A test for crumb rubber modified asphalt containing 20% crumb rubber particles（30 mesh） was performed using a scanning electron microscope（SEM）.The experimental results indicate that the crumb rubber particles are...A test for crumb rubber modified asphalt containing 20% crumb rubber particles（30 mesh） was performed using a scanning electron microscope（SEM）.The experimental results indicate that the crumb rubber particles are evenly distributed in the asphalt.Shear rate sweep and shear-temperature sweep tests on the crumb rubber modified asphalt at-20-80 ℃ using a dynamic shear rheology（DSR） instrument,were carried out.The tests show that the complex modulus decreases with increasing temperature;at equivalent temperature,higher load frequencies lead to a larger complex modulus,and this value increasingly decreases as the temperature increases;the phase angle increases with temperature and decreases as the load frequency increases.It can be concluded that the rutting resistance limiting temperature of crumb rubber modified asphalt is 78 ℃,and the anti-fatigue limiting temperature is 16 ℃,which shows that the asphalt has preferable rutting resistance characteristics at high temperature,as well as anti-fatigue characteristics.In addition,the complex modulus master curve at different temperatures was plotted according to the time temperature equivalence principle,which allows the study of the dynamic state behavior of crumb rubber modified asphalt at a wide range of load frequency.展开更多
Crumb rubber modified asphalt containing 20 percent crumb rubber particles of 30 mesh has been examined by Scanning Electron Microscope （SEM） to observe the microcosmic appearance and the characteristic distribution...Crumb rubber modified asphalt containing 20 percent crumb rubber particles of 30 mesh has been examined by Scanning Electron Microscope （SEM） to observe the microcosmic appearance and the characteristic distribution of crumb rubber particles in asphalt. The SEM pictures reveal that the crumb rubber particles distribute evenly in the asphalt and they are compatible well with asphalt. The shear creep test of crumb rubber modified asphalt was carried out at -10 ℃ and 40 ℃ by Dynamic Shear Rheology （DSR）. The shearing deformation at different temperature and creep stiffness modulus curve at loading stage of crumb rubber modified asphalt have been measured. The stiffness modulus of crumb rubber modified asphalt is much temperature sensitive and it decays much quick at the early stage of loading than normal asphalt. The rate of decay of stiffness modulus is slow at the subsequent stage and stiffness modulus approaches to a stable value at the final stage at a higher temperature. In addition, Burgers model is suitable to describe and simulate experimental results of viscoelastic properties of the crumb rubber modified asphalt.展开更多
In this paper,organic montmorillonite(OMMT)was added into crumb rubber modified asphalt(CRMA)to improve its high temperature performance,anti-aging performance and storage stability.The effects of different OMMT conte...In this paper,organic montmorillonite(OMMT)was added into crumb rubber modified asphalt(CRMA)to improve its high temperature performance,anti-aging performance and storage stability.The effects of different OMMT content on properties of CRMA were studied.The rutting factor obtained by dynamic shear rheological(DSR)test was adopted to evaluate the high-temperature performance.The creep stiffness and m value determined by the bending beam rheometer(BBR)test were employed to evaluate the low-temperature performance.The softening point,ductility,rutting factor before and after rolling thin film ovens test(RTFOT)and pressure aging vessel test(PAV)were compared to characterize the aging properties.Moreover,the segregation test after being reserved for 48 h and 7 d was conducted,and the softening point and rutting factor of upper and lower layers of segregation pipe were adopted to evaluate the storage stability.The results indicated that the high-temperature performance and anti-aging performance were developed with the increasing content of OMMT,while the low-temperature performance deteriorated.The storage stability was improved with the increasing content of OMMT before the content exceeded 4%,after which the storage stability declined.Taking account of all factors,it is suggested that the optimum content of OMMT is 3%−4%.展开更多
In this study,it is shown how recycled rubber and waste plastics can modify the softening point and penetration of asphalt traditionally used for highways.It is shown that the modified asphalt can meet the performance...In this study,it is shown how recycled rubber and waste plastics can modify the softening point and penetration of asphalt traditionally used for highways.It is shown that the modified asphalt can meet the performance index requirements when the components are present with a certain proportion or relative ratio(1:3.5).The dispersion process of the masterbatch in base asphalt can effectively be implemented,with good results and a smaller mixing time.The proposed approach may be regarded as a good strategy to achieve energy savings and protection of the environment.展开更多
The poor fatigue properties and high rigidity of cement asphalt emulsion treated mis(CETM) have for a long time been problems restricting its further development making it impossible for C-ETMto be used as surface lay...The poor fatigue properties and high rigidity of cement asphalt emulsion treated mis(CETM) have for a long time been problems restricting its further development making it impossible for C-ETMto be used as surface layer materials. In this paper, a new kind of cement asphalt emulsion composite-rubberized asphalt emulsion modified Portland cement concrete (RACC) was proposed, which was formed by dispersing rubberized aSPhalt emulsion coated coarse aggregates into cement mortar matrix. In order to evaluate systematically the performance of RACC, laboratory tests with nearly one thousand SPecimen were conducted for resilient modulus, fatigue properties, ultimate ban and length,abrasion, temperature contraction, and dry shrinkage. The experimental results show that the problems existed in C-ETM have to a great extends been solved by RACc. To verify the field performance and inquire into paving technology, teSt road appearsatlsfactory it is concluded that when thed ape surface laycr of semi-rigid base course, RACC is more for surface layer material than both Portland cement concrete(PCC) and asphalt concrete(AC)展开更多
Waste rubber-modified asphalt has good anti-aging properties and can significantly improve the service life of asphalt pavements. For domestic and foreign scholars of rubber modified asphalt thermal oxygen aging, phot...Waste rubber-modified asphalt has good anti-aging properties and can significantly improve the service life of asphalt pavements. For domestic and foreign scholars of rubber modified asphalt thermal oxygen aging, photo-oxidative aging and water aging some behavioural research, and rubber asphalt aging after the characteristics of the research progress are reviewed. Especially rubber-modified asphalt after light, water and other multi-factor agingsituations, the aging situation is more serious, for rubber-modified asphalt mixture aging, rubber asphalt anti-aging process research and analysis means are still very few, the future research must have more thinking.展开更多
Conventional repairing methods for asphalt pavement have some inconveniences,such as insufficient strength,and are typically time-consuming.To address these issues,this study proposes a new technological method to des...Conventional repairing methods for asphalt pavement have some inconveniences,such as insufficient strength,and are typically time-consuming.To address these issues,this study proposes a new technological method to design and prepare a high-performance assembled asphalt concrete block for fast repair of the potholes.A series of composite modified asphalt binders with 10%crumb rubber(CR)and different dosages(0%,1%,3%,5%)of polyurethane(PU)are examined to determine the optimized binder.Subsequently,the corresponding asphalt mixtures are prepared for further comparison and assessment of engineering properties,such as moistureinduced damage,high-temperature deformation,and low-temperature cracking characteristics.The test results show that PU can significantly improve the high-temperature performance and hardness of(crumb rubber modified asphalt)CRMA binder;3%PU contributes allowing the resistance of CRMA mixture to moisture-induced damage at higher levels,particularly under water whole immersion;as 3%PU is added,the high-temperature rutting deformation resistance of the CRMA mixture increases significantly,and the low-temperature anti-cracking properties are also improved slightly.Therefore,the innovatively designed high-quality assembled fast-repairing asphalt concrete block is recommended as an appropriate option for highway maintenance.展开更多
The road construction industry aims to contribute to the protection of already compromised environment.Cold mix asphalt(CMA)is a measure initiated by the road industry to protect the environment and preserve energy.De...The road construction industry aims to contribute to the protection of already compromised environment.Cold mix asphalt(CMA)is a measure initiated by the road industry to protect the environment and preserve energy.Despite having additional benefits,CMA has attracted little attention due to its inferior performance.CMA's performance is enhanced using a sustainable binder bio-modifier,natural cup lump rubber(CLR)is one of them.This study evaluated the tensile properties,rutting,moisture susceptibility,and adhesion properties of CLR-modified CMA(CMA-CR).The tensile property was enhanced by 26%due to CLR modification.CMA-CR had excellent rutting resistance of less than 2 mm rut depth at 10,000 load cycles,showing 70%improvement compared with conventional CMA.Moisture susceptibility evaluation indicated that CMA-CR had tensile strength ratio(TSR)value of 104%,satisfying the minimum 80%requirement of AASHTO T283.It also retained more than 96%bitumen coating.The moisture damage resistance was improved by 12%and 10%in terms of TSR and stripping,respectively.The durability results revealed that the CMA-CR mixture prevented higher mass loss,representing 14%improvement compared with conventional CMA.展开更多
The research considered urgent ecological reasons linked to environment such as worn tires, the waste tire rubber＇s powder was collected from the tire cars repair shops （passed from the sieve No 18 μm）, and used t...The research considered urgent ecological reasons linked to environment such as worn tires, the waste tire rubber＇s powder was collected from the tire cars repair shops （passed from the sieve No 18 μm）, and used to improve the asphalt concrete properties. Raw materials used were prepared and tested. Varies of asphalt concrete mixtures were prepared with different ratios of bitumen （5, 5.5, 6, 6.5, 7% % of concrete weight）. The Marshall mix design method was used to determine optimum conditions for bitumen in asphalt concrete with specific weight, stability and flow Test, the optimum amount of bitumen was 6.1% of whole asphalt concrete. The different percentages of waste tire rubber powder （0.0, 0.05, 0.10, 0.15% of bitumen weight） were added in optimum bitumen of asphalt concretes, then specific weight and Marshall test were evaluated. These asphalt-rubber mixtures were found to act quite differently from traditional, unmodified asphalt mixtures. However, these results indicate that improved pavement performance can be achieved with asphalt-rubber binder.展开更多
The research and development of high-performance pavement materials has been intensified owing to the demand for long-life pavements.This study is performed to develop a novel pavement material using waste rubber powd...The research and development of high-performance pavement materials has been intensified owing to the demand for long-life pavements.This study is performed to develop a novel pavement material using waste rubber powder,waste lubricating by-product(LBP),and asphalt.Subsequently,the aging properties and aging mechanism of activated waste rubber powder modified asphalt(ARMA)are investigated based on its rheological properties and microcharacterization.The rheological results show that,compared with waste rubber powder modified asphalt(RMA),ARMA offers a higher aging resistance and a longer fatigue life.A comparison and analysis of the rheological aging parameters of ARMA and RMA show that LBP activation diminishes the aging sensitivity of ARMA.The microcharacterization result shows that the aging of ARMA may be caused by the fact that LBP-activated waste rubber powder is more reactive and can form a dense colloidal structure with asphalt.Therefore,the evaporation loss of asphalt light components by heat and the damage to the colloidal structure by oxygen during the aging process are impeded,and the thermal-oxidative aging resistance of ARMA is improved.展开更多
基金Funded by the Communication Science and Technology Foundation of Inner Mongolia (NJ-2005-25)
文摘A test for crumb rubber modified asphalt containing 20% crumb rubber particles（30 mesh） was performed using a scanning electron microscope（SEM）.The experimental results indicate that the crumb rubber particles are evenly distributed in the asphalt.Shear rate sweep and shear-temperature sweep tests on the crumb rubber modified asphalt at-20-80 ℃ using a dynamic shear rheology（DSR） instrument,were carried out.The tests show that the complex modulus decreases with increasing temperature;at equivalent temperature,higher load frequencies lead to a larger complex modulus,and this value increasingly decreases as the temperature increases;the phase angle increases with temperature and decreases as the load frequency increases.It can be concluded that the rutting resistance limiting temperature of crumb rubber modified asphalt is 78 ℃,and the anti-fatigue limiting temperature is 16 ℃,which shows that the asphalt has preferable rutting resistance characteristics at high temperature,as well as anti-fatigue characteristics.In addition,the complex modulus master curve at different temperatures was plotted according to the time temperature equivalence principle,which allows the study of the dynamic state behavior of crumb rubber modified asphalt at a wide range of load frequency.
基金Funded by Inner Mongolia Communication Technology Project (No.NJ-2005-25)
文摘Crumb rubber modified asphalt containing 20 percent crumb rubber particles of 30 mesh has been examined by Scanning Electron Microscope （SEM） to observe the microcosmic appearance and the characteristic distribution of crumb rubber particles in asphalt. The SEM pictures reveal that the crumb rubber particles distribute evenly in the asphalt and they are compatible well with asphalt. The shear creep test of crumb rubber modified asphalt was carried out at -10 ℃ and 40 ℃ by Dynamic Shear Rheology （DSR）. The shearing deformation at different temperature and creep stiffness modulus curve at loading stage of crumb rubber modified asphalt have been measured. The stiffness modulus of crumb rubber modified asphalt is much temperature sensitive and it decays much quick at the early stage of loading than normal asphalt. The rate of decay of stiffness modulus is slow at the subsequent stage and stiffness modulus approaches to a stable value at the final stage at a higher temperature. In addition, Burgers model is suitable to describe and simulate experimental results of viscoelastic properties of the crumb rubber modified asphalt.
基金Projects(51838001,51878070,51908069)supported by the National Natural Science Foundation of China。
文摘In this paper,organic montmorillonite(OMMT)was added into crumb rubber modified asphalt(CRMA)to improve its high temperature performance,anti-aging performance and storage stability.The effects of different OMMT content on properties of CRMA were studied.The rutting factor obtained by dynamic shear rheological(DSR)test was adopted to evaluate the high-temperature performance.The creep stiffness and m value determined by the bending beam rheometer(BBR)test were employed to evaluate the low-temperature performance.The softening point,ductility,rutting factor before and after rolling thin film ovens test(RTFOT)and pressure aging vessel test(PAV)were compared to characterize the aging properties.Moreover,the segregation test after being reserved for 48 h and 7 d was conducted,and the softening point and rutting factor of upper and lower layers of segregation pipe were adopted to evaluate the storage stability.The results indicated that the high-temperature performance and anti-aging performance were developed with the increasing content of OMMT,while the low-temperature performance deteriorated.The storage stability was improved with the increasing content of OMMT before the content exceeded 4%,after which the storage stability declined.Taking account of all factors,it is suggested that the optimum content of OMMT is 3%−4%.
文摘In this study,it is shown how recycled rubber and waste plastics can modify the softening point and penetration of asphalt traditionally used for highways.It is shown that the modified asphalt can meet the performance index requirements when the components are present with a certain proportion or relative ratio(1:3.5).The dispersion process of the masterbatch in base asphalt can effectively be implemented,with good results and a smaller mixing time.The proposed approach may be regarded as a good strategy to achieve energy savings and protection of the environment.
文摘The poor fatigue properties and high rigidity of cement asphalt emulsion treated mis(CETM) have for a long time been problems restricting its further development making it impossible for C-ETMto be used as surface layer materials. In this paper, a new kind of cement asphalt emulsion composite-rubberized asphalt emulsion modified Portland cement concrete (RACC) was proposed, which was formed by dispersing rubberized aSPhalt emulsion coated coarse aggregates into cement mortar matrix. In order to evaluate systematically the performance of RACC, laboratory tests with nearly one thousand SPecimen were conducted for resilient modulus, fatigue properties, ultimate ban and length,abrasion, temperature contraction, and dry shrinkage. The experimental results show that the problems existed in C-ETM have to a great extends been solved by RACc. To verify the field performance and inquire into paving technology, teSt road appearsatlsfactory it is concluded that when thed ape surface laycr of semi-rigid base course, RACC is more for surface layer material than both Portland cement concrete(PCC) and asphalt concrete(AC)
文摘Waste rubber-modified asphalt has good anti-aging properties and can significantly improve the service life of asphalt pavements. For domestic and foreign scholars of rubber modified asphalt thermal oxygen aging, photo-oxidative aging and water aging some behavioural research, and rubber asphalt aging after the characteristics of the research progress are reviewed. Especially rubber-modified asphalt after light, water and other multi-factor agingsituations, the aging situation is more serious, for rubber-modified asphalt mixture aging, rubber asphalt anti-aging process research and analysis means are still very few, the future research must have more thinking.
基金the Scientific Technology R&D Project of CCCC Asset Management Co.,Ltd.(RP2022015294&RP2022015296).
文摘Conventional repairing methods for asphalt pavement have some inconveniences,such as insufficient strength,and are typically time-consuming.To address these issues,this study proposes a new technological method to design and prepare a high-performance assembled asphalt concrete block for fast repair of the potholes.A series of composite modified asphalt binders with 10%crumb rubber(CR)and different dosages(0%,1%,3%,5%)of polyurethane(PU)are examined to determine the optimized binder.Subsequently,the corresponding asphalt mixtures are prepared for further comparison and assessment of engineering properties,such as moistureinduced damage,high-temperature deformation,and low-temperature cracking characteristics.The test results show that PU can significantly improve the high-temperature performance and hardness of(crumb rubber modified asphalt)CRMA binder;3%PU contributes allowing the resistance of CRMA mixture to moisture-induced damage at higher levels,particularly under water whole immersion;as 3%PU is added,the high-temperature rutting deformation resistance of the CRMA mixture increases significantly,and the low-temperature anti-cracking properties are also improved slightly.Therefore,the innovatively designed high-quality assembled fast-repairing asphalt concrete block is recommended as an appropriate option for highway maintenance.
基金financially supported by the UTM Shine(Q.J130000.2451.09G26)the UTM High Impact Research Grant(Q.J130000.2451.09G20)provided by Universiti Teknologi Malaysia(UTM)。
文摘The road construction industry aims to contribute to the protection of already compromised environment.Cold mix asphalt(CMA)is a measure initiated by the road industry to protect the environment and preserve energy.Despite having additional benefits,CMA has attracted little attention due to its inferior performance.CMA's performance is enhanced using a sustainable binder bio-modifier,natural cup lump rubber(CLR)is one of them.This study evaluated the tensile properties,rutting,moisture susceptibility,and adhesion properties of CLR-modified CMA(CMA-CR).The tensile property was enhanced by 26%due to CLR modification.CMA-CR had excellent rutting resistance of less than 2 mm rut depth at 10,000 load cycles,showing 70%improvement compared with conventional CMA.Moisture susceptibility evaluation indicated that CMA-CR had tensile strength ratio(TSR)value of 104%,satisfying the minimum 80%requirement of AASHTO T283.It also retained more than 96%bitumen coating.The moisture damage resistance was improved by 12%and 10%in terms of TSR and stripping,respectively.The durability results revealed that the CMA-CR mixture prevented higher mass loss,representing 14%improvement compared with conventional CMA.
文摘The research considered urgent ecological reasons linked to environment such as worn tires, the waste tire rubber＇s powder was collected from the tire cars repair shops （passed from the sieve No 18 μm）, and used to improve the asphalt concrete properties. Raw materials used were prepared and tested. Varies of asphalt concrete mixtures were prepared with different ratios of bitumen （5, 5.5, 6, 6.5, 7% % of concrete weight）. The Marshall mix design method was used to determine optimum conditions for bitumen in asphalt concrete with specific weight, stability and flow Test, the optimum amount of bitumen was 6.1% of whole asphalt concrete. The different percentages of waste tire rubber powder （0.0, 0.05, 0.10, 0.15% of bitumen weight） were added in optimum bitumen of asphalt concretes, then specific weight and Marshall test were evaluated. These asphalt-rubber mixtures were found to act quite differently from traditional, unmodified asphalt mixtures. However, these results indicate that improved pavement performance can be achieved with asphalt-rubber binder.
基金supported by the National Natural Science Foundation of China(Grant No.51778136)the Technology Research and Development Project of China Railway(No.J2019G003)The authors would like to thank the staff at the National Demonstration Center for Experimental Road and Traffic Engineering Education(Southeast University)for their active contributions to this study.
文摘The research and development of high-performance pavement materials has been intensified owing to the demand for long-life pavements.This study is performed to develop a novel pavement material using waste rubber powder,waste lubricating by-product(LBP),and asphalt.Subsequently,the aging properties and aging mechanism of activated waste rubber powder modified asphalt(ARMA)are investigated based on its rheological properties and microcharacterization.The rheological results show that,compared with waste rubber powder modified asphalt(RMA),ARMA offers a higher aging resistance and a longer fatigue life.A comparison and analysis of the rheological aging parameters of ARMA and RMA show that LBP activation diminishes the aging sensitivity of ARMA.The microcharacterization result shows that the aging of ARMA may be caused by the fact that LBP-activated waste rubber powder is more reactive and can form a dense colloidal structure with asphalt.Therefore,the evaporation loss of asphalt light components by heat and the damage to the colloidal structure by oxygen during the aging process are impeded,and the thermal-oxidative aging resistance of ARMA is improved.