（ CdS/ TiO2 ）/ MCM-41 loaded nanometer photocatalyst was prepared by the sol-gel method and dipping process, the photocatalytic degradation of methyl thionine chloride in water was investigated by using the photocat...（ CdS/ TiO2 ）/ MCM-41 loaded nanometer photocatalyst was prepared by the sol-gel method and dipping process, the photocatalytic degradation of methyl thionine chloride in water was investigated by using the photocatalyst. The experimental results show that the optimum concentration of CdS over TiO2 was 3% （ molar ratio ）, the photocatalytic activity was enhanced when making TiO2 the anatase ptase with a rise of the roasting temperature, and the carrier, mesoporous molecular sieve MCM-41, was beneficial to improving the photocatalytic activity of TiO2 for photocatalytic degradation of methyl thionine chloride. The morphology and the crystalline phase of the photocatalyst were discussed by means of XRD and SEM techniques, and the reaction mechanism of catalytic properties was also discussed.展开更多
制备了不同Al含量的Al-MCM-41试样,其中Si/Al比值最小为3,即最高含铝量xAl=0.303.X射线粉末衍射（XPD）分析表明样品具有MCM-41的特征结构,氮气吸附研究表明,样品呈现Ⅳ型吸附等温线,具有孔径分布均一的中孔结构.文中还利用27Al MAS NM...制备了不同Al含量的Al-MCM-41试样,其中Si/Al比值最小为3,即最高含铝量xAl=0.303.X射线粉末衍射（XPD）分析表明样品具有MCM-41的特征结构,氮气吸附研究表明,样品呈现Ⅳ型吸附等温线,具有孔径分布均一的中孔结构.文中还利用27Al MAS NMR研究了试样中Al的化学环境,结果表明,即使在高铝含量的情况下,样品中的铝原子仍以四配位结合在MCM-41的硅骨架上,未能检测出骨架外六配位铝的存在.文中还就Al含量对孔结构的影响以及Al-MCM-41形成机理作了讨论.展开更多
基金Funded by Special Fund of Education Department of ShaanxiProvince(No.03JK144)
文摘（ CdS/ TiO2 ）/ MCM-41 loaded nanometer photocatalyst was prepared by the sol-gel method and dipping process, the photocatalytic degradation of methyl thionine chloride in water was investigated by using the photocatalyst. The experimental results show that the optimum concentration of CdS over TiO2 was 3% （ molar ratio ）, the photocatalytic activity was enhanced when making TiO2 the anatase ptase with a rise of the roasting temperature, and the carrier, mesoporous molecular sieve MCM-41, was beneficial to improving the photocatalytic activity of TiO2 for photocatalytic degradation of methyl thionine chloride. The morphology and the crystalline phase of the photocatalyst were discussed by means of XRD and SEM techniques, and the reaction mechanism of catalytic properties was also discussed.
文摘制备了不同Al含量的Al-MCM-41试样,其中Si/Al比值最小为3,即最高含铝量xAl=0.303.X射线粉末衍射（XPD）分析表明样品具有MCM-41的特征结构,氮气吸附研究表明,样品呈现Ⅳ型吸附等温线,具有孔径分布均一的中孔结构.文中还利用27Al MAS NMR研究了试样中Al的化学环境,结果表明,即使在高铝含量的情况下,样品中的铝原子仍以四配位结合在MCM-41的硅骨架上,未能检测出骨架外六配位铝的存在.文中还就Al含量对孔结构的影响以及Al-MCM-41形成机理作了讨论.