Materials with the formula Yb2-xAlxMo3O12 （x = 0.1, 0.2, 0.3, 0.4, 0.5, 0.7, 0.9, 1.0, 1.1, 1.3, 1.5, and 1.8） were synthesized and their structures, phase transitions, and hygroscopicity investigated using X-ray po...Materials with the formula Yb2-xAlxMo3O12 （x = 0.1, 0.2, 0.3, 0.4, 0.5, 0.7, 0.9, 1.0, 1.1, 1.3, 1.5, and 1.8） were synthesized and their structures, phase transitions, and hygroscopicity investigated using X-ray powder diffraction, Raman spectroscopy, and thermal analysis. It is shown that Yb2-xAlxMo3012 solid solutions crystallize in a single monoclinic phase for 1.7 〈 x 〈 2.0 and in a single orthorhombic phase for 0.0 〈 x 〈 0,4, and exhibit the characteristics of both monoclinic and orthorhombic structures outside these compositional ranges. The monoclinic to orthorhonlbic phase transition temperature of A12Mo3012 can be reduced by partial substitution of A13＋ by Yb3＋, and the Yb2-zAlxMo3012 （0.0 〈 x 〈 2.0） materials are hydrated at room temperature and contain two kinds of water species. One of these interacts strongly with and hinders the motions of the polyhedra, while the other does not. The partial substitution of A13＋ for Yb3＋ in Yb2Mo3012 decreases its hygroscopicity, and the linear thermal expansion coefficients after complete removal of water species are measured to be -9.1 x 10-6/K, -5.5 x 10-6/K, 5.74 x 10-6/K, and 9.5 x 10 6/K for Ybl.sAlo.2（MoO4）3, Yb1.6Alo.4（MoO4）3, Ybo.4All.6（Mo04）3, and Ybo.2Al1.8（MoO4）3, respectively.展开更多
基金supported by the National Natural Science Foundation of China (Grant No. 10974183)
文摘Materials with the formula Yb2-xAlxMo3O12 （x = 0.1, 0.2, 0.3, 0.4, 0.5, 0.7, 0.9, 1.0, 1.1, 1.3, 1.5, and 1.8） were synthesized and their structures, phase transitions, and hygroscopicity investigated using X-ray powder diffraction, Raman spectroscopy, and thermal analysis. It is shown that Yb2-xAlxMo3012 solid solutions crystallize in a single monoclinic phase for 1.7 〈 x 〈 2.0 and in a single orthorhombic phase for 0.0 〈 x 〈 0,4, and exhibit the characteristics of both monoclinic and orthorhombic structures outside these compositional ranges. The monoclinic to orthorhonlbic phase transition temperature of A12Mo3012 can be reduced by partial substitution of A13＋ by Yb3＋, and the Yb2-zAlxMo3012 （0.0 〈 x 〈 2.0） materials are hydrated at room temperature and contain two kinds of water species. One of these interacts strongly with and hinders the motions of the polyhedra, while the other does not. The partial substitution of A13＋ for Yb3＋ in Yb2Mo3012 decreases its hygroscopicity, and the linear thermal expansion coefficients after complete removal of water species are measured to be -9.1 x 10-6/K, -5.5 x 10-6/K, 5.74 x 10-6/K, and 9.5 x 10 6/K for Ybl.sAlo.2（MoO4）3, Yb1.6Alo.4（MoO4）3, Ybo.4All.6（Mo04）3, and Ybo.2Al1.8（MoO4）3, respectively.