Thermal diffusion salt-bath vanadizing was finished for Crl2MoV die steel, in order to investigate the properties of vanadium carbide coatings related with the Mo contents in Crl2MoV die steel. Scanning electron micro...Thermal diffusion salt-bath vanadizing was finished for Crl2MoV die steel, in order to investigate the properties of vanadium carbide coatings related with the Mo contents in Crl2MoV die steel. Scanning electron micro- scopic observation reveals that Mo can decrease the growth rate of coating as a carbide forming element. Besides, Mo element can promote grain refinement of the coating. X-ray diffraction analysis shows that the different Mo contents have no influence on the phase structure of the coatings. Energy dispersive spectrum analysis and mechanical properties test show that Mo can diffuse into the coating and make a strengthening effect on the coating.展开更多
The Nb-Ti microalloyed high strength IF steel sheet was used to study the effect of annealing temperature on the microstructures,mechanical properties and textures.The experimental results show that experimental steel...The Nb-Ti microalloyed high strength IF steel sheet was used to study the effect of annealing temperature on the microstructures,mechanical properties and textures.The experimental results show that experimental steel is incomplete recrystallization at 750℃ annealing,but complete recrystallization from 780℃ to 870℃ under experimental conditions.When the annealing temperature was increased,the yield strength and tensile strength would gradually reduce,the plastic strain ratio and yield point elongation would gradually increase.The yield strength,tensile strength,elongation,the plastic strain ratio and the strain hardening exponent were approximate 300MPa,410MPa,36.5%,1.7 and 0.22 respectively under annealing temperature 810℃ to 840℃.When the annealing temperature was increased,the α-textures and γ-textures were gradually weakened,and the α-textures have a trend to {111} texture.Therefore,the suggestion of the optimal recrystallization annealing temperature is about 810℃ to 840℃ in industrial production.展开更多
基金Item Sponsored by National Natural Science Foundation of China(50671012)
文摘Thermal diffusion salt-bath vanadizing was finished for Crl2MoV die steel, in order to investigate the properties of vanadium carbide coatings related with the Mo contents in Crl2MoV die steel. Scanning electron micro- scopic observation reveals that Mo can decrease the growth rate of coating as a carbide forming element. Besides, Mo element can promote grain refinement of the coating. X-ray diffraction analysis shows that the different Mo contents have no influence on the phase structure of the coatings. Energy dispersive spectrum analysis and mechanical properties test show that Mo can diffuse into the coating and make a strengthening effect on the coating.
文摘The Nb-Ti microalloyed high strength IF steel sheet was used to study the effect of annealing temperature on the microstructures,mechanical properties and textures.The experimental results show that experimental steel is incomplete recrystallization at 750℃ annealing,but complete recrystallization from 780℃ to 870℃ under experimental conditions.When the annealing temperature was increased,the yield strength and tensile strength would gradually reduce,the plastic strain ratio and yield point elongation would gradually increase.The yield strength,tensile strength,elongation,the plastic strain ratio and the strain hardening exponent were approximate 300MPa,410MPa,36.5%,1.7 and 0.22 respectively under annealing temperature 810℃ to 840℃.When the annealing temperature was increased,the α-textures and γ-textures were gradually weakened,and the α-textures have a trend to {111} texture.Therefore,the suggestion of the optimal recrystallization annealing temperature is about 810℃ to 840℃ in industrial production.