Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were resea...Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.展开更多
Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, ...Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, inductive devices, etc. Most recently, the factors effecting the texture and magnetic properties, e.g. impurities, rolling process and annealing process, have been greatly studied. The benefits of this study are that low core loss silicon steels with stable high-performance can be obtained through an economic production process. This review is intended to summarize the recent developments in the texture, properties, manufacture and application of oriented silicon steel sheets.展开更多
CW-CO2 laser nitriding technique was applied to improve the properties （such as aging property and the core loss） of grain oriented silicon steel. The samples were nitrided with regular space. Laser power density an...CW-CO2 laser nitriding technique was applied to improve the properties （such as aging property and the core loss） of grain oriented silicon steel. The samples were nitrided with regular space. Laser power density and scanning speed were chosen as 7.8×10^5W·cm^-2 and 100mm·min^-1. By some laser irradiation, Fe4N and Fe3N were formed in the nitrided zone. The nitrided samples were annealed at the temperatures ranged from 100 to 90℃. The core loss of some interested samples was tested. The results show that the core loss of the nitrided samples with different thickness of 0.23 and 0.30mm decreased by 14.9% and 9.4% respectively, and the aging property were improved up to 800℃. The mechanism of laser nitriding to improve the properties of grain oriented silicon steel is discussed.展开更多
基金National Natural Science Foundation of China!(No. 59671037).
文摘Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.
文摘Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, inductive devices, etc. Most recently, the factors effecting the texture and magnetic properties, e.g. impurities, rolling process and annealing process, have been greatly studied. The benefits of this study are that low core loss silicon steels with stable high-performance can be obtained through an economic production process. This review is intended to summarize the recent developments in the texture, properties, manufacture and application of oriented silicon steel sheets.
基金supported by the National Natural Science Foundation of China(No.50174020).
文摘CW-CO2 laser nitriding technique was applied to improve the properties （such as aging property and the core loss） of grain oriented silicon steel. The samples were nitrided with regular space. Laser power density and scanning speed were chosen as 7.8×10^5W·cm^-2 and 100mm·min^-1. By some laser irradiation, Fe4N and Fe3N were formed in the nitrided zone. The nitrided samples were annealed at the temperatures ranged from 100 to 90℃. The core loss of some interested samples was tested. The results show that the core loss of the nitrided samples with different thickness of 0.23 and 0.30mm decreased by 14.9% and 9.4% respectively, and the aging property were improved up to 800℃. The mechanism of laser nitriding to improve the properties of grain oriented silicon steel is discussed.