Quantitative analysis was employed to establish reasonable and practical homogenization model of INCONEL718 superalloy. Metallographic method was applied to determining the incipient melting temperature. The result sh...Quantitative analysis was employed to establish reasonable and practical homogenization model of INCONEL718 superalloy. Metallographic method was applied to determining the incipient melting temperature. The result shows that the incipient melting temperature of d406 mm INCONEL718 ingot is situated between 1 170 ℃ and 1 180 ℃. In order to predict the elimination process of Laves phase in quantity, a time and temperature dependent homogenization model was proposed. Among all the elements in the as-cast microstructure, Nb and Ti are the most positive segregated elements. The diffusion coefficients of alloying elements at 1 140 ℃ were obtained by fitting the linear relationship between In δ （δ residual segregation index） and time. The calculation results of diffusion coefficients were compared with other two commercial Nb-bearing superalloys.展开更多
Inconel 718 superalloy is widely used in the aerospace and turbine industry. Segregation of niobium appears in the laser cladding Inconel 718 superalloy and consequently influences the phase transformation during the ...Inconel 718 superalloy is widely used in the aerospace and turbine industry. Segregation of niobium appears in the laser cladding Inconel 718 superalloy and consequently influences the phase transformation during the rapid solidification. In order to control the microstructure and improve the mechanical properties of the deposited coating, the the influence of solidification conditions on the segregation of niobium and the resultant formation of Nb-rich Laves phase was studied using the microstructure observation and EDS analysis. The results show that the cooling rate has considerable influence on the microstructure of the deposited coating. High cooling rate is beneficial for suppressing the segregation of Nb and reducing the formation of Laves phase, which is believed to be detrimental to the performance of the Inconel 718 alloy.展开更多
Inconel 718 superalloys deposited by laser solid forming （LSF） were heat treated with solution treatment,intermediate heat treatment （IHT） and two-stage aging treatment in sequence （SITA heat treatment）.The effe...Inconel 718 superalloys deposited by laser solid forming （LSF） were heat treated with solution treatment,intermediate heat treatment （IHT） and two-stage aging treatment in sequence （SITA heat treatment）.The effect of IHT temperature on microstructure,tensile property and notch sensitivity of LSFed Inconel 718 superalloy at 500 ℃ were investigated.As-deposited columnar grains have transformed to equiaxed grains and the grains were refined due to the recrystallization during the SITA heat treatment.It is found that the size and amount of δ phase dispersed at grain boundaries decreased with the increasing of IHT temperature,and δ phase disappeared when the IHT temperature reached 1 020 ℃.The ultimate tensile strength （UTS） and yield strength （YS） of smooth samples increased to a maximum when the IHT temperature reached 980 ℃ and then decreased slightly to a minimum when the IHT temperature was 1 000 ℃,and followed by slight increasing again till the IHT temperature reached 1 020 ℃,resulted from the competition of precipitation strengthening effect of γ″ and γ＇ phase and the grain boundary weakening effect caused by the gradual disappearance of δ phase with increasing the IHT temperature.The notch sensitivity factor （qe） decreased but still greater than 1 as the IHT temperature increased,which is attributed to the decrease of the size and amount of δ precipitation.展开更多
The microstructure and composition of the residual liquid at different temperatures were investigated by scanning electron microscopy （SEM） and energy dispersive X-ray spectrometer （EDX） associated with the Thermo...The microstructure and composition of the residual liquid at different temperatures were investigated by scanning electron microscopy （SEM） and energy dispersive X-ray spectrometer （EDX） associated with the Thermo-calc software calculation of the equilibrium phase diagrams of Inconel 718 and segregated liquid. The liquid density difference and Rayleigh number variation during solidification were estimated as well. It is found that the heavy segregation of Nb in liquid prompts the precipitation of δ and Laves phase directly from liquid and the resultant quenched liquid microstructure consists of pro-eutectic γ＋eutectic,or complete eutectic according to the content of Nb from low to high. The liquid density increases with decreasing temperature during the solidification of Inconel 718 and the liquid density difference is positive. The largest relative Rayleigh number occurs at 1320°C when the liquid fraction is about 40vol%.展开更多
Inconel 718 superalloy coating was prepared on a martensitic steel substrate by cold gas dynamic spraying （ CGDS ）. Microstructure and micro-hardness of the coating were characterized by means of scanning electronic...Inconel 718 superalloy coating was prepared on a martensitic steel substrate by cold gas dynamic spraying （ CGDS ）. Microstructure and micro-hardness of the coating were characterized by means of scanning electronic microscope （SEM） ,energy dispersive spectrometer （EDS）, and micro-hardness and nano-indentation tests. The results have indicated that the coating＇ s thickness can reach more than 300 um, and there exists a good interfacial cohesion between the coating and the substrate. The quantity and size of the defects at the bottom, middle and top areas increase gradually. There is no significant change to the original microstructure of the Inconel 718 superalloy particle after the process of CGDS ;and an obvious torsional deformation on the particle＇ s profile is produced while little deformation at the center part occurs. The micro-hardness of the coating at the bottom, middle and top areas decreases in turn. Compared with the bottom area, the micro-hardness of the middle and top areas decreases by about 10% and 21%, respectively. The nano-hardness of the coating is much lower than the original particle,which decreases by about 13.5% at the bottom area and 28% at the top area,respectively. The distribution of micro-defects is an important factor to the micro-hardness of the coating.展开更多
基金Project (08dj1400402) supported by the Major Program for the Fundamental Research of Shanghai Committee of Science and Technology,China
文摘Quantitative analysis was employed to establish reasonable and practical homogenization model of INCONEL718 superalloy. Metallographic method was applied to determining the incipient melting temperature. The result shows that the incipient melting temperature of d406 mm INCONEL718 ingot is situated between 1 170 ℃ and 1 180 ℃. In order to predict the elimination process of Laves phase in quantity, a time and temperature dependent homogenization model was proposed. Among all the elements in the as-cast microstructure, Nb and Ti are the most positive segregated elements. The diffusion coefficients of alloying elements at 1 140 ℃ were obtained by fitting the linear relationship between In δ （δ residual segregation index） and time. The calculation results of diffusion coefficients were compared with other two commercial Nb-bearing superalloys.
基金Project(51341004)supported by the National Natural Science Foundation of ChinaProject(S050ITP7005)supported by the Shanghai Jiao Tong University Undergraduate Innovative Practice Program,China
文摘Inconel 718 superalloy is widely used in the aerospace and turbine industry. Segregation of niobium appears in the laser cladding Inconel 718 superalloy and consequently influences the phase transformation during the rapid solidification. In order to control the microstructure and improve the mechanical properties of the deposited coating, the the influence of solidification conditions on the segregation of niobium and the resultant formation of Nb-rich Laves phase was studied using the microstructure observation and EDS analysis. The results show that the cooling rate has considerable influence on the microstructure of the deposited coating. High cooling rate is beneficial for suppressing the segregation of Nb and reducing the formation of Laves phase, which is believed to be detrimental to the performance of the Inconel 718 alloy.
基金Funded by the Program for New Century Excellent Talents in University of China (No.NCET-06-0879)the National Natural Science Foundation of China (NSFC) (No.50971102)+2 种基金NPU Foundation for Fundamental Research(No.NPU-FFR-JC200808)the Fund of the State Key Laboratory of Solidification Processing (NPU) (Nos.16-TZ-2007 and 39-QZ-2009)supported by the Program of Introducing Talents of Discipline to Universities (No.08040)
文摘Inconel 718 superalloys deposited by laser solid forming （LSF） were heat treated with solution treatment,intermediate heat treatment （IHT） and two-stage aging treatment in sequence （SITA heat treatment）.The effect of IHT temperature on microstructure,tensile property and notch sensitivity of LSFed Inconel 718 superalloy at 500 ℃ were investigated.As-deposited columnar grains have transformed to equiaxed grains and the grains were refined due to the recrystallization during the SITA heat treatment.It is found that the size and amount of δ phase dispersed at grain boundaries decreased with the increasing of IHT temperature,and δ phase disappeared when the IHT temperature reached 1 020 ℃.The ultimate tensile strength （UTS） and yield strength （YS） of smooth samples increased to a maximum when the IHT temperature reached 980 ℃ and then decreased slightly to a minimum when the IHT temperature was 1 000 ℃,and followed by slight increasing again till the IHT temperature reached 1 020 ℃,resulted from the competition of precipitation strengthening effect of γ″ and γ＇ phase and the grain boundary weakening effect caused by the gradual disappearance of δ phase with increasing the IHT temperature.The notch sensitivity factor （qe） decreased but still greater than 1 as the IHT temperature increased,which is attributed to the decrease of the size and amount of δ precipitation.
文摘The microstructure and composition of the residual liquid at different temperatures were investigated by scanning electron microscopy （SEM） and energy dispersive X-ray spectrometer （EDX） associated with the Thermo-calc software calculation of the equilibrium phase diagrams of Inconel 718 and segregated liquid. The liquid density difference and Rayleigh number variation during solidification were estimated as well. It is found that the heavy segregation of Nb in liquid prompts the precipitation of δ and Laves phase directly from liquid and the resultant quenched liquid microstructure consists of pro-eutectic γ＋eutectic,or complete eutectic according to the content of Nb from low to high. The liquid density increases with decreasing temperature during the solidification of Inconel 718 and the liquid density difference is positive. The largest relative Rayleigh number occurs at 1320°C when the liquid fraction is about 40vol%.
文摘Inconel 718 superalloy coating was prepared on a martensitic steel substrate by cold gas dynamic spraying （ CGDS ）. Microstructure and micro-hardness of the coating were characterized by means of scanning electronic microscope （SEM） ,energy dispersive spectrometer （EDS）, and micro-hardness and nano-indentation tests. The results have indicated that the coating＇ s thickness can reach more than 300 um, and there exists a good interfacial cohesion between the coating and the substrate. The quantity and size of the defects at the bottom, middle and top areas increase gradually. There is no significant change to the original microstructure of the Inconel 718 superalloy particle after the process of CGDS ;and an obvious torsional deformation on the particle＇ s profile is produced while little deformation at the center part occurs. The micro-hardness of the coating at the bottom, middle and top areas decreases in turn. Compared with the bottom area, the micro-hardness of the middle and top areas decreases by about 10% and 21%, respectively. The nano-hardness of the coating is much lower than the original particle,which decreases by about 13.5% at the bottom area and 28% at the top area,respectively. The distribution of micro-defects is an important factor to the micro-hardness of the coating.