Effects of grain refining and modification on mechanical properties and microstructures of Al-7.5Si-4Cu cast alloy

Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.

Microstructure and mechanical properties of aluminium metal matrix composites with addition of bamboo leaf ash by stir casting method

Al-4.5%Cu alloy was used as a matrix at2%,4%and6%of bamboo leaf ash(BLA)which was extruded from agro waste and was used as reinforcement.The composite which was fabricated by stir casting method possessed superior properties due to an effective bonding between matrix and reinforcement particles.The fabricated composite specimens were subjected to various tests to determine the mechanical properties such as density,porosity,hardness and tensile strength.The results were compared with basic matrix alloy.Furthermore,the OM,SEM with EDAX and XRD analyses were carried out to analyze the dispersion of the reinforced particles in the selected matrix alloy.It was observed that the homogeneous distribution of BLA particles in composites was intragranular in nature.Moreover,it was also observed that BLA particles were well bonded with matrix alloy with clear interface.It was also found that the density decreased with increase in mass fraction of BLA particles and porosity increased with increase in mass fraction of BLA particles.The hardness and tensile strength were increased up to4%of BLA in the composite,with a further increase in BLA content the hardness and tensile strength decreased.