The cutting performance of particulate reinforced me tallic matrix composites(PRMMCs) SiC p/Al in ultrasonic vibration cutting and c ommon cutting with carbide tools and PCD tools was researched in the paper. Mic rost...The cutting performance of particulate reinforced me tallic matrix composites(PRMMCs) SiC p/Al in ultrasonic vibration cutting and c ommon cutting with carbide tools and PCD tools was researched in the paper. Mic rostructure of machined surface was described, the relation between cutting para meters and surface roughness was presented, and characteristic of the surface re mained stress was also presented. Furthermore, wear regularity and abrasion resi stance ability of tools in ultrasonic vibration cutting and common cutting o f PRMMCs were discussed in detail. The test results show: (1) The surface config urations are obviously different when using different tools to machine such PRMM Cs. The surface machined with carbide tools looks luminous and orderly and there are seldom surface defects on it. The reason is that the soft basal body is apt to flow during cutting, therefore a layer of Al matrix film covers machined sur face. On the contrary, the surface machined with PCD tools looks lackluster. But the profile of machined surface is very clear. Superfine grooves, pits and blac k reinforce particulates can be seen easily without obvious Al film. (2) Because of unstable cutting process in common cutting, the surface is easy to produce s ome defects such as burrs, built-up edges and so on so that the quality of surf ace becomes very poor. Vibration cutting can reduce the influence of tearing, pl astic deformation and built-up edge in cutting and can restrain flutter so as t o make cutting process more stable. Therefore, surface roughness of vibration cu tting is better than that of common cutting. (3) There is an optimum value of fe ed rate in vibration cutting of PRMMCs due to the influence of material characte ristics. Whether feed rate is more than or less than this optimum value, surface roughness will increase. (4) According to analyzing the wear rate of tools in v ibration cutting PRMMCs, it can be concluded that abrasion resistance of tools w ill be improved remarkably when vibration cutting composites have a lower pe rcentage of reinforce particulate. If the percentage of reinforce particulate is higher, the influence on abrasion resistance of carbide tool in vibration cut ting will not be obvious. The research result indicates that vibration cutting effect has a close relation with material characteristics.展开更多
In planar linkage mechanisms,when dimensions of the mechanisms and one position of inputlink are given,there are,in general,two or more corresponding positions of output link even withthe dimensions of all links uncha...In planar linkage mechanisms,when dimensions of the mechanisms and one position of inputlink are given,there are,in general,two or more corresponding positions of output link even withthe dimensions of all links unchangable.So,prior to the analysis and synthesis of the mechanisms,we should determine the necessary assembling position.This paper presents a method to solve thisproblem for a sort of planar linkage mechanisms and provides a very simple rule for pivot four-barlinkage mechanism.展开更多
文摘The cutting performance of particulate reinforced me tallic matrix composites(PRMMCs) SiC p/Al in ultrasonic vibration cutting and c ommon cutting with carbide tools and PCD tools was researched in the paper. Mic rostructure of machined surface was described, the relation between cutting para meters and surface roughness was presented, and characteristic of the surface re mained stress was also presented. Furthermore, wear regularity and abrasion resi stance ability of tools in ultrasonic vibration cutting and common cutting o f PRMMCs were discussed in detail. The test results show: (1) The surface config urations are obviously different when using different tools to machine such PRMM Cs. The surface machined with carbide tools looks luminous and orderly and there are seldom surface defects on it. The reason is that the soft basal body is apt to flow during cutting, therefore a layer of Al matrix film covers machined sur face. On the contrary, the surface machined with PCD tools looks lackluster. But the profile of machined surface is very clear. Superfine grooves, pits and blac k reinforce particulates can be seen easily without obvious Al film. (2) Because of unstable cutting process in common cutting, the surface is easy to produce s ome defects such as burrs, built-up edges and so on so that the quality of surf ace becomes very poor. Vibration cutting can reduce the influence of tearing, pl astic deformation and built-up edge in cutting and can restrain flutter so as t o make cutting process more stable. Therefore, surface roughness of vibration cu tting is better than that of common cutting. (3) There is an optimum value of fe ed rate in vibration cutting of PRMMCs due to the influence of material characte ristics. Whether feed rate is more than or less than this optimum value, surface roughness will increase. (4) According to analyzing the wear rate of tools in v ibration cutting PRMMCs, it can be concluded that abrasion resistance of tools w ill be improved remarkably when vibration cutting composites have a lower pe rcentage of reinforce particulate. If the percentage of reinforce particulate is higher, the influence on abrasion resistance of carbide tool in vibration cut ting will not be obvious. The research result indicates that vibration cutting effect has a close relation with material characteristics.
文摘In planar linkage mechanisms,when dimensions of the mechanisms and one position of inputlink are given,there are,in general,two or more corresponding positions of output link even withthe dimensions of all links unchangable.So,prior to the analysis and synthesis of the mechanisms,we should determine the necessary assembling position.This paper presents a method to solve thisproblem for a sort of planar linkage mechanisms and provides a very simple rule for pivot four-barlinkage mechanism.