Highly uniformed barium-strontium titanate nanotube arrays were fabricated using a porous anodic aluminum oxide template from a barium-strontium titanate sol-gel solution. Electron microscope results showed that nanot...Highly uniformed barium-strontium titanate nanotube arrays were fabricated using a porous anodic aluminum oxide template from a barium-strontium titanate sol-gel solution. Electron microscope results showed that nanotubes with uniform length and diameter were obtained. The diameters and lengths of these nanotubes were dependent on the pore diameter and the thickness of the applied anodic aluminum oxide template. High resolution transmission electron microscopy and the selected-area electron diffraction pattern investigations demonstrated the perovskite structure and the polycrystalline of the fabricated barium-strontium titanate nanotubes. The characterization of the electrical and dielectric properties had also been made. Compared to thin film material, the intrinsic leakage current density is almost the same. Besides, at 30 ℃ the dielectric constant and dielectric loss of the fabricated nanotube is 80 and 0.027 at 1 MHz respectively.展开更多
基金supported by the National Natural Science Foundation of China (Grant No 60244003)
文摘Highly uniformed barium-strontium titanate nanotube arrays were fabricated using a porous anodic aluminum oxide template from a barium-strontium titanate sol-gel solution. Electron microscope results showed that nanotubes with uniform length and diameter were obtained. The diameters and lengths of these nanotubes were dependent on the pore diameter and the thickness of the applied anodic aluminum oxide template. High resolution transmission electron microscopy and the selected-area electron diffraction pattern investigations demonstrated the perovskite structure and the polycrystalline of the fabricated barium-strontium titanate nanotubes. The characterization of the electrical and dielectric properties had also been made. Compared to thin film material, the intrinsic leakage current density is almost the same. Besides, at 30 ℃ the dielectric constant and dielectric loss of the fabricated nanotube is 80 and 0.027 at 1 MHz respectively.