) sulfate heptahydrate solution with silver nitrate solution directly by high-speed stirring at room temperature.It is found that a large number of micro-sized and uniform spherical particles with rough surfaces are obtained.The mass ratio of iron(II) sulfate heptahydrate to silver nitrate greatly affects the shape of particles,and when it is relatively low,spherical particles cannot be obtained.The reaction temperature has a great impact on the particle size.As the reaction temperature increases from 8 to 15°C,the mean diameter of particles decreases from 3.5 to 1.6 μm.The additive n-methyl-2-pyrrolidone improves the surface smoothness and compactness of the particles while the particle size is kept unchanged.Scanning electron microscopy,X-ray diffractometry and energy dispersive X-ray analysis were used to characterize the particle products.

Fabrication and Characterization of Nano Silver Powder Prepared by Spray Pyrolysis

Silver powder was fabricated by spray pyrolysis, using 2%-20% AgNO3 solution, 336-500 mL/h flux of AgNO3 solution, 0.28-0.32 MPa flux of carrier gas and in the 620-820 ℃ temperature range. The effects of furnace set temperature, concentration of AgNO3 aqueous solution, flux of AgNO3 aqueous solution as well as carrier gas on the morphology and particle size distribution of silver powder, were investigated. The experimental results showed that with the high concentration of AgNO3 aqueous solution, the average grain size of silver decreased with the increasing of furnace set temperature. But the gain size distribution was not homogenous, the discontinuous grain growth occurred. With the low concentration of AgNO3 aqueous solution, the higher furnace set temperature made the nano sliver grains sintered together to grow. Nano silver powder about 100 nm was fabricated by spray pyrolysis, using 2wt% AgNO3 solutions, 336 mL/h flux of AgNO3 aqueous solution, 0.32 MPa flux of carrier gas at 720 ℃ furnace set temperature.

Preparation of flake AgSnO_2 composite powders by hydrothermal method

Silver-tin oxide composite powders and silver powders were synthesized by hydrothermal method using NH3 to complex Ag+, SO 32?to reduce Ag (NH3)+2 and Na2SnO3 as the source of tin. The powders were characterized by XRD, SEM and EDX. The results show that there are macroscopic and microscopic differences between two kinds of powders. Spherical silver powders are 3 μm in diameter, and silver-tin oxide composite powders are mainly flake of about 0.3 μm in thickness. Silver crystal in silver-tin oxide composite powders is preferentially oriented in the (111) crystallographic direction and its oriented index is 2.581. Crystal lattice parameter of silver crystal of silver tin-oxide composite powders is 0.409 34 nm, larger than 0.408 68 nm of silver powders. The XPS analysis shows that silver in silver-tin oxide composite powders is metallic silver and tin oxide in silver tin-oxide composite powders has the red shift for Sn4+(3d5/2) and O2-(1s).

PREPARATION OF SILVER POWDER FOR CONDUCTIVE PASTE

ＰＲＥＰＡＲＡＴＩＯＮＯＦＳＩＬＶＥＲＰＯＷＤＥＲＦＯＲＣＯＮＤＵＣＴＩＶＥＰＡＳＴＥＣｈａｉ，Ｌｉｙｕａｎ；Ｚｈｏｎｇ，Ｈａｉｙｕｎ；Ｗｕ，Ｈｕｉｙｕｎ（ＤｅｐａｒｔｍｅｎｔｏｆＮｏｎｆｅｒｒｏｕｓＭｅｔａｌｌｕｒｇｙ，ＣｅｎｔｒａｌＳｏｕｔｈＵｎ...

A Facile Route for Synthesis of LiFePO_4/C Cathode Material with Nano-sized Primary Particles

A facile and practical route was introduced to prepare LiFePO4/C cathode material with nano-sized primary particles and excellent electrochemical performance. LiH2PO4 was synthesized by using H3PO4 and LiOH as raw materials. Then, as-prepared LiH2PO4, reduced iron powder andα-D-glucose were ball-milled, dried and sin-tered to prepare LiFePO4/C. X-ray diffractometry was used to characterize LiH2PO4, ball-milled product and LiFePO4/C. Differential scanning calorimeter-thermo gravimetric analysis was applied to investigate possible reac-tions in sintering and find suitable temperature for LiFePO4 formation. Scanning electron microscopy was em-ployed for the morphology of LiFePO4/C. As-prepared LiH2PO4 is characterized to be in P21cn（33） space group, which reacts with reduced iron powder to form Li3PO4, Fe3（PO4）2 and H2 in ball-milling and sintering. The appro-priate temperature for LiFePO4/C synthesis is 541.3-976.7 ℃. LiFePO4/C prepared at 700 ℃ presents nano-sized primary particles forming aggregates. Charge-discharge examination indicates that as-prepared LiFePO4/C displays appreciable discharge capacities of 145 and 131 mA·h·g^-1 at 0.1 and 1 C respectively and excellent discharge ca-pacity retention.

Effect of Water Chestnut Powder on Gel Properties of Silver Carp Surimi

[Objectives]The effects of water chestnut powder on the gel properties and quality of silver carp surimi were investigated.[Methods]The surimi gel was prepared by adding 0%,1%,2%,3%,4%and 5%of water chestnut powder to the surimi of silver carp.The gel properties,water-holding capacity,cooking loss,whiteness value,puncture and texture profile analysis(TPA)indexes of surimi products were determined to assess the effects of adding different amounts of water chestnut powder on surimi gel.[Results]The results showed that the gel strength,breaking force and depression distance of surimi products increased first and then decreased with the increase of the addition of water chestnut powder.Compared with the control group,the hardness and chewiness of surimi gel in TPA could be significantly improved by adding water chestnut powder.When the addition of water chestnut powder was 2%,the maximum water-holding capacity was 83.68%;the cooking loss rate was the lowest;and the whiteness value was the highest.Adding 2%of water chestnut powder could significantly improve the gel properties of silver carp surimi and obtain a good gel product.[Conclusions]This study provides a scientific basis for the effective utilization of water chestnut resources and the development of new fish surimi products.

Preparation of titanium dioxide/silver sulfate powder and its antibacterial activity

Antibacterial powders of titanium dioxide/silver sulfate were produced by heat-treatment of the metatitanic acid, as precursor, into which the silver nitrate was added. The influences of heating temperature on the structure and composition of the product were investigated through XRD and SEM. The results show that the powder is spherical in the phase of TiO2-Ag2SO4. The granularity of the particles increases from 10.7nm to 28.7nm with the temperature of heat-treatment increasing from 300℃ to 800℃. The antibacterial activity of the powder was judged in the way of the minimum inhibitory contents （MiCs）. When the content of silver sulfate is less than 2%, the photocatalysis of titanium dioxide and silver ions cooperate to kill bacteria. And the MiCs decrease and keep around 1.0×10 -41.5×10 -4 constantly with the increase of silver content. Furthermore, the MiCs decrease with the increase of temperature of heat-treatment when the temperature is lower than 500℃. But when the temperature is beyond 600℃ the MiCs increase quickly, which shows the inferior antibacterial performance.

Silver removal from molten lead through zinc powder injection

A silver removal process was carried out on a Pb-Ag alloy through zinc powder injection of three different sizes （3.55, 44.4 and 734.8μm） with a top submerged lance using nitrogen as carrying gas. The higher silver removal was obtained for the zinc powder size of 44.4μm, while the lowest silver removal efficiency was attained for the smaller particle size. The AgZn phase was detected in the slag for the 44.4 and 734.8μm particle sizes by XRD, which was in agreement with SEM-EDS analysis. Experimental behavior was explained according to the melting and residence time of the injected particles.

Study on Properties of Silver Powder for Maki-e

Maki-e is a traditional Japanese decorative technique that uses the natural lacquer Urushi and metal powders. In 2014, there exist only two companies that manufacture silver powder for the purpose of Maki-e, and this study focuses on comparing the powders manufactured by them. Gloss and color of each silver powder were measured after Maki-e decoration was finished, and EDS (energy-dispersive X-ray spectroscopy) was used to determine the differences in their chemical composition. In addition, to verify the effect of polishing, residual gloss after sulfuration and polishing was measured. The study revealed that the shapes of the silver powders (Maru-fun, No. 1) manufactured by the two companies are different and it affects the occupancy rate of Urushi and powder, which in turn affects their gloss and color. Wakou silver has a very strong resistance to sulfuration;however, owing to its Pd content, its chroma is much lower than that of other powders. It was shown that sulfuration on powder surface can be removed by polishing irrespective of the shape and chemical composition ratio of the particles.

Effects of Supplemental Amount of Tuanfeng Lotus Seed Powder on Quality of Silver Carp Surimi Products

[Objectives]This study was conducted to improve the gel properties of freshwater surimi and its products. [Methods] Tuanfeng lotus seed powder was added to frozen silver carp, and the relationship between the addiamount of Tuanfeng lotus seed powder(1%, 2%, 3%, 4% and 5%) and the quality of surimi products was studied, so as to improve the quality of surimi products. [Results] The water holding capacity(86.71%±0.36%), hardness(3 566.64±51.15) g, chewiness(2 697.16±15.81) g and gel strength(692.54±23.19) of surimi products increased to the maximums when the addition amount of lotus seed powder was 3%. Meanwhile, the cooking loss rate was reduced to the minimum(13.00%±0.17%), and the sensory quality was the best, although the whiteness of surimi products decreased slightly with the increase of Tuanfeng lotus seed powder. Therefore, the quality of silver carp surimi products could be improved obviously when the dosage of Tuanfeng lotus seed powder was 3%. [Conclusions] This study provides more new ideas for improving the quality of silver carp surimi products, and simultaneously makes the development of lotus seed food more diversified.

枸杞粉对白鲢鱼糜凝胶品质的影响

该研究以冷冻白鲢鱼糜为实验原料,向其中添加枸杞粉(wolfberry powder,WP),分析不同添加量[0.25%、0.5%、0.75%、1%、1.5%(质量分数)]的WP对白鲢鱼糜凝胶持水性、蒸煮损失率、白度值、水分分布、凝胶特性、微观结构、感官评价及气味特征的影响。结果表明,随着WP含量的增加,鱼糜凝胶的持水性、硬度、咀嚼性和凝胶强度都表现出先增大后减小的趋势,当WP的添加量为0.5%时达到最大,分别为78.55%、(2716.77±75.76)g、(2185.15±32.46)g和1087 g·cm;而蒸煮损失率则表现出先减小后增大的趋势,在0.5%的添加量时,蒸煮损失率最小,为7.49%。在鱼糜中加入WP后,可以减少鱼糜凝胶中自由水的比例,增加不易流动水的比例,使鱼糜凝胶保留更多水分,且当WP在最适添加量0.5%时,鱼糜凝胶中只检测到结合水和不易流动水,未检测到自由水。适量WP的添加会增强鱼糜凝胶的网络结构,使其变得更加致密均匀。WP的添加会减小鱼糜凝胶的白度值和色泽评分,但在最适添加量0.5%时,其颜色总体可接受。此外,感官评价和电子鼻分析结果表明,当WP在最适添加量0.5%时,可以显著改善鱼糜凝胶的风味品质。研究结果可为生产高品质的鱼糜产品提供理论依据。

银粉对硅异质结太阳电池用低温银浆的影响综述

银浆是硅异质结太阳电池的重要材料,更低的体积电阻率和接触电阻、良好的附着力、优良的细线印刷性能及组件栅线抗腐蚀老化是其不断改进的方向。作为导电相,银粉的性能和含量对银浆有着至关重要的影响。该文基于低温固化银浆导电机理以及SHJ电池对银浆性能的追求,综述了银粉的振实密度、形貌、粒径、表面处理剂及其与有机物的适配。进一步探讨了纳米银粉和银包铜粉在SHJ太阳电池用低温银浆中的应用。

非水溶液体系中晶种法制备球形银纳米颗粒

以丙三醇作溶剂,硝酸银为原料,聚乙烯吡咯烷酮(PVP)为分散剂,硼氢化钠为还原剂制备了银纳米晶种;以此银纳米粒子作为初级晶种,以丙三醇作溶剂和还原剂,通过升温提高丙三醇的还原性制备银纳米颗粒。研究分散剂种类、生长液银浓度、晶种加入量对银粉的影响,采用X射线粉末衍射仪(XRD)、场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)对制备产物的结构、物相、形貌进行表征。结果表明,通过改变条件可以制备出分散性良好、粒径均匀的70nm左右的球形银粉。

高功率半导体用纳米银焊膏的研究现状

第3代半导体作为核心部件,使得更紧凑、高频率、高功率的电子器件在射频和微波电子、能源转换与储存、雷达和通信等领域展现出广泛的应用潜力。然而,高性能电子器件对其封装材料的导电性、导热性以及连接处的机械性能提出了更为严格的要求。纳米银焊膏因其卓越的低温烧结性能和在高温环境下的出色表现引起了广泛关注。然而,国内银粉和银焊膏产品的质量相对较低,且研发过程缺乏理论指导,必须依赖进口材料。基于高功率半导体用纳米银焊膏,综述了通过液相化学还原法合成纳米银粉的研究进展,以及纳米银焊膏的烧结机理、影响其性能的因素和控制方法,有望为国内纳米银焊膏的研发和生产提供有益的指导和支持。