Solid solution-strengthened copper alloys have the advantages of a simple composition and manufacturing process,high mechanical and electrical comprehensive performances,and low cost;thus,they are widely used in high-...Solid solution-strengthened copper alloys have the advantages of a simple composition and manufacturing process,high mechanical and electrical comprehensive performances,and low cost;thus,they are widely used in high-speed rail contact wires,electronic component connectors,and other devices.Overcoming the contradiction between low alloying and high performance is an important challenge in the development of solid solution-strengthened copper alloys.Taking the typical solid solution-strengthened alloy Cu-4Zn-1Sn as the research object,we proposed using the element In to replace Zn and Sn to achieve low alloying in this work.Two new alloys,Cu-1.5Zn-1Sn-0.4In and Cu-1.5Zn-0.9Sn-0.6In,were designed and prepared.The total weight percentage content of alloying elements decreased by 43%and 41%,respectively,while the product of ultimate tensile strength(UTS)and electrical conductivity(EC)of the annealed state increased by 14%and 15%.After cold rolling with a 90%reduction,the UTS of the two new alloys reached 576 and 627MPa,respectively,the EC was 44.9%IACS and 42.0%IACS,and the product of UTS and EC(UTS×EC)was 97%and 99%higher than that of the annealed state alloy.The dislocations proliferated greatly in cold-rolled alloys,and the strengthening effects of dislocations reached 332 and 356 MPa,respectively,which is the main reason for the considerable improvement in mechanical properties.展开更多
To date,there is still a lack of a comprehensive explanation for caged dynamics which is regarded as one of the intricate dynamic behaviors in amorphous alloys.This study focuses on Pd_(82)Si_(18)as the research objec...To date,there is still a lack of a comprehensive explanation for caged dynamics which is regarded as one of the intricate dynamic behaviors in amorphous alloys.This study focuses on Pd_(82)Si_(18)as the research object to further elucidate the underlying mechanism of caged dynamics from multiple perspectives,including the cage's lifetime,atomic local environment,and atomic potential energy.The results reveal that Si atoms exhibit a pronounced cage effect due to the hindrance of Pd atoms,resulting in an anomalous peak in the non-Gaussian parameters.An in-depth investigation was conducted on the caged dynamics differences between fast and slow Si atoms.In comparison to fast Si atoms,slow Si atoms were surrounded by more Pd atoms and occupied lower potential energy states,resulting in smaller diffusion displacements for the slow Si atoms.Concurrently,slow Si atoms tend to be in the centers of smaller clusters with coordination numbers of 9 and 10.During the isothermal relaxation process,clusters with coordination numbers 9 and 10 have longer lifetimes,suggesting that the escape of slow Si atoms from their cages is more challenging.The findings mentioned above hold significant implications for understanding the caged dynamics.展开更多
In order to overcome the problems of many pores,large deformation and unstable weld quality of traditional laser welded aluminumcopper alloy joints,a red-blue dual-beam laser source and a swinging laser were introduce...In order to overcome the problems of many pores,large deformation and unstable weld quality of traditional laser welded aluminumcopper alloy joints,a red-blue dual-beam laser source and a swinging laser were introduced for welding.T2 copper and 6063 aluminum thin plates were lap welded by coaxial dual-beam laser welding.The morphology of weld cross section was compared to explore the influence of process parameters on the formation of lap joints.The microstructure characteristics of the weld zone were observed and compared by optical microscope.The results show that the addition of laser beam swing can eliminate the internal pores of the weld.With the increase of the swing width,the weld depth decreases,and the weld width increases first and then decreases.The influence of welding speed on the weld cross section morphology is similar to that of swing width.With the increase of welding speed,the weld width increases first and then decreases,while the weld depth decreases all the time.This is because that the red laser is used as the main heat source to melt the base metals,with the increase of red laser power,the weld depth increases.As an auxiliary laser source,blue laser reduces the total energy consumption,consequently,the effective heat input increases and the spatter is restrained effectively.As a result,the increase of red laser power has an enhancement effect on the weld width and weld depth.When the swing width is 1.2 mm,the red laser power is 550 W,the blue laser power is 500 W,and the welding speed is 35 mm/s,the weld forming is the best.The lap joint of T2 copper and 6063 aluminum alloy thin plate can be connected stably with the hybrid of blue laser.The effect rules of laser beam swing on the weld formation were obtained,which improved the quality of the joints.展开更多
Multi-material laser-based powder bed fusion (PBF-LB) allows manufacturing of parts with 3-dimensional gradient and additional functionality in a single step. This research focuses on the combination of thermally-cond...Multi-material laser-based powder bed fusion (PBF-LB) allows manufacturing of parts with 3-dimensional gradient and additional functionality in a single step. This research focuses on the combination of thermally-conductive CuCr1Zr with hard M300 tool steel.Two interface configurations of M300 on CuCr1Zr and CuCr1Zr on M300 were investigated. Ultra-fine grains form at the interface due to the low mutual solubility of Cu and steel. The material mixing zone size is dependent on the configurations and tunable in the range of0.1–0.3 mm by introducing a separate set of parameters for the interface layers. Microcracks and pores mainly occur in the transition zone.Regardless of these defects, the thermal diffusivity of bimetallic parts with 50vol% of CuCr1Zr significantly increases by 70%–150%compared to pure M300. The thermal diffusivity of CuCr1Zr and the hardness of M300 steel can be enhanced simultaneously by applying the aging heat treatment.展开更多
Laser-induced breakdown spectroscopy(LIBS)is a capable technique for elementary analysis,while LIBS quantitation is still under development.In quantitation,precise laser focusing plays an important role because it ens...Laser-induced breakdown spectroscopy(LIBS)is a capable technique for elementary analysis,while LIBS quantitation is still under development.In quantitation,precise laser focusing plays an important role because it ensures the distance between the laser and samples.In the present work,we employed spectral intensity as a direct way to assist laser focusing in LIBS quantitation for copper alloys.It is found that both the air emission and the copper line could be used to determine the position of the sample surface by referencing the intensity maximum.Nevertheless,the fine quantitation was only realized at the position where the air emission(e.g.O(I)777.4 nm)reached intensity maximum,and also in this way,a repeatable quantitation was successfully achieved even after 120 days.The results suggested that the LIBS quantitation was highly dependent on the focusing position of the laser,and spectra-assisted focusing could be a simple way to find the identical condition for different samples’detection.In the future,this method might be applicable in field measurements for LIBS analysis of solids.展开更多
Cu-Ni-Al alloys at different concentrations were obtained using a high frequency induction melting unit, keeping a balance in the nominal compositions. Light alloys are important to be used in industrial applications....Cu-Ni-Al alloys at different concentrations were obtained using a high frequency induction melting unit, keeping a balance in the nominal compositions. Light alloys are important to be used in industrial applications. Aluminum additions result in a positive hardness increment of the ternary alloys in comparison with the binary Cu-Ni alloys. Generalized wear mechanisms of the alloys with low aluminum content are basically type abrasive, while samples with 5 and 10 at.% Al present an oxidative-adhesive wear mechanism. Wear results have indicated that aluminum addition affects positively the wear resistance, mainly in samples with high aluminum content product of the creation during the test of different oxides corresponding to the elements present in the alloys.展开更多
Rapidly solidified aging is an effective way to refine the microstructure of Cu-Cr-Sn-Zn lead frame alloy and enhance its hardness. The artificial neural network methodology(ANN) along with genetic algorithms were use...Rapidly solidified aging is an effective way to refine the microstructure of Cu-Cr-Sn-Zn lead frame alloy and enhance its hardness. The artificial neural network methodology(ANN) along with genetic algorithms were used for data analysis and optimization. In this paper the input parameters of the artificial neural network (ANN) are the aging temperature and aging time. The outputs of the ANN model are the hardness and conductivity properties. Some explanations of these predicted results from the microstructure and precipitation-hardening viewpoint are given. After the ANN model is trained successfully, genetic algorithms(GAs) are applied for optimizing the aging processes parameters.展开更多
The aging hardening process makes it possible to get higher hardness and electrical conductivity of lead frame copper alloy. The process has only been studied empirically by trial-and-error method so far. The use of a...The aging hardening process makes it possible to get higher hardness and electrical conductivity of lead frame copper alloy. The process has only been studied empirically by trial-and-error method so far. The use of a supervised artificial neural network(ANN) was proposed to model the non-linear relationship between parameters of aging process with respect to hardness and conductivity properties of Cu-Cr-Zr alloy. The improved model was developed by the Levenberg-Marquardt training algorithm. A basic repository on the domain knowledge of aging process was established via sufficient data mining by the network. The results show that the ANN system is effective and successful for predicting and analyzing the properties of Cu-Cr-Zr alloy.展开更多
A kinetic study on the sulfuric acid leaching of multi-metal oxide, which is the product of multi-metal copper alloy with iron trioxide roasted in oxygen, was carried out. The effects of leaching time, stirring speed,...A kinetic study on the sulfuric acid leaching of multi-metal oxide, which is the product of multi-metal copper alloy with iron trioxide roasted in oxygen, was carried out. The effects of leaching time, stirring speed, sulfuric acid concentration, reaction temperature, and particle size of the multi-metal oxide on the kinetics and mechanism of copper extraction were studied. It was found that the reaction kinetic model about the copper extraction from multi-metal oxide follows the mixed kinetic shrinking core mode: 1/3ln(1–X)+(1–X)^(–1/3)–1=680.5C(H_2SO_4)^(0.4297)d_P^(–0.75115)exp(–E_a/RT)t.展开更多
China is quite poor in argent resource. Roughly 80% of this industrial argent is imported every year. In order to improve the situation, we took advantage of rare earth (RE) mineral resource and successfully developed...China is quite poor in argent resource. Roughly 80% of this industrial argent is imported every year. In order to improve the situation, we took advantage of rare earth (RE) mineral resource and successfully developed the non-argent Lanthanum-tellurium-copper alloy as a substitute for industry argent-copper. In our research, we were able to successfully apply rare earth lanthanum to copper alloy. The defects as porosity, inclusion, etc. originating from nonvacuum melting processing were controlled. Fine grain was obtained. Meanwhile, the comprehensive properties of the copper alloy, such as strength, conductivity and thermal conductivity were improved. The research results in increasing conductivity and thermal conductivity by 5% and 15%, respectively, while the tensile strength is increased by 6% higher than Ag-Cu alloy. The anti-electric corrosion property is good, and there is no argent-cadmium steam population originating from the electric arc effect. The addition of lanthanum further reduces the content of oxygen and hydrogen. The optimum quantity of the addition of RE lanthanum in the copper alloy is 0.010% - 0.020% .展开更多
The electrodeposition of A1 and A1-Cu binary alloys on to gold substrates from a room temperature ionic liquid electrolyte containing A1C13-EtaNHC1 was studied. The electrochemical behavior of the electrolyte and the ...The electrodeposition of A1 and A1-Cu binary alloys on to gold substrates from a room temperature ionic liquid electrolyte containing A1C13-EtaNHC1 was studied. The electrochemical behavior of the electrolyte and the mechanism of deposition were investigated through cyclic voltammetry (CV), and the properties of deposits obtained were assessed by scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) and X-ray diffraction (XRD). A1 of 70μm in thickness and an A1-Cu alloy of 30μm in thickness with 8at% copper were deposited from the electrolyte. SEM images of the deposits indicate that the A1 deposit was smooth and uniform, whereas the Al-Cu deposit was nodular. The average crystalline size, as determined by XRD patterns, was found to be (30±5) and (29±5) nm, respectively, for A1 and A1-Cu alloys. Potentiodynamic polarization (Tafel plots) and electrochemical impedance spectroscopic (EIS) measurements showed that Al-Cu alloys are more corrosion resistant than Al.展开更多
To study the effect of titanium alloy cage on the treatment of the ischemic necrosis of femoral head in dog, the model of the ischemic necrosis of femoral head was made with the liquid nitrogen in 15 hybrid adult dogs...To study the effect of titanium alloy cage on the treatment of the ischemic necrosis of femoral head in dog, the model of the ischemic necrosis of femoral head was made with the liquid nitrogen in 15 hybrid adult dogs. The titanium alloy cage made of a hollow cylinder was driven into the subchondral bone of necrotic femoral head via central channel. The dogs were divided into 3 groups, each group was sacrificed 3, 6, 12 weeks after the operation respectively. No collapse of femoral head was observed after the operation. The position of the cages was good on radiograph. Microscopically, the cancellous bone of necrotic femoral head rebuilt gradually and grew into cage. After 12 weeks of creeping substitution, the cancellous bone filled up the hollow cavity and holes of the cages. It is concluded that the titanium alloy cage can provide structural support for the subchondral bone and prevent collapse and can be used for the treatment of the ischemic necrosis of femoral head.展开更多
The laser cladding of Ni1015 alloy on Cu substrate was prepared by a high power continuous wave CO2 laser. Its microstructure was analyzed by optical microscope (OM), scanning electron microscope (SEM), and X-Ray ...The laser cladding of Ni1015 alloy on Cu substrate was prepared by a high power continuous wave CO2 laser. Its microstructure was analyzed by optical microscope (OM), scanning electron microscope (SEM), and X-Ray diffraction (XRD). The average microhardness of the cladding coating was Hv 280, which was almost three times of that of the Cu substrate (Hv 85). OM and SEM observations showed that the obtained coating had a smooth and uniform surface, as well as a metallurgical combination with the Cu substrate without cracks and pores at the interface. With the addition of copper into the nickel-based alloy, the differences of thermal expansion coefficient and melting point between the interlayer and cladding were reduced, which resulted in low stresses during rapid cooling. Moreover, large amount of (Cu, Ni) solid solution formed a metallurgical bonding between the cladding coating and the substrate, which also relaxed the stresses, leading to the reduction of interfacial cracks and pores after laser cladding.展开更多
Al2O3 dispersion copper alloy powder was prepared by intemal oxidation, and three consolidation methods--high-velocity compaction (HVC), hot pressing (HP), and hot extrusion (HE)--were used to prepare Al2O3 disp...Al2O3 dispersion copper alloy powder was prepared by intemal oxidation, and three consolidation methods--high-velocity compaction (HVC), hot pressing (HP), and hot extrusion (HE)--were used to prepare Al2O3 dispersion-strengthened copper (Cu-Al2O3) alloys. The microstructures and properties of these alloys were investigated and compared. The results show that the alloys prepared by the HP and HE methods exhibited the coarsest and finest grain sizes, respectively. The alloy prepared by the HVC method exhibited the lowest relative density (98.3% vs. 99.5% for HP and 100% for HE), which resulted in the lowest electrical conductivity (81% IACS vs. 86% IACS for HP and 87% IACS for HE). However, this alloy also exhibited the highest hardness (77 HRB vs. 69 HRB for HP and 70 HRB for HE), the highest compressive strength (443 MPa vs. 386 MPa for I/P and 378 MPa for HE), and the best hardness retention among the investigated alloys. The results illustrate that the alloy prepared by the HVC method exhibits high softening temperature and good mechanical properties at high temperatures, which imply long service life when used as spot-welding electrodes.展开更多
This paper mainly concentrated on the feasibility of friction stir welding of dissimilar metal of aluminum alloy to copper (I2) and a preliminary analysis of welding parameters influencing on the microstructures and...This paper mainly concentrated on the feasibility of friction stir welding of dissimilar metal of aluminum alloy to copper (I2) and a preliminary analysis of welding parameters influencing on the microstructures and properties of joint was carried out. The results indicated that the thickness of workpiece played an important role in the welding parameters which could succeed in the friction stir welding of dissimilar metal of copper to aluminum alloy, and the parameters were proved to be a narrow choice. The interfacial region between copper and aluminum in the dissimilar joint was not uniformly mixed, constituted with part of incomplete mixing zone, complete mixing zone, dispersion zone and the most region' s boundary was obvious. Meantime a kind banded structure with inhomogeneous width was formed. The intermetallic compounds generated during friction stir welding in the interfacial region were mainly CugAl4, Al2Cu etc, and their hardness was higher than oihers.展开更多
Dissimilar joints comprised of copper–nickel and steel alloys are a challenge for manufacturers in modern industries, as these metals are not thermomechanically or chemically well matched. The present study investiga...Dissimilar joints comprised of copper–nickel and steel alloys are a challenge for manufacturers in modern industries, as these metals are not thermomechanically or chemically well matched. The present study investigated the effects of tool rotational speed and linear speed on the microstructure and mechanical properties of friction stir-welded C71000 copper–nickel and 340 stainless steel alloys using a tungsten carbide tool with a cylindrical pin. The results indicated that a rotational-to-linear speed ratio of 12.5 r/mm did not cause any macro defects, whereas some tunneling defects and longitudinal cracks were found at other ratios that were lower and higher. Furthermore, chromium carbide was formed on the grain boundaries of the 304 stainless steel near the shoulder zone and inside the joint zone, directing carbon and chromium penetration toward the grain boundaries. Tensile strength and elongation percentages were 84% and 65% of the corresponding values in the copper–nickel base metal, respectively.展开更多
With CuMn alloy as interlayer, the transient liquid phase (TLP) diffusion bonding of Cu alloys (CuAlBe) to stainless steel (1Cr18Ni9Ti) was studied. The results show that the bonding pressure, time and temperature and...With CuMn alloy as interlayer, the transient liquid phase (TLP) diffusion bonding of Cu alloys (CuAlBe) to stainless steel (1Cr18Ni9Ti) was studied. The results show that the bonding pressure, time and temperature and the content of Mn in CuMn alloy have great effects on the strength of bonding interface; when they are 1 MPa, 40 min, 1 223 K and 30% respectively, the maximum joint strength of 487 MPa is attained. The fracture occurring at the bonding interface is a plastic one and the effect of Mn has been analyzed.展开更多
Mechanical properties and tribological behavior of a novel cast heat resisting copper based alloy are investigated. The corresponding properties of a commercial aluminum bronze C95500 (ASTM B30) are compared with the ...Mechanical properties and tribological behavior of a novel cast heat resisting copper based alloy are investigated. The corresponding properties of a commercial aluminum bronze C95500 (ASTM B30) are compared with the alloy. The results show that the alloy possesses better mechanical properties and tribological behaviors than that of C95500 at elevated temperature. The tensile strength, elongation and hardness at 500℃ are 470MPa, 2.5% and HB220, respectively. The wear rate of the developed alloy at ambient and elevated temperature is about one sixth and one fortieth of that of C95500, respectively. The alloy is very suitable for ma nufacturing heat resisting and wear resisting parts. Major strengthening mechanisms for the alloy are solution strengthening and the second phase strengthening.展开更多
The grain boundary structure of Cu alloy was observed and the characteristic of the boundaries was studied,including 70∶30 cupronickel and 70∶30 brass. The results show that in the case of the 70∶30 cupronickel thi...The grain boundary structure of Cu alloy was observed and the characteristic of the boundaries was studied,including 70∶30 cupronickel and 70∶30 brass. The results show that in the case of the 70∶30 cupronickel thin platelets with nickel and iron enrichment in it precipitate intergranular so that the alloy was sensitive to seawater corrosion. In the case of 70∶30 brass the situation of grain boundary segregation of different inclusions made the corrosion resistance of the alloy even worse. All of those were discovered through the corrosion behavior of the two different copper alloys served in various environments. The experimental methods used here were, scanning electron microscopy(SEM), transmission electron microscopy(TEM) and energy dispersive of X ray(EDX). The intergranular corrosion morphologies of those copper alloys served in engineering or exposed to seawater for a long term were given.展开更多
The mechanical properties of Al-Cu-Mn casting alloy mainly depend on the morphology, distribution, size, and number ofθ′(Al2Cu) precipitates. In this study, we have analyzed the effect of rare earth samarium (Sm...The mechanical properties of Al-Cu-Mn casting alloy mainly depend on the morphology, distribution, size, and number ofθ′(Al2Cu) precipitates. In this study, we have analyzed the effect of rare earth samarium (Sm) addition on the kinetics of precipitation in the Al-Cu-Mn casting alloy by using differential scanning calorimetry (DSC) and high-resolution transmission electron microscopy. Thermal ef-fect peaks that are attributed to the formation and the dissolution of Guinier-Preston (GP) zone andθ′phase were identified from the DSC curves. The activation energy ofθ′formation was calculated by using both the Kissinger method and the analytical model, and the corre-sponding results were compared. Results suggest that the activation energy ofθ′formation in Al-Cu-Mn alloy is dramatically higher than that in Al-Cu-Mn-Sm alloy. Accordingly, it is concluded that the addition of rare earth Sm decreases the activation energy ofθ′formation and promotes the formation ofθ′precipitates.展开更多
基金financially supported by the National Key Research and Development Program of China(No.2021YFB3803101)the National Natural Science Foundation of China(Nos.52022011,51974028,and 52090041)+1 种基金the Xiaomi Young Scholars ProgramChina National Postdoctoral Program for Innovative Talents(No.BX20230042)。
文摘Solid solution-strengthened copper alloys have the advantages of a simple composition and manufacturing process,high mechanical and electrical comprehensive performances,and low cost;thus,they are widely used in high-speed rail contact wires,electronic component connectors,and other devices.Overcoming the contradiction between low alloying and high performance is an important challenge in the development of solid solution-strengthened copper alloys.Taking the typical solid solution-strengthened alloy Cu-4Zn-1Sn as the research object,we proposed using the element In to replace Zn and Sn to achieve low alloying in this work.Two new alloys,Cu-1.5Zn-1Sn-0.4In and Cu-1.5Zn-0.9Sn-0.6In,were designed and prepared.The total weight percentage content of alloying elements decreased by 43%and 41%,respectively,while the product of ultimate tensile strength(UTS)and electrical conductivity(EC)of the annealed state increased by 14%and 15%.After cold rolling with a 90%reduction,the UTS of the two new alloys reached 576 and 627MPa,respectively,the EC was 44.9%IACS and 42.0%IACS,and the product of UTS and EC(UTS×EC)was 97%and 99%higher than that of the annealed state alloy.The dislocations proliferated greatly in cold-rolled alloys,and the strengthening effects of dislocations reached 332 and 356 MPa,respectively,which is the main reason for the considerable improvement in mechanical properties.
基金Project supported by the National Natural Science Foundation of China (Grant No.51701071)the Natural Science Foundation of Hunan Province,China (Grant Nos.2022JJ50115 and 2021JJ30179)the Research Foundation of the Education Bureau of Hunan Province,China (Grant No.22A0522)。
文摘To date,there is still a lack of a comprehensive explanation for caged dynamics which is regarded as one of the intricate dynamic behaviors in amorphous alloys.This study focuses on Pd_(82)Si_(18)as the research object to further elucidate the underlying mechanism of caged dynamics from multiple perspectives,including the cage's lifetime,atomic local environment,and atomic potential energy.The results reveal that Si atoms exhibit a pronounced cage effect due to the hindrance of Pd atoms,resulting in an anomalous peak in the non-Gaussian parameters.An in-depth investigation was conducted on the caged dynamics differences between fast and slow Si atoms.In comparison to fast Si atoms,slow Si atoms were surrounded by more Pd atoms and occupied lower potential energy states,resulting in smaller diffusion displacements for the slow Si atoms.Concurrently,slow Si atoms tend to be in the centers of smaller clusters with coordination numbers of 9 and 10.During the isothermal relaxation process,clusters with coordination numbers 9 and 10 have longer lifetimes,suggesting that the escape of slow Si atoms from their cages is more challenging.The findings mentioned above hold significant implications for understanding the caged dynamics.
基金supported by Guangdong Science and Technology Plan Project(Grant No.20170902,No.20180902)Yangjiang Science and Technology Plan Project(Grant No.SDZX2020063)+1 种基金Shenzhen Key Projects of Innovation and Entrepreneurship Plan Technology(JSGG20210420091802007)Yunfu 2023 Science and Technology Plan Project(S2023020201).
文摘In order to overcome the problems of many pores,large deformation and unstable weld quality of traditional laser welded aluminumcopper alloy joints,a red-blue dual-beam laser source and a swinging laser were introduced for welding.T2 copper and 6063 aluminum thin plates were lap welded by coaxial dual-beam laser welding.The morphology of weld cross section was compared to explore the influence of process parameters on the formation of lap joints.The microstructure characteristics of the weld zone were observed and compared by optical microscope.The results show that the addition of laser beam swing can eliminate the internal pores of the weld.With the increase of the swing width,the weld depth decreases,and the weld width increases first and then decreases.The influence of welding speed on the weld cross section morphology is similar to that of swing width.With the increase of welding speed,the weld width increases first and then decreases,while the weld depth decreases all the time.This is because that the red laser is used as the main heat source to melt the base metals,with the increase of red laser power,the weld depth increases.As an auxiliary laser source,blue laser reduces the total energy consumption,consequently,the effective heat input increases and the spatter is restrained effectively.As a result,the increase of red laser power has an enhancement effect on the weld width and weld depth.When the swing width is 1.2 mm,the red laser power is 550 W,the blue laser power is 500 W,and the welding speed is 35 mm/s,the weld forming is the best.The lap joint of T2 copper and 6063 aluminum alloy thin plate can be connected stably with the hybrid of blue laser.The effect rules of laser beam swing on the weld formation were obtained,which improved the quality of the joints.
基金supported by VTT Technical Research Centre of Finland,Aalto University,Aerosint SA,and partially from European Union Horizon 2020 (No.768775)。
文摘Multi-material laser-based powder bed fusion (PBF-LB) allows manufacturing of parts with 3-dimensional gradient and additional functionality in a single step. This research focuses on the combination of thermally-conductive CuCr1Zr with hard M300 tool steel.Two interface configurations of M300 on CuCr1Zr and CuCr1Zr on M300 were investigated. Ultra-fine grains form at the interface due to the low mutual solubility of Cu and steel. The material mixing zone size is dependent on the configurations and tunable in the range of0.1–0.3 mm by introducing a separate set of parameters for the interface layers. Microcracks and pores mainly occur in the transition zone.Regardless of these defects, the thermal diffusivity of bimetallic parts with 50vol% of CuCr1Zr significantly increases by 70%–150%compared to pure M300. The thermal diffusivity of CuCr1Zr and the hardness of M300 steel can be enhanced simultaneously by applying the aging heat treatment.
基金financially supported by the Provincial Key Research and Development Program of Shandong,China(No.2019GHZ010)the Natural Science Foundation of Shandong Province(No.ZR2020MF123)+1 种基金National Natural Science Foundation of China(Nos.61975190 and12174359)the Fundamental Research Funds for the Central Universities(No.202161002)。
文摘Laser-induced breakdown spectroscopy(LIBS)is a capable technique for elementary analysis,while LIBS quantitation is still under development.In quantitation,precise laser focusing plays an important role because it ensures the distance between the laser and samples.In the present work,we employed spectral intensity as a direct way to assist laser focusing in LIBS quantitation for copper alloys.It is found that both the air emission and the copper line could be used to determine the position of the sample surface by referencing the intensity maximum.Nevertheless,the fine quantitation was only realized at the position where the air emission(e.g.O(I)777.4 nm)reached intensity maximum,and also in this way,a repeatable quantitation was successfully achieved even after 120 days.The results suggested that the LIBS quantitation was highly dependent on the focusing position of the laser,and spectra-assisted focusing could be a simple way to find the identical condition for different samples’detection.In the future,this method might be applicable in field measurements for LIBS analysis of solids.
文摘Cu-Ni-Al alloys at different concentrations were obtained using a high frequency induction melting unit, keeping a balance in the nominal compositions. Light alloys are important to be used in industrial applications. Aluminum additions result in a positive hardness increment of the ternary alloys in comparison with the binary Cu-Ni alloys. Generalized wear mechanisms of the alloys with low aluminum content are basically type abrasive, while samples with 5 and 10 at.% Al present an oxidative-adhesive wear mechanism. Wear results have indicated that aluminum addition affects positively the wear resistance, mainly in samples with high aluminum content product of the creation during the test of different oxides corresponding to the elements present in the alloys.
文摘Rapidly solidified aging is an effective way to refine the microstructure of Cu-Cr-Sn-Zn lead frame alloy and enhance its hardness. The artificial neural network methodology(ANN) along with genetic algorithms were used for data analysis and optimization. In this paper the input parameters of the artificial neural network (ANN) are the aging temperature and aging time. The outputs of the ANN model are the hardness and conductivity properties. Some explanations of these predicted results from the microstructure and precipitation-hardening viewpoint are given. After the ANN model is trained successfully, genetic algorithms(GAs) are applied for optimizing the aging processes parameters.
文摘The aging hardening process makes it possible to get higher hardness and electrical conductivity of lead frame copper alloy. The process has only been studied empirically by trial-and-error method so far. The use of a supervised artificial neural network(ANN) was proposed to model the non-linear relationship between parameters of aging process with respect to hardness and conductivity properties of Cu-Cr-Zr alloy. The improved model was developed by the Levenberg-Marquardt training algorithm. A basic repository on the domain knowledge of aging process was established via sufficient data mining by the network. The results show that the ANN system is effective and successful for predicting and analyzing the properties of Cu-Cr-Zr alloy.
基金Project(2011AA061003)supported by Hi-Tech Research and Development Program of China
文摘A kinetic study on the sulfuric acid leaching of multi-metal oxide, which is the product of multi-metal copper alloy with iron trioxide roasted in oxygen, was carried out. The effects of leaching time, stirring speed, sulfuric acid concentration, reaction temperature, and particle size of the multi-metal oxide on the kinetics and mechanism of copper extraction were studied. It was found that the reaction kinetic model about the copper extraction from multi-metal oxide follows the mixed kinetic shrinking core mode: 1/3ln(1–X)+(1–X)^(–1/3)–1=680.5C(H_2SO_4)^(0.4297)d_P^(–0.75115)exp(–E_a/RT)t.
基金Project supported by the National Scientific and Technological Achievements Spread Project (2004EC00299)Science and Technology Type Middle and Small Business Technique Invention Fund (04C26225121390)
文摘China is quite poor in argent resource. Roughly 80% of this industrial argent is imported every year. In order to improve the situation, we took advantage of rare earth (RE) mineral resource and successfully developed the non-argent Lanthanum-tellurium-copper alloy as a substitute for industry argent-copper. In our research, we were able to successfully apply rare earth lanthanum to copper alloy. The defects as porosity, inclusion, etc. originating from nonvacuum melting processing were controlled. Fine grain was obtained. Meanwhile, the comprehensive properties of the copper alloy, such as strength, conductivity and thermal conductivity were improved. The research results in increasing conductivity and thermal conductivity by 5% and 15%, respectively, while the tensile strength is increased by 6% higher than Ag-Cu alloy. The anti-electric corrosion property is good, and there is no argent-cadmium steam population originating from the electric arc effect. The addition of lanthanum further reduces the content of oxygen and hydrogen. The optimum quantity of the addition of RE lanthanum in the copper alloy is 0.010% - 0.020% .
基金financial support from ISRO under RESPOND scheme(No.ISRO/RES/3/580/2007-08)
文摘The electrodeposition of A1 and A1-Cu binary alloys on to gold substrates from a room temperature ionic liquid electrolyte containing A1C13-EtaNHC1 was studied. The electrochemical behavior of the electrolyte and the mechanism of deposition were investigated through cyclic voltammetry (CV), and the properties of deposits obtained were assessed by scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) and X-ray diffraction (XRD). A1 of 70μm in thickness and an A1-Cu alloy of 30μm in thickness with 8at% copper were deposited from the electrolyte. SEM images of the deposits indicate that the A1 deposit was smooth and uniform, whereas the Al-Cu deposit was nodular. The average crystalline size, as determined by XRD patterns, was found to be (30±5) and (29±5) nm, respectively, for A1 and A1-Cu alloys. Potentiodynamic polarization (Tafel plots) and electrochemical impedance spectroscopic (EIS) measurements showed that Al-Cu alloys are more corrosion resistant than Al.
基金a grant from the National Natural Sciences Foundation of China (No. 30170945)
文摘To study the effect of titanium alloy cage on the treatment of the ischemic necrosis of femoral head in dog, the model of the ischemic necrosis of femoral head was made with the liquid nitrogen in 15 hybrid adult dogs. The titanium alloy cage made of a hollow cylinder was driven into the subchondral bone of necrotic femoral head via central channel. The dogs were divided into 3 groups, each group was sacrificed 3, 6, 12 weeks after the operation respectively. No collapse of femoral head was observed after the operation. The position of the cages was good on radiograph. Microscopically, the cancellous bone of necrotic femoral head rebuilt gradually and grew into cage. After 12 weeks of creeping substitution, the cancellous bone filled up the hollow cavity and holes of the cages. It is concluded that the titanium alloy cage can provide structural support for the subchondral bone and prevent collapse and can be used for the treatment of the ischemic necrosis of femoral head.
基金This research was financially supported by the National Natural Science Foundation of China (No.50574020) and Shanghai BaoSteel Group Co.
文摘The laser cladding of Ni1015 alloy on Cu substrate was prepared by a high power continuous wave CO2 laser. Its microstructure was analyzed by optical microscope (OM), scanning electron microscope (SEM), and X-Ray diffraction (XRD). The average microhardness of the cladding coating was Hv 280, which was almost three times of that of the Cu substrate (Hv 85). OM and SEM observations showed that the obtained coating had a smooth and uniform surface, as well as a metallurgical combination with the Cu substrate without cracks and pores at the interface. With the addition of copper into the nickel-based alloy, the differences of thermal expansion coefficient and melting point between the interlayer and cladding were reduced, which resulted in low stresses during rapid cooling. Moreover, large amount of (Cu, Ni) solid solution formed a metallurgical bonding between the cladding coating and the substrate, which also relaxed the stresses, leading to the reduction of interfacial cracks and pores after laser cladding.
基金financially supported by Guangdong Provincial Industrial High-tech Project (No. 2015A010105020)Guangzhou Science & Technology New Star of Pearl River Project (No. 2012J2200096)+3 种基金the Open Research Fund of State Key Laboratory of Powder Metallurgy of Central South UniversityGuangdong Provincial Innovation Ability Construction Project (No. 2016B070701024)Guangzhou Innovation Platform Construction and Sharing Project (No. 201509010003)Guangdong Provincial Science & Technology Basic Condition Construction Field Project (No. 2014B030301012)
文摘Al2O3 dispersion copper alloy powder was prepared by intemal oxidation, and three consolidation methods--high-velocity compaction (HVC), hot pressing (HP), and hot extrusion (HE)--were used to prepare Al2O3 dispersion-strengthened copper (Cu-Al2O3) alloys. The microstructures and properties of these alloys were investigated and compared. The results show that the alloys prepared by the HP and HE methods exhibited the coarsest and finest grain sizes, respectively. The alloy prepared by the HVC method exhibited the lowest relative density (98.3% vs. 99.5% for HP and 100% for HE), which resulted in the lowest electrical conductivity (81% IACS vs. 86% IACS for HP and 87% IACS for HE). However, this alloy also exhibited the highest hardness (77 HRB vs. 69 HRB for HP and 70 HRB for HE), the highest compressive strength (443 MPa vs. 386 MPa for I/P and 378 MPa for HE), and the best hardness retention among the investigated alloys. The results illustrate that the alloy prepared by the HVC method exhibits high softening temperature and good mechanical properties at high temperatures, which imply long service life when used as spot-welding electrodes.
基金This project is supported by National Natural Science Foundation of China ( NSFC)(10577010)
文摘This paper mainly concentrated on the feasibility of friction stir welding of dissimilar metal of aluminum alloy to copper (I2) and a preliminary analysis of welding parameters influencing on the microstructures and properties of joint was carried out. The results indicated that the thickness of workpiece played an important role in the welding parameters which could succeed in the friction stir welding of dissimilar metal of copper to aluminum alloy, and the parameters were proved to be a narrow choice. The interfacial region between copper and aluminum in the dissimilar joint was not uniformly mixed, constituted with part of incomplete mixing zone, complete mixing zone, dispersion zone and the most region' s boundary was obvious. Meantime a kind banded structure with inhomogeneous width was formed. The intermetallic compounds generated during friction stir welding in the interfacial region were mainly CugAl4, Al2Cu etc, and their hardness was higher than oihers.
基金the funding support of Babol Noshirvani University of Technology (No. BNUT/370167/97)
文摘Dissimilar joints comprised of copper–nickel and steel alloys are a challenge for manufacturers in modern industries, as these metals are not thermomechanically or chemically well matched. The present study investigated the effects of tool rotational speed and linear speed on the microstructure and mechanical properties of friction stir-welded C71000 copper–nickel and 340 stainless steel alloys using a tungsten carbide tool with a cylindrical pin. The results indicated that a rotational-to-linear speed ratio of 12.5 r/mm did not cause any macro defects, whereas some tunneling defects and longitudinal cracks were found at other ratios that were lower and higher. Furthermore, chromium carbide was formed on the grain boundaries of the 304 stainless steel near the shoulder zone and inside the joint zone, directing carbon and chromium penetration toward the grain boundaries. Tensile strength and elongation percentages were 84% and 65% of the corresponding values in the copper–nickel base metal, respectively.
文摘With CuMn alloy as interlayer, the transient liquid phase (TLP) diffusion bonding of Cu alloys (CuAlBe) to stainless steel (1Cr18Ni9Ti) was studied. The results show that the bonding pressure, time and temperature and the content of Mn in CuMn alloy have great effects on the strength of bonding interface; when they are 1 MPa, 40 min, 1 223 K and 30% respectively, the maximum joint strength of 487 MPa is attained. The fracture occurring at the bonding interface is a plastic one and the effect of Mn has been analyzed.
文摘Mechanical properties and tribological behavior of a novel cast heat resisting copper based alloy are investigated. The corresponding properties of a commercial aluminum bronze C95500 (ASTM B30) are compared with the alloy. The results show that the alloy possesses better mechanical properties and tribological behaviors than that of C95500 at elevated temperature. The tensile strength, elongation and hardness at 500℃ are 470MPa, 2.5% and HB220, respectively. The wear rate of the developed alloy at ambient and elevated temperature is about one sixth and one fortieth of that of C95500, respectively. The alloy is very suitable for ma nufacturing heat resisting and wear resisting parts. Major strengthening mechanisms for the alloy are solution strengthening and the second phase strengthening.
文摘The grain boundary structure of Cu alloy was observed and the characteristic of the boundaries was studied,including 70∶30 cupronickel and 70∶30 brass. The results show that in the case of the 70∶30 cupronickel thin platelets with nickel and iron enrichment in it precipitate intergranular so that the alloy was sensitive to seawater corrosion. In the case of 70∶30 brass the situation of grain boundary segregation of different inclusions made the corrosion resistance of the alloy even worse. All of those were discovered through the corrosion behavior of the two different copper alloys served in various environments. The experimental methods used here were, scanning electron microscopy(SEM), transmission electron microscopy(TEM) and energy dispersive of X ray(EDX). The intergranular corrosion morphologies of those copper alloys served in engineering or exposed to seawater for a long term were given.
基金financially supported by the Aeronautical Science Foundation of China(No.2012ZF53080)the Shaanxi Province Science and Technology Research and Development Program of China(No.2013K08-11)+1 种基金the Fund of the State Key Laboratory of Solidification Processing in Northwestern Polytechnical University(No.SKLSP201009)the 111 Project of China(No.B08040)
文摘The mechanical properties of Al-Cu-Mn casting alloy mainly depend on the morphology, distribution, size, and number ofθ′(Al2Cu) precipitates. In this study, we have analyzed the effect of rare earth samarium (Sm) addition on the kinetics of precipitation in the Al-Cu-Mn casting alloy by using differential scanning calorimetry (DSC) and high-resolution transmission electron microscopy. Thermal ef-fect peaks that are attributed to the formation and the dissolution of Guinier-Preston (GP) zone andθ′phase were identified from the DSC curves. The activation energy ofθ′formation was calculated by using both the Kissinger method and the analytical model, and the corre-sponding results were compared. Results suggest that the activation energy ofθ′formation in Al-Cu-Mn alloy is dramatically higher than that in Al-Cu-Mn-Sm alloy. Accordingly, it is concluded that the addition of rare earth Sm decreases the activation energy ofθ′formation and promotes the formation ofθ′precipitates.