An Analysis of Contemporary Copper Recycling in China

Copper consumption increased very quickly in China in recent years,which could not be met by inland copper industry.In order to achieve a sustainable development of copper industry,an analysis of copper recycling in China was necessary.For the life cycle of copper products a copper-flow diagram with time factor was worked out and the contemporary copper recycling in China was analyzed,from which the following data were obtained.The average life cycle of copper products was 30 years.From 1998 to 2002,the use ratio of copper scraps in copper production,the use ratio of copper scraps in copper manufacture,the materials self-support ratio in copper production,and the materials self-support ratio in copper manufacture were 26.50%,15.49%,48.05% and 59.41%,respectively.The materials self-support ratios in copper production and manufacture declined year by year in recent years on the whole,and the latter dropped more quickly.The average index of copper ore and copper scrap from 1998 to 2002 were 0.8475 t/t and 0.0736 t/t,respectively;and copper resource efficiency was 1.1855 t/t.Some efforts should be paid to reduce copper ores consumption and promote copper scraps regeneration.Copper scraps were mostly imported from foreign countries because of shortage in recent years in China.Here the reasons related to copper scraps deficiency were also demonstrated.But we can forecast:when copper production was in a slow rise or in a steady state in China,the deficiency of copper scraps may be mitigated;when copper production was in a steady state for a very long time,copper scraps may become relatively abundant.According to the status of copper industry in China,the raw materials of copper production and manufacture have to depend on oversea markets heavily in recent years,and at the same time,the copper scraps using proportion and efficiency in copper industry should be improved.

The study of metal cycles in China

A model of Fe-flow in the life cycle of steel product was put forward and analyzed. Three important resource and environmental indicators for Fe-flow analysis,that is,steel scrap index,iron ore index and iron loss index were derived from this model. Illustrative examples,demonstrating the influence of the variation of steel output on steel scrap index and iron ore index were given. Case studies for estimating the values of steel scrap index of Japan,China and USA in the period of 1988-1997 were carried out. It was clarified that the main reason of severe deficiency in steel scraps for China's steel industry was its continued rapid growth. The study of iron,copper,zinc and lead cycle in China was carried out successfully according to this model.

Delineation of Potential Mineral Resources RegionBased on Geo-anomaly Unit

The geological anomaly unit method (GAUM) is a new way to delineate and evaluate ore finding targets in line with the “geological anomaly ore finding theory”. Comprehensive ore finding information from geological, geochemical and geophysical data is used for quantitative measurement of the “ore forming geological anomaly unit” in this paper. The main procedures are shown as follows: (1) The geo anomalous events associated with gold mineralization are analyzed in Tongshi gold field; (2) The zonation in the concentrated heavy minerals and the stream sediment elements of ore forming geo anomaly are studied in detail; (3) The deep geological structural framework is deduced by means of the synthetic geological interpretation of gravity and magnetic information; (4) The ore controlling geo anomalies and ore anomalies are chosen as the variables of the favorable ore forming indexes that can be used for the quantitative delineation and evaluation of the potential ore forming regions.

Effect of Ca-Fe oxides additives on NOx reduction in iron ore sintering

As the emission control regulations get stricter,the NO;reduction in the sintering process becomes an important environmental concern owing to its role in the formation of photochemical smog and acid rain.The NOxemissions from the sintering machine account for 48% of total amount from the iron and steel industry.Thus,it is essential to reduce NO;emissions from the sintering machine,for the achievement of clean production of sinter.Ca-Fe oxides,serving as the main binding phase in the sinter,are therefore used as additives into the sintering mixture to reduce NOxemissions.The results show that the NO;reduction ratio achieves 27.76% with 8% Ca-Fe oxides additives since the Ca-Fe oxides can advance the ignition and inhibit the nitrogen oxidation compared with the conventional condition.Meanwhile,the existence of Ca-Fe oxides was beneficial to the sinter quality since they were typical low melting point compounds.The optimal mass fraction of Ca-Fe oxides additives should be less than 8%since the permeability of sintering bed was significantly decreased with a further increase of the Ca-Fe oxides fines,inhibiting the mineralization reaction of sintering mixture.Additionally,the appropriate particle size can be obtained when mixing an equal amount of Ca-Fe oxides additives of-0.5 mm and 0.5-3.0 mm in size.

Sintered Ore Sprayed by Acid and Alkaline Waste Water Resulted From Cold Rolling

In order to prevent the powdering of a sintered ore from influencing the smooth operation of a blast furnace,the conventional way to deal with it is that the CaCl2 solution is prepared by tap water,and then the solution is sprayed onto the sintered ore for improving its RDI（low temperature reduction degradation index）.The CaCl2 solution prepared by adding acid and alkaline waste water resulted from cold rolling is sprayed onto the sintered ore to improve its RDI.The values of RDI＋6.3 and RDI＋3.15 of the sintered ore which is sprayed by the CaCl2 solution with the CaCl2 concentration of 3.5%（mass percent） are increased by 17.5% and 11.63%,but the index of RDI-0.5 is decreased by 3.1% when the spraying amount of the solution is making up 0.5% of the total sintered ore sprayed in comparison with those of the sintered ore which is not sprayed by using the CaCl2 solution.Experimental results show that after the CaCl2 solutions prepared by adding the acid and alkaline waste water are sprayed on the sintered ore,RDI of the ore can be remarkably improved and therefore another way for recycling acid and alkaline waste water can be available,by which both cost for treating waste water and cost for producing a sintered ore can be decreased and environment is free of pollution by harmful substances in the waste water.