Styrene-butadiene-styrene （SBS） modified bitumen crack filling material with organophilic montmorillonite （OCFM） was prepared by melt blending. X-ray diffraction analysis shows that the interlayer spacing of organ...Styrene-butadiene-styrene （SBS） modified bitumen crack filling material with organophilic montmorillonite （OCFM） was prepared by melt blending. X-ray diffraction analysis shows that the interlayer spacing of organophilic montmorillonite （OMMT） in OCFM is widened and an exfoliated structure may be formed. Thermal-oxidative aging behavior of OCFM and SBS modified bitumen crack filling material （SCFM） was investigated. The experimental results indicate that the rate of thermal-oxidative aging of OCFM is much slower than that of SCFM, which can be attributed to barrier of exfoliated structure of OCFM to oxygen.展开更多
A kind of novel shape-stabilized phase change material （SSPCM） was prepared by using a melting intercalation technique. This kind of SSPCM was made of lauric acid （LA） as a phase change material and organophilic m...A kind of novel shape-stabilized phase change material （SSPCM） was prepared by using a melting intercalation technique. This kind of SSPCM was made of lauric acid （LA） as a phase change material and organophilic montmorillonite （OMMT） as a support material. And the thermal properties and morphology of the SSPCM were characterized by X-ray diffraction （XRD）, transmission electron microscope （TEM）, scanning electronic microscope （SEM）, scanning calorimeter （DSC）, and differential thermal cravimetry （TG）. The DSC result shows that the phase change temperature of the SSPCM is close to that of LA, and its latent heat is equivalent to that of the calculated value based on the mass ratio of LA measured by TG. The XRD, SEM and TEM results demonstrate that the LA intercalates into the silicate layers of the OMMT, thus forming a typically intercalted hybrid, which can restrict the molecular chain of the LA within the structure of OMMT at high temperature. And consequently SSPCM can keep its solid state during its solid-liquid phase change processing.展开更多
Poly (3-hydroxybutyrate-co-3-hydroxyvalerate)/Organophilic montmorillonite (PHBV/OMMT) nanocomposites were prepared and the biodegradability of the PHBV/OMMT nanocomposites was studied by a cultivation degrading metho...Poly (3-hydroxybutyrate-co-3-hydroxyvalerate)/Organophilic montmorillonite (PHBV/OMMT) nanocomposites were prepared and the biodegradability of the PHBV/OMMT nanocomposites was studied by a cultivation degrading method in soil suspension. The relationship between structure and biodegradability of PHBV/OMMT nanocomposites was investigated. The results showed that the biodegradability of PHBV/OMMT nanocomposites decreased with increasing amount of OMMT and it was related to the number of PHBV degrading microorganisms in degradation environment, the anti-microbial property of OMMT and the degree of crystallinity of the nanocomposites.展开更多
基金Funded by the National Natural Science Foundation of China (50773061)
文摘Styrene-butadiene-styrene （SBS） modified bitumen crack filling material with organophilic montmorillonite （OCFM） was prepared by melt blending. X-ray diffraction analysis shows that the interlayer spacing of organophilic montmorillonite （OMMT） in OCFM is widened and an exfoliated structure may be formed. Thermal-oxidative aging behavior of OCFM and SBS modified bitumen crack filling material （SCFM） was investigated. The experimental results indicate that the rate of thermal-oxidative aging of OCFM is much slower than that of SCFM, which can be attributed to barrier of exfoliated structure of OCFM to oxygen.
文摘A kind of novel shape-stabilized phase change material （SSPCM） was prepared by using a melting intercalation technique. This kind of SSPCM was made of lauric acid （LA） as a phase change material and organophilic montmorillonite （OMMT） as a support material. And the thermal properties and morphology of the SSPCM were characterized by X-ray diffraction （XRD）, transmission electron microscope （TEM）, scanning electronic microscope （SEM）, scanning calorimeter （DSC）, and differential thermal cravimetry （TG）. The DSC result shows that the phase change temperature of the SSPCM is close to that of LA, and its latent heat is equivalent to that of the calculated value based on the mass ratio of LA measured by TG. The XRD, SEM and TEM results demonstrate that the LA intercalates into the silicate layers of the OMMT, thus forming a typically intercalted hybrid, which can restrict the molecular chain of the LA within the structure of OMMT at high temperature. And consequently SSPCM can keep its solid state during its solid-liquid phase change processing.
基金The National Natural Science Foundation of China (No. 20374032) Chinese Education Ministry Foundation for N & T Joint Academy
文摘Poly (3-hydroxybutyrate-co-3-hydroxyvalerate)/Organophilic montmorillonite (PHBV/OMMT) nanocomposites were prepared and the biodegradability of the PHBV/OMMT nanocomposites was studied by a cultivation degrading method in soil suspension. The relationship between structure and biodegradability of PHBV/OMMT nanocomposites was investigated. The results showed that the biodegradability of PHBV/OMMT nanocomposites decreased with increasing amount of OMMT and it was related to the number of PHBV degrading microorganisms in degradation environment, the anti-microbial property of OMMT and the degree of crystallinity of the nanocomposites.