Strain rate and cold rolling dependence of tensile strength and ductility in high nitrogen nickel-free austenitic stainless steel

The tensile strength and ductility of a high nitrogen nickel-free austenitic stainless steel with solution and cold rolling treatment were investigated by performing tensile tests at different strain rates and at room temperature. The tensile tests demonstrated that this steel exhibits a significant strain rate and cold rolling dependence of the tensile strength and ductility.With the increase of the strain rate from 10^-4s^-1to 1 s^-1, the yield strength and ultimate tensile strength increase and the uniform elongation and total elongation decrease. The analysis of the double logarithmic stress–strain curves showed that this steel exhibits a two-stage strain hardening behavior, which can be well examined and analyzed by using the Ludwigson equation. The strain hardening exponents at low and high strain regions（n2and n1） and the transition strain（εL） decrease with increasing strain rate and the increase of cold rolling RA. Based on the analysis results of the stress–strain curves, the transmission electron microscopy characterization of the microstructure and the scanning electron microscopy observation of the deformation surfaces, the significant strain rate and cold rolling dependence of the strength and ductility of this steel were discussed and connected with the variation in the work hardening and dislocation activity with strain rate and cold rolling.

Aging precipitation and recrystallization in high-nitrogen austenitic stainless steel

The interaction between precipitation and recrystallization in cold deformed Fe-18Cr-12Mn-0.48N high-nitrogen austenitic stainless steel was investigated by means of hardness test, optical microscopy (OM) and transmission electron microscopy (TEM). The results show that the recrystallization of the steel begins at about 750℃ . When aging at 750℃ , the precipitation occurs prior to recrystallization. Large numbers of the second phases nucleate in dislocation, grain boundary and subgrain boundary. Precipitation of the second-phase particles hinders the formation of recrystallization nucleus.

Application of Grain Boundary Engineering to Improve Intergranular Corrosion Resistance in a Fe–Cr–Mn–Mo–N High-Nitrogen and Nickel-Free Austenitic Stainless Steel

Optimization of grain boundary engineering(GBE) process is explored in a Fe–20Cr–19Mn–2Mo–0.82N high-nitrogen and nickel-free austenitic stainless steel, and its intergranular corrosion(IGC) property after GBE treatment is experimentally evaluated. The proportion of low Σ coincidence site lattice(CSL) boundaries reaches 79.4% in the sample processed with 5% cold rolling and annealing at 1423 K for 72 h;there is an increase of 32.1% compared with the solution-treated sample. After grain boundary character distribution optimization, IGC performance is noticeably improved. Only Σ3 boundaries in the special boundaries are resistant to IGC under the experimental condition. The size of grain cluster enlarges with increasing fraction of low ΣCSL boundaries, and the amount of Σ3 boundaries interrupting the random boundary network increases during growth of the clusters, which is the essential reason for the improvement of IGC resistance.

Effect of Grain Size on Mechanical Properties of Nickel-Free High Nitrogen Austenitic Stainless Steel

The fine grained structures of nickel-free high nitrogen austenitic stainless steels had been obtained by means of cold rolling and subsequent annealing. The relationship between microstructure and mechanical properties and gain size of nickel-free high nitrogen austenitic stainless steels was examined. High strength and good ductility of the steel were found. In the grain size range, the Hall-Petch dependency for yield stress, tensile strength, and hardness was valid for grain size ranges for the nickel-free high nitrogen austenitic stainless steel. In the present study, the ductility of cold rolled nickel-free high nitrogen austenitic stainless steel decreased with annealing time when the grain size was refined. The fracture surfaces of the tensile specimens in the grain size range were covered with dimples as usually seen in a ductile fracture mode.

In vitro Study on a New High Nitrogen Nickel-free Austenitic Stainless Steel for Coronary Stents

Most commercialized coronary stents are made of 316L stainless steels due to its good combination of properties, and currently some new stents are made of cobalt-based alloy owing to its higher mechanical properties. However, the presence of high quantity of nickel and/or cobalt elements in these materials, which are known to trigger the toxic and allergic responses, has caused many concerns. Nickel-free austenitic stainless steels have been developed in order to solve these problems. In this paper, based on the development of a new Fe- Cr-Mn-Mo-N type high nitrogen nickel-free austenitic stainless steel, properties such as mechanical property, corrosion resistance in Hankls solution, and in vitro blood compatibility including the kinetic clotting time and the platelets adhesion, were investigated in comparison to the above two conventional materials, a 316L stainless steel and a Co-28Cr-6Mo alloy. The results showed that the new high nitrogen steel possessed better combination of mechanical properties, corrosion resistance and blood compatibility than those of 316L steel and the Co-28Cr-OMo alloy, and can be a promising alternative material for manufacture of coronary stents.

Effect of Cold Deformation on the Friction–Wear Property of a Biomedical Nickel-Free High-Nitrogen Stainless Steel

The microstructural,mechanical and corrosion properties of different cold-rolled biomedical nickel-free highnitrogen stainless steels（NFHNSSs） were investigated to study the effect of cold deformation on its dry wear resistance as well as corrosion–wear behaviors in distilled water and Hank＇s solution. The results indicated that NFHNSS was characterized by stable austenite and possessed excellent work-hardening capacity; due to increasing cold deformation,the corrosion resistance just decreased very slightly and the dry wear rate decreased initially but subsequently increased,while the corrosion–wear resistance was improved monotonically in both distilled water and Hank＇s solution in spite of the presence of corrosive ions. The friction coefficients for different cold-rolled NFHNSSs were very close under the same lubricating condition,but they were the largest in distilled water compared to that in dry wear tests and Hank＇s solution.

Improving Intergranular Stress Corrosion Cracking Resistance in a Fe–18Cr–17Mn–2Mo–0.85N Austenitic Stainless Steel Through Grain Boundary Character Distribution Optimization

The grain boundary character distribution(GBCD) optimization and its effect on the intergranular stress corrosion cracking(IGSCC) resistance in a cold-rolled and subsequently annealed Fe-18 Cr-17 Mn-2 Mo-0.85 N high-nitrogen nickel-free austenitic stainless steel were systematically explored.The results show that stacking faults and planar slip bands appearing at the right amount of deformation(lower than 10%) are beneficial cold-rolled microstructures to the GBCD optimization.The proportion of special boundaries gradually increases in the subsequent stages of recrystallization and grain growth,accompanying with the growth of twin-related domain in the experimental steel.In this way,the fraction of low ∑ coincidence site lattice(CSL) boundaries can reach as high as 82.85% for the specimen cold-rolled by 5% and then annealed at 1423 K for 72 h.After GBCD optimization,low ∑ CSL boundaries and the special triple junctions(J2,J3) of high proportion can greatly hinder the nitride precipitation along grain boundaries and enhance the capability for intergranular crack arrest,thus improving the IGSCC resistance of the experimental steel.