The Al_2O_3-（W,Ti）C composites with Ni and Mo additions varying from 0vol% to 12vol% were prepared via hot pressing sintering under 30 MPa. The microstructure was investigated via X-ray diffraction（XRD） and scanni...The Al_2O_3-（W,Ti）C composites with Ni and Mo additions varying from 0vol% to 12vol% were prepared via hot pressing sintering under 30 MPa. The microstructure was investigated via X-ray diffraction（XRD） and scanning electron microscopy（SEM） equipped with energy dispersive spectrometry（EDS）. Mechanical properties such as flexural strength, fracture toughness, and Vickers hardness were also measured. Results show that the main phases A12O3 and（W,Ti）C were detected by XRD. Compound Mo Ni also existed in sintered nanocomposites. The fracture modes of the nanocomposites were both intergranular and transgranular fractures. The plastic deformation of metal particles and crack bridging were the main toughening mechanisms. The maximum flexural strength and fracture toughness were obtained for 9vol% and 12vol% additions of Ni and Mo, respectively. The hardness of the composites reduced gradually with increasing content of metals Ni and Mo.展开更多
Cubic silicon nitride(-Si_(3)N_(4))is superhard and one of the hardest materials after diamond and cubic boron nitride(cBN),but has higher thermal stability in an oxidizing environment than diamond,making it a competi...Cubic silicon nitride(-Si_(3)N_(4))is superhard and one of the hardest materials after diamond and cubic boron nitride(cBN),but has higher thermal stability in an oxidizing environment than diamond,making it a competitive candidate for technological applications in harsh conditions(e.g.,drill head and abrasives).Here,we report the high-pressure synthesis and characterization of the structural and mechanical properties of a γ-Si_(3)N_(4)/Hf_(3)N_(4) ceramic nanocomposite derived from single-phase amorphous silicon(Si)-hafnium(Hf)-nitrogen(N)precursor.The synthesis of the-Si_(3)N_(4)/Hf_(3)N_(4) nanocomposite is performed at~20 GPa and ca.1500 ℃ in a large volume multi anvil press.The structural evolution of the amorphous precursor and its crystallization to-Si_(3)N_(4)/Hf_(3)N_(4) nanocomposites under high pressures is assessed by the in situ synchrotron energy-dispersive X-ray diffraction(ED-XRD)measurements at~19.5 GPa in the temperature range of ca.1000-1900℃.The fracture toughness(K_(IC))of the two-phase nanocomposite amounts~6/6.9 MPa·m^(1/2) and is about 2 times that of single-phaseγ-Si_(3)N_(4),while its hardness of ca.30 GPa remains high.This work provides a reliable and feasible route for the synthesis of advanced hard and tough-Si_(3)N_(4)-based nanocomposites with excellent thermal stabililty.展开更多
The fabrication of carbon nanotube(CNT)-reinforced ceramic nanocomposites through laser sintering has been rarely studied,and the fabrication feasibility has been rarely tested.Laser sintering is a flexible,localized ...The fabrication of carbon nanotube(CNT)-reinforced ceramic nanocomposites through laser sintering has been rarely studied,and the fabrication feasibility has been rarely tested.Laser sintering is a flexible,localized and high-precision process,which can also potentially produce coatings or parts with complicated shapes and/or spatially controlled compositions.Therefore,compared with other technologies laser sintering has its own advantages.Experimental investigations reported in this paper have confirmed the feasibility of fabricating CNT-reinforced ceramic nanocomposites through laser sintering of ceramic nanoparticles and CNTs.The studies show that laser sintering can induce the agglomeration of ceramic nanoparticles into a relatively more continuous ceramic phase,and during the sintering process CNTs are well preserved without any obvious quality degradation,and they are also bonded with the ceramic phase after laser sintering.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51475273)
文摘The Al_2O_3-（W,Ti）C composites with Ni and Mo additions varying from 0vol% to 12vol% were prepared via hot pressing sintering under 30 MPa. The microstructure was investigated via X-ray diffraction（XRD） and scanning electron microscopy（SEM） equipped with energy dispersive spectrometry（EDS）. Mechanical properties such as flexural strength, fracture toughness, and Vickers hardness were also measured. Results show that the main phases A12O3 and（W,Ti）C were detected by XRD. Compound Mo Ni also existed in sintered nanocomposites. The fracture modes of the nanocomposites were both intergranular and transgranular fractures. The plastic deformation of metal particles and crack bridging were the main toughening mechanisms. The maximum flexural strength and fracture toughness were obtained for 9vol% and 12vol% additions of Ni and Mo, respectively. The hardness of the composites reduced gradually with increasing content of metals Ni and Mo.
基金Part of this research was carried out at PETRA III LVP at beamline P61B(beamtime I-20200434)and P02.1Shrikant Bhat and Robert Farla acknowedge the support from the Federal Ministry of Education and Research,Germany(BMBF,Nos.05K16WC2 and 05K13WC2)+2 种基金Wei Li and Leonore Wiehl also acknowledge the travel support from DESY.Zhaoju Yu thanks the National Natural Science Foundation of China(Nos.51872246 and 52061135102)for financial supportMarc Widenmeyer and Anke Weidenkaff are grateful for the financial support by the German Ministry of Education and Research(No.03SF0618B)Wei Li acknowledges the financial support from China Scholarship Council(No.201907040060).
文摘Cubic silicon nitride(-Si_(3)N_(4))is superhard and one of the hardest materials after diamond and cubic boron nitride(cBN),but has higher thermal stability in an oxidizing environment than diamond,making it a competitive candidate for technological applications in harsh conditions(e.g.,drill head and abrasives).Here,we report the high-pressure synthesis and characterization of the structural and mechanical properties of a γ-Si_(3)N_(4)/Hf_(3)N_(4) ceramic nanocomposite derived from single-phase amorphous silicon(Si)-hafnium(Hf)-nitrogen(N)precursor.The synthesis of the-Si_(3)N_(4)/Hf_(3)N_(4) nanocomposite is performed at~20 GPa and ca.1500 ℃ in a large volume multi anvil press.The structural evolution of the amorphous precursor and its crystallization to-Si_(3)N_(4)/Hf_(3)N_(4) nanocomposites under high pressures is assessed by the in situ synchrotron energy-dispersive X-ray diffraction(ED-XRD)measurements at~19.5 GPa in the temperature range of ca.1000-1900℃.The fracture toughness(K_(IC))of the two-phase nanocomposite amounts~6/6.9 MPa·m^(1/2) and is about 2 times that of single-phaseγ-Si_(3)N_(4),while its hardness of ca.30 GPa remains high.This work provides a reliable and feasible route for the synthesis of advanced hard and tough-Si_(3)N_(4)-based nanocomposites with excellent thermal stabililty.
文摘The fabrication of carbon nanotube(CNT)-reinforced ceramic nanocomposites through laser sintering has been rarely studied,and the fabrication feasibility has been rarely tested.Laser sintering is a flexible,localized and high-precision process,which can also potentially produce coatings or parts with complicated shapes and/or spatially controlled compositions.Therefore,compared with other technologies laser sintering has its own advantages.Experimental investigations reported in this paper have confirmed the feasibility of fabricating CNT-reinforced ceramic nanocomposites through laser sintering of ceramic nanoparticles and CNTs.The studies show that laser sintering can induce the agglomeration of ceramic nanoparticles into a relatively more continuous ceramic phase,and during the sintering process CNTs are well preserved without any obvious quality degradation,and they are also bonded with the ceramic phase after laser sintering.