The behavior of flow stress of Al sheets used for pressure can prepared by different melt-treatment during plastic deformation at elevated temperature was studied by isothermal compression test using Gleeble1500 dynam...The behavior of flow stress of Al sheets used for pressure can prepared by different melt-treatment during plastic deformation at elevated temperature was studied by isothermal compression test using Gleeble1500 dynamic hot-simulation testing machine. The results show that the AI sheets possess the remarkable characteristic of steady state flow stress when they are deformed in the temperature range of 350-500℃ at strain rates within the range of 0.01-10.0s^-1. A hyperbolic sine relationship is found to correlate well the flow stress with the strain rate, and an Arrhenius relationship with the temperature, which implies that the process of plastic deformation at elevated temperature for this material is thermally activated. Compared with the AI pieces prepared by no or conventional melt-treatment, hot deformation activation energy of AI sheets prepared by high-efficient melt-treatment is the smallest （ Q= 168.0kJ/mol）, which reveals that the hot working formability of this material is very better, and has directly to do with the effective improvement of its metallurgical quality.展开更多
Strain-hardening and warm deformation behaviors of extruded Mg-2Sn-0.5Yb alloy(at.%)sheet were investigated in uniaxial tensile test at temperatures of 25-250 ℃ and strain rates of 1×10^(−3) s^(−1)-0.1 s^(−1).Th...Strain-hardening and warm deformation behaviors of extruded Mg-2Sn-0.5Yb alloy(at.%)sheet were investigated in uniaxial tensile test at temperatures of 25-250 ℃ and strain rates of 1×10^(−3) s^(−1)-0.1 s^(−1).The data fit with the Kocks-Mecking type plots were used to show different stages of strain hardening.Besides III-stage and IV-stage,the absence of the II-stage strain hardening at room temperature should be related to the sufficient dynamic recrystallization during extrusion.The decrease of strain hardening ability of the alloy after yielding was attributed to the reduction of dislocation density with increasing testing temperature.Strain rate sensitivity(SRS)was significantly enhanced with increasing temperature,and the corresponding m-value was calculated as 0.07-0.12,which indicated that the deformation mechanism was dominated by the climb-controlled dislocation creep at 200 ℃.Furthermore,the grain boundary sliding(GBS)was activated at 250 ℃,which contributed to the higher SRS.The activation energy was calculated as 213.67 kJ mol^(−1),which was higher than that of lattice diffusion or grain boundary self-diffusion.In addition,the alloy exhibited a quasi superplasticity at 250 ℃ with a strain rate of 1×10^(−3) s^(−1),which was mainly related to the fine microstructure and the presence of the Mg2Sn and Mg2(Sn,Yb)particles.展开更多
In this paper the alkali-activated slag cementitious materials(AASCM)which strength at 600 ℃ is larger than that of AASCM at room temperature,were prepared to paste CFRP sheets to strengthen four simply supported unb...In this paper the alkali-activated slag cementitious materials(AASCM)which strength at 600 ℃ is larger than that of AASCM at room temperature,were prepared to paste CFRP sheets to strengthen four simply supported unbonded prestressed composite beams encased circular steel tube truss after ultimate limit state.Test on flexural behavior of these four beams was performed.Moreover,normal section load-bearing capacity of these beams and the curve load-deflection at mid-span were obtained.Experimental results show that it is feasible to strengthen concrete members with CFRP sheets bonded with AASCM.Based on the experimental results and theoretical study,computational method of stiffness is proposed for calculating bending rigidity and normal section load-bearing capacity of concrete simply supported beams strengthened with CFRP sheets bonded with AASCM.Formula of bending rigidity calculation was founded which results are in good agreement with testing data.展开更多
基金supported by the Fujian Provincial Natural Science Foundation(No.E0210011)the Educational Commission of Fujian province(No.K20014).
文摘The behavior of flow stress of Al sheets used for pressure can prepared by different melt-treatment during plastic deformation at elevated temperature was studied by isothermal compression test using Gleeble1500 dynamic hot-simulation testing machine. The results show that the AI sheets possess the remarkable characteristic of steady state flow stress when they are deformed in the temperature range of 350-500℃ at strain rates within the range of 0.01-10.0s^-1. A hyperbolic sine relationship is found to correlate well the flow stress with the strain rate, and an Arrhenius relationship with the temperature, which implies that the process of plastic deformation at elevated temperature for this material is thermally activated. Compared with the AI pieces prepared by no or conventional melt-treatment, hot deformation activation energy of AI sheets prepared by high-efficient melt-treatment is the smallest （ Q= 168.0kJ/mol）, which reveals that the hot working formability of this material is very better, and has directly to do with the effective improvement of its metallurgical quality.
基金This work was financially supported by the National Nature Science Foundations of China(No.51371089 and No.51301082).
文摘Strain-hardening and warm deformation behaviors of extruded Mg-2Sn-0.5Yb alloy(at.%)sheet were investigated in uniaxial tensile test at temperatures of 25-250 ℃ and strain rates of 1×10^(−3) s^(−1)-0.1 s^(−1).The data fit with the Kocks-Mecking type plots were used to show different stages of strain hardening.Besides III-stage and IV-stage,the absence of the II-stage strain hardening at room temperature should be related to the sufficient dynamic recrystallization during extrusion.The decrease of strain hardening ability of the alloy after yielding was attributed to the reduction of dislocation density with increasing testing temperature.Strain rate sensitivity(SRS)was significantly enhanced with increasing temperature,and the corresponding m-value was calculated as 0.07-0.12,which indicated that the deformation mechanism was dominated by the climb-controlled dislocation creep at 200 ℃.Furthermore,the grain boundary sliding(GBS)was activated at 250 ℃,which contributed to the higher SRS.The activation energy was calculated as 213.67 kJ mol^(−1),which was higher than that of lattice diffusion or grain boundary self-diffusion.In addition,the alloy exhibited a quasi superplasticity at 250 ℃ with a strain rate of 1×10^(−3) s^(−1),which was mainly related to the fine microstructure and the presence of the Mg2Sn and Mg2(Sn,Yb)particles.
基金Sponsored by the Changjiang Scholars Program of China(Grant No.2009-37)the National Natural Science Foundation of China(Grant No.50678050)
文摘In this paper the alkali-activated slag cementitious materials(AASCM)which strength at 600 ℃ is larger than that of AASCM at room temperature,were prepared to paste CFRP sheets to strengthen four simply supported unbonded prestressed composite beams encased circular steel tube truss after ultimate limit state.Test on flexural behavior of these four beams was performed.Moreover,normal section load-bearing capacity of these beams and the curve load-deflection at mid-span were obtained.Experimental results show that it is feasible to strengthen concrete members with CFRP sheets bonded with AASCM.Based on the experimental results and theoretical study,computational method of stiffness is proposed for calculating bending rigidity and normal section load-bearing capacity of concrete simply supported beams strengthened with CFRP sheets bonded with AASCM.Formula of bending rigidity calculation was founded which results are in good agreement with testing data.