Nanosized ZrO2 powder was prepared by evaporative decomposition of solution（EDS）. The particle size is from 50 nm to 200 nm. This process has such advantages as high purity, precise compositional control, simple pro...Nanosized ZrO2 powder was prepared by evaporative decomposition of solution（EDS）. The particle size is from 50 nm to 200 nm. This process has such advantages as high purity, precise compositional control, simple procedure and successive auto-operating. In this process, mixed solution of zirconium acetate and yttrium nitrate was atomized to from a fine mist and blown into the hot zone from the bottom of furnace. The solution was rapidly decomposed at 900℃ and the powder was collected by a filter system. The powder characteristics can be controlled by adjusting the concentration, droplet volume and decomposition temperature of the solution.展开更多
Ce Zr O solid solution was prepared by four different methods, i.e., decomposition of nitrate, coprecipiation, hydroxysuainic acid sol gel as well as citrate sol gel, and characterized by using X ray powder diffr...Ce Zr O solid solution was prepared by four different methods, i.e., decomposition of nitrate, coprecipiation, hydroxysuainic acid sol gel as well as citrate sol gel, and characterized by using X ray powder diffraction, Raman and temperature programmed reduction. The phase composition and the reduction properties of Ce Zr O depend on the preparation method. A cubic Ce 0.5 Zr 0.5 O 2 solid solution can be obtained by using the sol gel method. The Ce Zr O solid solution prepared by using decomposition or coprecipiation was composed of cubic Ce 0.8 Zr 0.2 O 2 and tetragonal Ce 0.2 Zr 0.8 O 2 solid solution. The Ce Zr O solid solution prepared with different methods shows the different reduction properties owing to different phase composition. Results of differential thermal analysis and XRD show that Ce 0.5 Zr 0.5 O 2 solid solution is formed during the decomposition or combustion of the gel.展开更多
Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characte...Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characteristics was calculated in the present investigation. The microstructure and properties of the synthesized Cu/Al2O3 were studied. The results show that high-energy milling can obviously promote internal oxidation of Al in Cu-Al powders in the same solid solubility. At the same milling conditions and internal oxidation parameters, the solid solution of Al in Cu either in low or high amount will result in the poor microstructure and properties of the Cu/Al2O3 composite. Subsequently, when high-energy milling and internal oxidation are synchronously used to prepare the Cu/Al2O3 composite, there should be an appropriate solubility and milling effect for the pre-alloyed powders.展开更多
Single-phase homogeneous Ce1-x ZrxO2 solid versed microemulsion method. The structural properties solutions with various compositions were synthesized using the reand performance of Ce1- xZrxO2 were studied using XRD,...Single-phase homogeneous Ce1-x ZrxO2 solid versed microemulsion method. The structural properties solutions with various compositions were synthesized using the reand performance of Ce1- xZrxO2 were studied using XRD, BET, SEM, HRTEM, TPR and CO oxidation measurements. The results show that in the range of x = 0.4 - 0.5 and x = 0.6 - 1.0, the solid solutions posses the cubic and the tetragonal phase structure, respectively, Solids obtained by the reversed microemulsion method were more homogeneous on the whole range of composition, XRD investigations of the prepared materials did not show segregation of cerium or zirconium oxides, Highly uniform nanosize solid solution particles of ceria-zirconia with high specific area （146.7 m^2·g^-1） were attained under the conditions of this study. The TPR results and CO oxidation measurements indicate that the performance of the CeO2-ZrO2 mixed oxides is strongly related to the composition and structure of the oxides. Enhancement of the activity was found for the catalyst prepared by reversed microemulsion method as compared to the sample prepared by sol-gel method.展开更多
In the study, sludge from the aluminum profile factory and kaolin were used as the raw materials. Through adding ZrO2 mineralizer in different contents, Al2-xZrx＋yTi1-yO5 and Al4.54Si1.46O9.73 solid solution multipha...In the study, sludge from the aluminum profile factory and kaolin were used as the raw materials. Through adding ZrO2 mineralizer in different contents, Al2-xZrx＋yTi1-yO5 and Al4.54Si1.46O9.73 solid solution multiphase material was prepared to effectively inhibit the decomposition of aluminum titanate solid solution and optimize high temperature property of the multiphase material. With XRD and SEM means, crystalline structure and microstructure of each sample were characterized, and properties of each sample were tested. According to experimental results, the optimal addition amount of ZrO2 mineralizer was determined to be 1.5%. Correspondingly, contents for aluminum titanate solid solution, mullite solid solution and α-Al2O3 were 70.3%, 26.8% and 2.9% respectively, bulk density was 3.20 g/cm3, degree of porosity was 5.57%, water absorption rate was 1.74%, and the once thermal shock rupture strength retention rate was 90.52%.展开更多
A series of CeO2–ZrO2–WO3（CZW）catalysts prepared by a hydrothermal synthesis method showed excellent catalytic activity for selective catalytic reduction（SCR）of NO with NH3 over a wide temperature of 150–550℃....A series of CeO2–ZrO2–WO3（CZW）catalysts prepared by a hydrothermal synthesis method showed excellent catalytic activity for selective catalytic reduction（SCR）of NO with NH3 over a wide temperature of 150–550℃.The effect of hydrothermal treatment of CZW catalysts on SCR activity was investigated in the presence of 10% H2O.The fresh catalyst showed above 90% NOx conversion at 201–459℃,which is applicable to diesel exhaust NOx purification（200–440℃）.The SCR activity results indicated that hydrothermal aging decreased the SCR activity of CZW at low temperatures（below 300℃）,while the activity was notably enhanced at high temperature（above 450℃）.The aged CZW catalyst（hydrothermal aging at 700℃ for 8 hr）showed almost 80% NOx conversion at 229–550℃,while the V2O5–WO3/TiO2 catalyst presented above 80% NOx conversion at 308–370℃.The effect of structural changes,acidity,and redox properties of CZW on the SCR activity was investigated.The results indicated that the excellent hydrothermal stability of CZW was mainly due to the CeO2–ZrO2 solid solution,amorphous WO3 phase and optimal acidity.In addition,the formation of WO3 clusters increased in size as the hydrothermal aging temperature increased,resulting in the collapse of structure,which could further affect the acidity and redox properties.展开更多
文摘Nanosized ZrO2 powder was prepared by evaporative decomposition of solution（EDS）. The particle size is from 50 nm to 200 nm. This process has such advantages as high purity, precise compositional control, simple procedure and successive auto-operating. In this process, mixed solution of zirconium acetate and yttrium nitrate was atomized to from a fine mist and blown into the hot zone from the bottom of furnace. The solution was rapidly decomposed at 900℃ and the powder was collected by a filter system. The powder characteristics can be controlled by adjusting the concentration, droplet volume and decomposition temperature of the solution.
文摘Ce Zr O solid solution was prepared by four different methods, i.e., decomposition of nitrate, coprecipiation, hydroxysuainic acid sol gel as well as citrate sol gel, and characterized by using X ray powder diffraction, Raman and temperature programmed reduction. The phase composition and the reduction properties of Ce Zr O depend on the preparation method. A cubic Ce 0.5 Zr 0.5 O 2 solid solution can be obtained by using the sol gel method. The Ce Zr O solid solution prepared by using decomposition or coprecipiation was composed of cubic Ce 0.8 Zr 0.2 O 2 and tetragonal Ce 0.2 Zr 0.8 O 2 solid solution. The Ce Zr O solid solution prepared with different methods shows the different reduction properties owing to different phase composition. Results of differential thermal analysis and XRD show that Ce 0.5 Zr 0.5 O 2 solid solution is formed during the decomposition or combustion of the gel.
基金supported by the National Natural Science Foundation of China (No.50574075)Program for New Century Excellent Talents in University(No.NCET-05-0873)Specialized Research Fund for the Doctoral Program of Higher Education (SRFDP 20060700011)
文摘Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characteristics was calculated in the present investigation. The microstructure and properties of the synthesized Cu/Al2O3 were studied. The results show that high-energy milling can obviously promote internal oxidation of Al in Cu-Al powders in the same solid solubility. At the same milling conditions and internal oxidation parameters, the solid solution of Al in Cu either in low or high amount will result in the poor microstructure and properties of the Cu/Al2O3 composite. Subsequently, when high-energy milling and internal oxidation are synchronously used to prepare the Cu/Al2O3 composite, there should be an appropriate solubility and milling effect for the pre-alloyed powders.
文摘Single-phase homogeneous Ce1-x ZrxO2 solid versed microemulsion method. The structural properties solutions with various compositions were synthesized using the reand performance of Ce1- xZrxO2 were studied using XRD, BET, SEM, HRTEM, TPR and CO oxidation measurements. The results show that in the range of x = 0.4 - 0.5 and x = 0.6 - 1.0, the solid solutions posses the cubic and the tetragonal phase structure, respectively, Solids obtained by the reversed microemulsion method were more homogeneous on the whole range of composition, XRD investigations of the prepared materials did not show segregation of cerium or zirconium oxides, Highly uniform nanosize solid solution particles of ceria-zirconia with high specific area （146.7 m^2·g^-1） were attained under the conditions of this study. The TPR results and CO oxidation measurements indicate that the performance of the CeO2-ZrO2 mixed oxides is strongly related to the composition and structure of the oxides. Enhancement of the activity was found for the catalyst prepared by reversed microemulsion method as compared to the sample prepared by sol-gel method.
基金Sponsored by the Fujian Provincial Reform and Development Commission
文摘In the study, sludge from the aluminum profile factory and kaolin were used as the raw materials. Through adding ZrO2 mineralizer in different contents, Al2-xZrx＋yTi1-yO5 and Al4.54Si1.46O9.73 solid solution multiphase material was prepared to effectively inhibit the decomposition of aluminum titanate solid solution and optimize high temperature property of the multiphase material. With XRD and SEM means, crystalline structure and microstructure of each sample were characterized, and properties of each sample were tested. According to experimental results, the optimal addition amount of ZrO2 mineralizer was determined to be 1.5%. Correspondingly, contents for aluminum titanate solid solution, mullite solid solution and α-Al2O3 were 70.3%, 26.8% and 2.9% respectively, bulk density was 3.20 g/cm3, degree of porosity was 5.57%, water absorption rate was 1.74%, and the once thermal shock rupture strength retention rate was 90.52%.
基金supported by the National Natural Science Foundation of China(Nos.U1137603,21307047)the Opening Project of Key Laboratory of Green Catalysis of Sichuan Institutes of High Education(No.LYJ1309)
文摘A series of CeO2–ZrO2–WO3（CZW）catalysts prepared by a hydrothermal synthesis method showed excellent catalytic activity for selective catalytic reduction（SCR）of NO with NH3 over a wide temperature of 150–550℃.The effect of hydrothermal treatment of CZW catalysts on SCR activity was investigated in the presence of 10% H2O.The fresh catalyst showed above 90% NOx conversion at 201–459℃,which is applicable to diesel exhaust NOx purification（200–440℃）.The SCR activity results indicated that hydrothermal aging decreased the SCR activity of CZW at low temperatures（below 300℃）,while the activity was notably enhanced at high temperature（above 450℃）.The aged CZW catalyst（hydrothermal aging at 700℃ for 8 hr）showed almost 80% NOx conversion at 229–550℃,while the V2O5–WO3/TiO2 catalyst presented above 80% NOx conversion at 308–370℃.The effect of structural changes,acidity,and redox properties of CZW on the SCR activity was investigated.The results indicated that the excellent hydrothermal stability of CZW was mainly due to the CeO2–ZrO2 solid solution,amorphous WO3 phase and optimal acidity.In addition,the formation of WO3 clusters increased in size as the hydrothermal aging temperature increased,resulting in the collapse of structure,which could further affect the acidity and redox properties.