The dispersion behavior of micro-diamond particles ranging from 0 to 0.5 micron was compared between in DI water and in electroless nickel solution. The effects of the concentration of electroless solution, temperatur...The dispersion behavior of micro-diamond particles ranging from 0 to 0.5 micron was compared between in DI water and in electroless nickel solution. The effects of the concentration of electroless solution, temperature, ultrasonic treatment, stirring speed, and baffles on the size distribution of micro diamond particles in electroless nickel solution were studied. Results show that the dispersion of micro diamond particles in DI water is obviously superior to that in electroless nickel solution. Micro diamond particles agglomerate evidently when the concentration of electroless solution Velect：VDI in dispersion media exceeds 5%0. Diamond particles agglomerate more and more seriously with the increase of the ion concentration. Applying ultrasonic, increasing stirring speed and adding baffles are helpful to improving the dispersion of diamond particles in the electroless nickel solution and its uniform distribution in the Ni-P coating.展开更多
基金Funded by the Jiangsu Key Laboratory for Materials Tribology(No.kjsmcx0901)
文摘The dispersion behavior of micro-diamond particles ranging from 0 to 0.5 micron was compared between in DI water and in electroless nickel solution. The effects of the concentration of electroless solution, temperature, ultrasonic treatment, stirring speed, and baffles on the size distribution of micro diamond particles in electroless nickel solution were studied. Results show that the dispersion of micro diamond particles in DI water is obviously superior to that in electroless nickel solution. Micro diamond particles agglomerate evidently when the concentration of electroless solution Velect：VDI in dispersion media exceeds 5%0. Diamond particles agglomerate more and more seriously with the increase of the ion concentration. Applying ultrasonic, increasing stirring speed and adding baffles are helpful to improving the dispersion of diamond particles in the electroless nickel solution and its uniform distribution in the Ni-P coating.