Nanoscale bimetallic Ni/Fe particles were synthesized from the reaction of sodium borohydride (NaBH4) with reduction of Ni^2+ and Fe^2+ in aqueous solution. The obtained Ni/Fe particles were characterized by TEM ...Nanoscale bimetallic Ni/Fe particles were synthesized from the reaction of sodium borohydride (NaBH4) with reduction of Ni^2+ and Fe^2+ in aqueous solution. The obtained Ni/Fe particles were characterized by TEM (transmission electron microscope), XRD (X-ray diffractometer), and N2-BET. The dechlorination activity of the Ni/Fe was investigated using p-chlorophenol (p-CP) as a probe agent. Results demonstrated that the nanoscale Ni/Fe could effectively dechlorinate p-CP at relatively low metal to solution ratio of 0.4 g/L (Ni 5 wt%). The target with initial concentration ofp-CP 0.625 mmol/L was dechlorinted completely in 60 rain under ambient temperature and pressure. Factors affecting dechlorination efficiency, including reaction temperature, pH, Ni loading percentage over Fe, and metal to solution ratio, were investigated. The possible mechanism of dechlorination ofp-CP was proposed and discussed. The pseudo-first- order reaction took place on the surface of the Ni/Fe bimetallic particles, and the activation energy of the dechlorination reaction was determined to be 21.2 kJ/mol at the temperature rang of 287-313 K.展开更多
Nanoscale Pd/Fe bimetallic particles were synthesized with an efficient method to dechlorinate o-chlorophenol. The nanoscale Pd/Fe particles were determined by transmission electron microscopy and BET specific surface...Nanoscale Pd/Fe bimetallic particles were synthesized with an efficient method to dechlorinate o-chlorophenol. The nanoscale Pd/Fe particles were determined by transmission electron microscopy and BET specific surface area analysis. Most of the particles are in the size range of 20—100 nm. The BET specific surface area of synthesized nanoscale Pd/Fe particles is 12.4 m 2/g. In contrast, a commercially available fine iron powder(<100 mesh) has a specific surface area of 0.49 m 2/g. Batch studies demonstrated that the nanoscale particles can effectively dechlorinate o-chlorophenol. The dechlorination reaction takes place on the surface of synthesized nanoscale Pd/Fe bimetallic particles in a pseudo-first order reaction. The surface-area-normalized rate coefficients(k_ SA) are comparable to those reported in the literature for chlorinated ethenes. The observed reaction rate constants(k_ obs) are dominated by the mass fraction of Pd and the mass concentration of the nanoscale Pd/Fe particles.展开更多
基金Project(51974048) supported by the National Natural Science Foundation of ChinaProject(CQBX202225) supported by Postdoctoral Innovation Talent Program of Chongqing,ChinaProject(CSTB2023NSCQ-BHX0166) supported by Natural Science Foundation of Chongqing,China。
基金Project supported by the National Basic Research Program (973) of China(No. 2003CB415006)the National Natural Science Foundation of China (No. 20337020)
文摘Nanoscale bimetallic Ni/Fe particles were synthesized from the reaction of sodium borohydride (NaBH4) with reduction of Ni^2+ and Fe^2+ in aqueous solution. The obtained Ni/Fe particles were characterized by TEM (transmission electron microscope), XRD (X-ray diffractometer), and N2-BET. The dechlorination activity of the Ni/Fe was investigated using p-chlorophenol (p-CP) as a probe agent. Results demonstrated that the nanoscale Ni/Fe could effectively dechlorinate p-CP at relatively low metal to solution ratio of 0.4 g/L (Ni 5 wt%). The target with initial concentration ofp-CP 0.625 mmol/L was dechlorinted completely in 60 rain under ambient temperature and pressure. Factors affecting dechlorination efficiency, including reaction temperature, pH, Ni loading percentage over Fe, and metal to solution ratio, were investigated. The possible mechanism of dechlorination ofp-CP was proposed and discussed. The pseudo-first- order reaction took place on the surface of the Ni/Fe bimetallic particles, and the activation energy of the dechlorination reaction was determined to be 21.2 kJ/mol at the temperature rang of 287-313 K.
文摘Nanoscale Pd/Fe bimetallic particles were synthesized with an efficient method to dechlorinate o-chlorophenol. The nanoscale Pd/Fe particles were determined by transmission electron microscopy and BET specific surface area analysis. Most of the particles are in the size range of 20—100 nm. The BET specific surface area of synthesized nanoscale Pd/Fe particles is 12.4 m 2/g. In contrast, a commercially available fine iron powder(<100 mesh) has a specific surface area of 0.49 m 2/g. Batch studies demonstrated that the nanoscale particles can effectively dechlorinate o-chlorophenol. The dechlorination reaction takes place on the surface of synthesized nanoscale Pd/Fe bimetallic particles in a pseudo-first order reaction. The surface-area-normalized rate coefficients(k_ SA) are comparable to those reported in the literature for chlorinated ethenes. The observed reaction rate constants(k_ obs) are dominated by the mass fraction of Pd and the mass concentration of the nanoscale Pd/Fe particles.