The enrichment of chloride anion within the occluded cell （OC） for Type 304 austenitic stainless steel in low chloride concentration solution has been investigated by means of a simulated OC. The influence of the en...The enrichment of chloride anion within the occluded cell （OC） for Type 304 austenitic stainless steel in low chloride concentration solution has been investigated by means of a simulated OC. The influence of the enrichment of chloride anion on stress corrosion crack （SCC） of Type 304 stainless steel has been studied. It was observed that the amount of chloride anion migration was proportional to the charge flowing through the anode. Owning to the effects of enrichment of chloride anion, low chloride concentration solution could induce SCC for Type 304 stainless steel.展开更多
An artificial localized corrosion system is assembled and some parameters related to the localized corrosion in active dissolution state (i.e., non-passive state) have been studied. The results showed that the develop...An artificial localized corrosion system is assembled and some parameters related to the localized corrosion in active dissolution state (i.e., non-passive state) have been studied. The results showed that the developed electrochemical system can satisfactorily imitate a naturally formed localized corrosion and the coupling current can indicate the maximum localized propagating rate. In this artificial system, the anodic dissolution reaction followed the auto-catalytic mechanism. The localized corrosion current density was dependent on the area ratio R of the cathode to the occluded anode. While R was equal to or more than 6, the coupling current reached at a maximum value and did not alter with the increase in R-value. Therefore, R=7 is chosen as one of these optimum parameters used in constructing the system, with which the biggest galvanic current might be obtained. In contrast, the thickness of the polymer filler separating the occluded anode area from the bulk electrolyte solution and the volume of the occluded anode area did not affect the corrosion current obviously. They might affect the response time to approach a steady state.展开更多
Corrosion of magnesium alloys is an important issue for their applications in automobile and aerospace industry. pH values as a function of time in two types of simulated occluded corrosion cells(OCC) for magnesium al...Corrosion of magnesium alloys is an important issue for their applications in automobile and aerospace industry. pH values as a function of time in two types of simulated occluded corrosion cells(OCC) for magnesium alloys AZ80 and AM60 were measured. The influence of mass ratio of solution to material or liquid to solid ratio(L/S ratio),initial pH value and chemical compositions of solutions on pH value in OCC was discussed. The experimental results show that pH value for magnesium alloys increases gradually or rapidly in Occ,depending on L/S ratio,initial pH value of solution and chloride ions concentration etc,and then reaches up to 10.5-10.6 and finally stabilizes at the level. The onset in the pH value time curve corresponds to the precipitate of magnesium hydroxide according to the theoretical calculation.展开更多
In order to provide scientific basis for advanced applications of near eutectic Al-Si-Mg alloys as architectural profiles, a comparative study on the corrosion resistance of an as-extruded near eutectic AI-Si-Mg alloy...In order to provide scientific basis for advanced applications of near eutectic Al-Si-Mg alloys as architectural profiles, a comparative study on the corrosion resistance of an as-extruded near eutectic AI-Si-Mg alloy and AA6063 aluminium alloy was carried out by means of neutral salt spray test. The corroded surfaces of the alloys were examined with optical microscopy and scanning electron microscope （SEM）. Results show that the corrosion type of these two alloys is pitting corrosion. The number of corrosion pits in the AA6063 aluminium alloy is more than that in the near eutectic AI-Si-Mg alloy, but the pits in the latter alloy are much larger and deeper. Because the relatively low polarization resistance of the near eutectic alloy leads to poorer repassivation ability, autocatalytic acidification occurs once a pit forms. Thus, occluded corrosion cells are developed in this alloy.展开更多
文摘The enrichment of chloride anion within the occluded cell （OC） for Type 304 austenitic stainless steel in low chloride concentration solution has been investigated by means of a simulated OC. The influence of the enrichment of chloride anion on stress corrosion crack （SCC） of Type 304 stainless steel has been studied. It was observed that the amount of chloride anion migration was proportional to the charge flowing through the anode. Owning to the effects of enrichment of chloride anion, low chloride concentration solution could induce SCC for Type 304 stainless steel.
文摘An artificial localized corrosion system is assembled and some parameters related to the localized corrosion in active dissolution state (i.e., non-passive state) have been studied. The results showed that the developed electrochemical system can satisfactorily imitate a naturally formed localized corrosion and the coupling current can indicate the maximum localized propagating rate. In this artificial system, the anodic dissolution reaction followed the auto-catalytic mechanism. The localized corrosion current density was dependent on the area ratio R of the cathode to the occluded anode. While R was equal to or more than 6, the coupling current reached at a maximum value and did not alter with the increase in R-value. Therefore, R=7 is chosen as one of these optimum parameters used in constructing the system, with which the biggest galvanic current might be obtained. In contrast, the thickness of the polymer filler separating the occluded anode area from the bulk electrolyte solution and the volume of the occluded anode area did not affect the corrosion current obviously. They might affect the response time to approach a steady state.
基金Projects (200413BA4002, 8655) supported by the Natural Science Foundation of Chongqing Municipal Science Commission, ChinaProject (KJ050604) supported by the Technology Commission and the Science and Technology foundation of Chongqing Municipal Education Commission, China
文摘Corrosion of magnesium alloys is an important issue for their applications in automobile and aerospace industry. pH values as a function of time in two types of simulated occluded corrosion cells(OCC) for magnesium alloys AZ80 and AM60 were measured. The influence of mass ratio of solution to material or liquid to solid ratio(L/S ratio),initial pH value and chemical compositions of solutions on pH value in OCC was discussed. The experimental results show that pH value for magnesium alloys increases gradually or rapidly in Occ,depending on L/S ratio,initial pH value of solution and chloride ions concentration etc,and then reaches up to 10.5-10.6 and finally stabilizes at the level. The onset in the pH value time curve corresponds to the precipitate of magnesium hydroxide according to the theoretical calculation.
基金financially supported by Jiangsu Graduate Student Innovation Program of China(No.CXZZ-0146)the Scientif ic Research Foundation of Graduate School of Southeast University(No.YBJJ1235)
文摘In order to provide scientific basis for advanced applications of near eutectic Al-Si-Mg alloys as architectural profiles, a comparative study on the corrosion resistance of an as-extruded near eutectic AI-Si-Mg alloy and AA6063 aluminium alloy was carried out by means of neutral salt spray test. The corroded surfaces of the alloys were examined with optical microscopy and scanning electron microscope （SEM）. Results show that the corrosion type of these two alloys is pitting corrosion. The number of corrosion pits in the AA6063 aluminium alloy is more than that in the near eutectic AI-Si-Mg alloy, but the pits in the latter alloy are much larger and deeper. Because the relatively low polarization resistance of the near eutectic alloy leads to poorer repassivation ability, autocatalytic acidification occurs once a pit forms. Thus, occluded corrosion cells are developed in this alloy.