Pore opening and binder flow during the initial stage of thermal debinding in metal injection molded parts was investigated. Scaning electron microscopy(SEM) pictures of 316 L stainless steel parts using wax based bin...Pore opening and binder flow during the initial stage of thermal debinding in metal injection molded parts was investigated. Scaning electron microscopy(SEM) pictures of 316 L stainless steel parts using wax based binder show that small particles will move to the surface with the process of debinding. SEM pictures of different mass loss rate specimens indicate that initial pores will emerge when as little as 4% binder removes. During the initial stage of thermal debinding, vapor tension varies in different place due to the difference of curvature. Thus more binders will be removed in places with smaller cavity between metal powders, and in these places small openings emerge.展开更多
A new CVD method without vacuum condition（CVDWV）was designed in this study,ithad been found that by modifying the flow rate of the carrier gas（N<sub>2</sub>）and the temperature of sur-face reaction,sil...A new CVD method without vacuum condition（CVDWV）was designed in this study,ithad been found that by modifying the flow rate of the carrier gas（N<sub>2</sub>）and the temperature of sur-face reaction,silicon saturator and sample tube,the amount of silica deposited on the external sur-face of the zeolite could be precisely controlled,The changes in the physicochemical properties ofzeolite,such as pore-opening size,acidity and reaction property were investigated.The results ob-tained showed that:modification of the improved CVD method did not change the internal structureand acidity of the zeolite,but could bring about significant change of pore-opening size and reactionproperty as desired.展开更多
文摘Pore opening and binder flow during the initial stage of thermal debinding in metal injection molded parts was investigated. Scaning electron microscopy(SEM) pictures of 316 L stainless steel parts using wax based binder show that small particles will move to the surface with the process of debinding. SEM pictures of different mass loss rate specimens indicate that initial pores will emerge when as little as 4% binder removes. During the initial stage of thermal debinding, vapor tension varies in different place due to the difference of curvature. Thus more binders will be removed in places with smaller cavity between metal powders, and in these places small openings emerge.
文摘A new CVD method without vacuum condition（CVDWV）was designed in this study,ithad been found that by modifying the flow rate of the carrier gas（N<sub>2</sub>）and the temperature of sur-face reaction,silicon saturator and sample tube,the amount of silica deposited on the external sur-face of the zeolite could be precisely controlled,The changes in the physicochemical properties ofzeolite,such as pore-opening size,acidity and reaction property were investigated.The results ob-tained showed that:modification of the improved CVD method did not change the internal structureand acidity of the zeolite,but could bring about significant change of pore-opening size and reactionproperty as desired.