In order to investigate the draping behavior of non-crimp fabrics（NCFs）, two types of carbon NCFs with tricot-chain stitches or chain stitches were formed on a hemispherical mould via a stretch forming process. The ...In order to investigate the draping behavior of non-crimp fabrics（NCFs）, two types of carbon NCFs with tricot-chain stitches or chain stitches were formed on a hemispherical mould via a stretch forming process. The shear angle and forming defects of the fabrics were measured on the hemisphere, under different blank holder forces（BHFs）. The results showed that increasing BHF could enhance the shear angle slightly, reduce the asymmetry for the deformation of the fabrics, and change the main type of the process-induced defects. Besides, compression tests were performed on the corresponding composite components. By analyzing the change of fiber volume fraction and structural parameters of the textile reinforcements, the effects of draping behavior of NCFs on the mechanical performance of the composites were studied. The results reveal that draping process has distinguishable impacts on the mechanical properties of the final components, which is closely related to the stitching pattern of the NCFs.展开更多
In previous research much effort has been devoted to the geometry of woven fabrics and relat-ed problems under the assumption of constant yarn configuration in fabric.This paper will first re-port that image crimp (ya...In previous research much effort has been devoted to the geometry of woven fabrics and relat-ed problems under the assumption of constant yarn configuration in fabric.This paper will first re-port that image crimp (yarn crimp measured by an image analysis method) seems larger than actualvalue.From the explanation of this result,the variation of yarn configuration in woven fabric dueto the non-uniform flattening is revealed.The significance of this actual structure of woven fabricsis discussed.It is believed that the variation of yarn configuration is very important for fabric per-formance,and may be an advantage for fabric quality.展开更多
Effects of ultrasonic vibrations on mechanical properties of fiber reinforced plastics were investigated during molding resin impregnation process in vacuum assisted resin transfer molding.?The vacuum bag including th...Effects of ultrasonic vibrations on mechanical properties of fiber reinforced plastics were investigated during molding resin impregnation process in vacuum assisted resin transfer molding.?The vacuum bag including the preformed each?non-crimp fabrics (carbon and glass fibers)?was placed in a water bath of an ultrasonic wave generator during resin impregnation. The mechanical properties of the laminates were evaluated?through the mechanical strength tests and scanning electron microscope?(SEM) observation. The results revealed that ultrasonic waves improved transverse tensile, flexural, interlaminar shear, and compressive strengths of the carbon fiber (CF) laminates and interlaminar shear and compressive strengths of the glass fiber (GF) laminates. It was found from SEM observation that the fracture modes of the CF and GF laminates processed using ultrasonic waves were resin fracture. Accordingly, the adhesion of the fiber/resin interface was improved by oscillating ultrasonic vibration during resin impregnation, leading to an increase of the interface strength.展开更多
基金Funded by the National Natural Science Foundation of China(No.51203144)
文摘In order to investigate the draping behavior of non-crimp fabrics（NCFs）, two types of carbon NCFs with tricot-chain stitches or chain stitches were formed on a hemispherical mould via a stretch forming process. The shear angle and forming defects of the fabrics were measured on the hemisphere, under different blank holder forces（BHFs）. The results showed that increasing BHF could enhance the shear angle slightly, reduce the asymmetry for the deformation of the fabrics, and change the main type of the process-induced defects. Besides, compression tests were performed on the corresponding composite components. By analyzing the change of fiber volume fraction and structural parameters of the textile reinforcements, the effects of draping behavior of NCFs on the mechanical performance of the composites were studied. The results reveal that draping process has distinguishable impacts on the mechanical properties of the final components, which is closely related to the stitching pattern of the NCFs.
文摘In previous research much effort has been devoted to the geometry of woven fabrics and relat-ed problems under the assumption of constant yarn configuration in fabric.This paper will first re-port that image crimp (yarn crimp measured by an image analysis method) seems larger than actualvalue.From the explanation of this result,the variation of yarn configuration in woven fabric dueto the non-uniform flattening is revealed.The significance of this actual structure of woven fabricsis discussed.It is believed that the variation of yarn configuration is very important for fabric per-formance,and may be an advantage for fabric quality.
文摘Effects of ultrasonic vibrations on mechanical properties of fiber reinforced plastics were investigated during molding resin impregnation process in vacuum assisted resin transfer molding.?The vacuum bag including the preformed each?non-crimp fabrics (carbon and glass fibers)?was placed in a water bath of an ultrasonic wave generator during resin impregnation. The mechanical properties of the laminates were evaluated?through the mechanical strength tests and scanning electron microscope?(SEM) observation. The results revealed that ultrasonic waves improved transverse tensile, flexural, interlaminar shear, and compressive strengths of the carbon fiber (CF) laminates and interlaminar shear and compressive strengths of the glass fiber (GF) laminates. It was found from SEM observation that the fracture modes of the CF and GF laminates processed using ultrasonic waves were resin fracture. Accordingly, the adhesion of the fiber/resin interface was improved by oscillating ultrasonic vibration during resin impregnation, leading to an increase of the interface strength.