Two kinds of TiO_2 nanometer thin films were prepared on stainless steel bythe reverse micellar and sol-gel methods, respectively. The calcined TiO_ 2 thin films werecharacterized by X-ray diffraction (XRD), atomic fo...Two kinds of TiO_2 nanometer thin films were prepared on stainless steel bythe reverse micellar and sol-gel methods, respectively. The calcined TiO_ 2 thin films werecharacterized by X-ray diffraction (XRD), atomic force microscopy (AFM), BET surface area and X-rayphotoelectron spectroscopy (XPS). Photocatalytic activity was evaluated by photocatalyticdecoloration of methyl orange aqueous solution. The results showed that the TiO_2 thin filmsprepared by reverse micellar method (designated as RM-TiO_2 films) showed higher photocatalyticactivity than those by sol-gel method (designated as SG-TiO_2 films). This is attributed to the factthat the former is composed of smaller monodispersed spherical particles with a size of about 15 nmand possesses higher surface areas.展开更多
The transparent anatase TiO 2 nanometer thin films were prepared by the sol-gel method on soda-lime glass.X-ray diffraction,thermal analysis and UV-visible spectrophotometer were used to analyze the formation of the ...The transparent anatase TiO 2 nanometer thin films were prepared by the sol-gel method on soda-lime glass.X-ray diffraction,thermal analysis and UV-visible spectrophotometer were used to analyze the formation of the phases.Only increasing the heat-treatment time,the average grain size has no obvious change.The mechanism of grain growth in TiO 2 thin film is probably as follows:the grain of coating will become grain core later;TiO 2 sol constantly deposited on the surface of TiO 2 grain and formed membrane with increasing of coating cycle times;TiO 2 grain in the film grow steadily.展开更多
基金This project is financially supported by the National Natural Science Foundation of China (No.s 50272049, 50072016) The Excellent Young Teachers Program of MOE, China (No. (2002)350)
文摘Two kinds of TiO_2 nanometer thin films were prepared on stainless steel bythe reverse micellar and sol-gel methods, respectively. The calcined TiO_ 2 thin films werecharacterized by X-ray diffraction (XRD), atomic force microscopy (AFM), BET surface area and X-rayphotoelectron spectroscopy (XPS). Photocatalytic activity was evaluated by photocatalyticdecoloration of methyl orange aqueous solution. The results showed that the TiO_2 thin filmsprepared by reverse micellar method (designated as RM-TiO_2 films) showed higher photocatalyticactivity than those by sol-gel method (designated as SG-TiO_2 films). This is attributed to the factthat the former is composed of smaller monodispersed spherical particles with a size of about 15 nmand possesses higher surface areas.
文摘The transparent anatase TiO 2 nanometer thin films were prepared by the sol-gel method on soda-lime glass.X-ray diffraction,thermal analysis and UV-visible spectrophotometer were used to analyze the formation of the phases.Only increasing the heat-treatment time,the average grain size has no obvious change.The mechanism of grain growth in TiO 2 thin film is probably as follows:the grain of coating will become grain core later;TiO 2 sol constantly deposited on the surface of TiO 2 grain and formed membrane with increasing of coating cycle times;TiO 2 grain in the film grow steadily.