SULFATE RESISTANCE MECHANISM OF HIGH- PERFORMANCE CONCRETE CONTAINING NCI

It is found that the incorporation of Nitrite Corrosion Inhibitor (NCI) greatly weakens the resistance of mixtures to sulfate attack. To study the mechanism of this phenomenon, in this paper, the influence of NCI addition on the cement paste and microstructure change of high performance concrete specimens is studied by means of quantitative XRD, SEM tests. The results demonstrate that the incorporation of NCI accelerates the formation of calcium hydroxide and ettringite crystals, and weakens the pore refinement effect caused by the secondary hydration reaction of fly ash and microsilica. At the age up to one year, the relative crystal quantity in mixture containing NCI is always higher than that in control mixture. The reasons for the degradation in sulfate resistance of mixtures may be attributed to the increase and stability of the calcium hydroxide and ettringite crystals formed and the weakening of secondary hydration reaction. Based on the results, conclusion can be drawn that NCI should be used cautiously in practical engineering where high resistance to sulfate attack is required. (Author abstract) 7 Refs.

高性能地聚物基珊瑚砂浆的配合比设计与性能研究

采用单一质心设计法研究了矿渣-偏高岭土-激发剂三元体系对地聚物流变性能和力学性能的影响,确定了最佳三元复配比例。在此基础上制备了高性能地聚物基珊瑚砂浆(HPGM),研究了其在MgSO_(4)与NaCl复合盐溶液侵蚀作用下的耐久性能及劣化机理,并与水泥基珊瑚砂浆(PC)进行了对比。结果表明:当矿渣、偏高岭土、激发剂的掺量分别为29、23、48 kg时,地聚物具有优异的流变性能(塑性黏度5.47 Pa·s、屈服应力547.21 Pa)和力学性能(7 d抗压强度76.3 MPa、28 d抗压强度93.2 MPa);在90 d侵蚀周期中,PC出现了明显的石膏型侵蚀破坏现象,抗压强度损失达31.6%,孔隙率增大了43.7%;HPGM内部致密的凝胶结构有效抑制了膨胀性石膏和其他劣化产物的形成,同时水化产物中的C-(A)-S-H凝胶和类水滑石相吸附了部分游离Cl-,使得HPGM在90 d侵蚀周期中未出现明显的侵蚀破坏现象,其抗压强度损失为12.0%,孔隙率增大了16.2%。

基于正交优化设计法制备高模量改性沥青

通过单因素试验设计,选取三个水平,基于高模量剂掺量、SBS改性剂含量、剪切时间及剪切速率四个因素进行正交试验设计,制备性能优异稳定的高模量改性沥青,采用目视分析法、极差分析法、灰色关联综合评分法及灰色关联极差法,研究各因素对高模量改性沥青试样弹性恢复率、离析稳定性及三大指标影响规律,确定满足高模量改性沥青性能要求的最佳剪切工艺参数和合理的高模剂用量范围。

复掺再生砂和超细粉煤灰对超高性能混凝土抗硫酸盐侵蚀性能的影响

为了研究再生砂超高性能混凝土(UHPC)的抗硫酸盐侵蚀性能,对掺再生砂和超细粉煤灰的超高性能混凝土进行了硫酸盐干湿循环侵蚀试验,测试了硫酸盐溶液侵蚀前后试件的抗压强度、相对动弹性模量、质量变化。通过离子滴定测定了不同侵蚀深度下硫酸根离子的分布,分析了再生砂和超细粉煤灰对硫酸根离子传输的影响。结果表明:经过90次硫酸盐干湿循环后,UHPC的耐侵蚀系数随着超细粉煤灰掺量的增加呈先增大后减小的趋势;超细粉煤灰掺量为20%(质量分数,下同)时,侵蚀全过程中UHPC的耐侵蚀系数、相对动弹性模量最大,硫酸根离子含量较低;再生砂掺量为50%时,UHPC在干湿循环45次之前的相对动弹性模量最大,相同深度下的硫酸根离子含量最低;复掺20%超细粉煤灰和50%再生砂的UHPC抗硫酸盐侵蚀性能最优。

硫酸盐防腐型聚羧酸高性能减水剂对混凝土性能的影响

为提升混凝土的强度,保证工程质量,分析硫酸盐防腐型聚羧酸高性能减水剂对混凝土性能的影响。以G4216线屏山新市至金阳段高速公路工程为例,采用P·O 42.5级水泥作为主材料,配合粉煤灰、中细砂、碎石以及硫酸盐等制备5种硫酸盐防腐型聚羧酸高性能减水剂掺量水泥浆以及混凝土样本,并对水泥浆流动性能、混凝土力学性能、混凝土抗硫酸盐性能分别实行试验。结果显示:硫酸盐防腐型聚羧酸高性能减水剂掺量越大,效果越佳,能够辅助水泥浆的塑化以及水泥基材的保塑;但是,当掺量达到2.0%时,水泥浆的保塑效果将受到影响,并且会造成混凝土抗碳化性能的下降;样本Y3的质量损失率和抗压强度腐蚀系数最低,分别为0.3%和0.2%左右;Y3样本在试验工程中的各项应用情况均满足标准结果,其对标判定结果均合格,满足工程需求。

基于正交试验设计的大黄甘草洗液提取工艺研究

目的对大黄甘草洗液的提取工艺进行优化,为中试放大生产提供质量控制依据。方法利用高效液相色谱法测定蒙花苷的含量,采用正交试验考察加水倍量、浸泡时间、提取时间及提取次数等因素对提取效果的影响。结果大黄甘草洗液的最佳提取工艺为药材加14倍量水浸泡1小时,提取2次,每次2小时。结论提取工艺优化后稳定可靠,可为该药的量产提供保证。

桩古40-多4高温井深部酸化技术研究及应用

为了进一步沟通天然裂缝,获得较好的酸化施工效果,实现胜利桩西油田桩古40-多4高温井的增产目的,对现场选用的酸液体系进行了高温缓蚀性能评价、缓速性能评价以及综合性能评价实验,根据实验评价结果和以往该区块的酸化施工参数,确定了该井本次施工酸液体系配方。结果显示:在170℃下,7.0%缓蚀剂FL-B的动态腐蚀速率为37.82 g/(m^(2)·h),远低于行业要求的小于70.00 g/(m^(2)·h),静态腐蚀速率为7.64 g/(m^(2)·h),低于10.00 g/(m^(2)·h)的行业标准;反应8 min时15%HCl+8%DJ-9的酸岩反应速度为0.1017 mol/(cm^(2)·s),15%HCl+7.0%RVA-2缓速剂的酸岩反应速度为0.0788 mol/(cm^(2)·s),15%HCl+8.0%RVA-2缓速剂的酸岩反应速度为0.0756 mol/(cm^(2)·s),加入7.0%和8.0%RVA-2缓速剂后酸岩反应速度要低于胶凝酸的酸岩反应速度;20%HCl+3%HAC+7.0%FL-B+1%NH4Cl酸液体系各项性能指标均达到行业标准。此外,对桩古40-多4井施工管柱进行了摩阻计算,结合施工安全性优化管柱设计后进行了酸化施工。该井酸化前累计生产原油19750 t,酸化后日产油最高可达170 t,后期稳产在70~80 t/d,一年时间累计增油25500 t,是酸化前累计生产原油的1.3倍,实现了增产目的。

基于正交试验的高黏沥青材料组成设计与性能研究

为制备一种适用于超薄罩面层的高黏沥青,基于正交试验进行了高黏沥青材料组成设计及路用性能评价,结果表明:在试验范围内,影响高黏沥青25℃针入度、5℃延度及60℃动力黏度的最显著因素为增黏剂掺量,影响软化点的最主要因素为基质沥青标号,SBS掺量对高黏沥青的路用性能指标影响最小。综合考虑高黏沥青各指标变化规律与要求范围,推荐高黏沥青的两种材料组成方案:90号基质沥青+8%增黏剂+2%SBS;70号基质沥青+10%增黏剂+2%SBS。

注射用红花黄色素与6种输液配伍的稳定性

目的考察注射用红花黄色素与6种输液配伍后的稳定性。方法采用L8(27)正交设计优选的红花黄色素溶解液分别与5%和10%葡萄糖注射液、0.9%氯化钠注射液、葡萄糖氯化钠注射液、乳酸钠林格注射液及复方氯化钠注射液稀释为成品输液,观察室温(22℃)条件下8 h内各成品输液理化性质的变化并计算HPLC指纹图谱的相似度。结果注射用红花黄色素配伍6种成品输液的性状和pH在0～8 h内没有显著变化。在6 h内不溶微粒数符合规定,只有0.9%复方氯化钠注射液,配伍8 h后,复方氯化钠稀释的成品输液中羟基红花黄色素A含量下降超出10%,其他5种成品输液中羟基红花黄色素A含量稳定。HPLC指纹图谱相似度均无显著变化。结论建议采用0.9%氯化钠等注射用红花黄色素调配为成品输液,并于室温下6 h内使用。

骨架密实型沥青混合料中高温性能与级配关系

针对骨架密实型沥青混合料设计方法中的不足,对目前的骨架结构检验方程进行了合理的改进,通过沥青路面分析仪试验研究揭示了级配中各档集料对其高温性能的影响规律,0.22d(d为集料的最大粒径)粒径撑开料的作用对沥青混合料高温性能最为关键,提出了各关键筛孔集料筛上剩余质量百分率的合理值,为骨架密实型沥青混合料设计提供了有价值的参考.

微波辅助萃取人参总皂苷与单体皂苷含量分析

通过单因素试验和正交试验对微波辅助萃取人参皂苷的工艺条件进行优化,采用分光光度法和高效液相色谱法对萃取物中的人参总皂苷及8种单体皂苷进行测定,考察不同提取条件下所得人参皂苷产率和组成的差异。结果表明:1)以总皂苷为提取目标时,最佳提取条件为萃取功率600 W、萃取温度45℃、萃取时间5 min、料液比1∶20,萃取3次;2)以8种单体皂苷为提取目标时,最佳提取条件为萃取功率300 W、萃取温度35℃、萃取时间15 min、料液比1∶25,萃取3次(提取率为0.98%);3)在最佳提取条件下,以体积分数80%甲醇为提取溶剂时,总皂苷提取率为6.02%,而单体皂苷提取率之和为0.43%;以水饱和正丁醇为提取溶剂时8种单体皂苷提取率达到0.71%。综上所述,人参质量评价和工艺优化结果与提取方法、提取条件、评价指标密切相关。

高性能混凝土配合比设计的正交试验研究

高性能混凝土配合比设计的研究对实际工程应用有着重要的意义 ,是高性能混凝土研究领域的主要方面之一。采用四因素、三水平的正交试验设计方法对高性能混凝土的配合比进行了试验 ,研究了水泥、硅灰、粉煤灰和外加剂等不同试验因素对高性能混凝土强度的影响 ,分析了每个因素水平对高性能混凝土配合比的作用及各个水平之间的差异。结果表明 ,对混凝土强度的影响因素依次为外加剂、硅灰、水灰比和粉煤灰。并用正交试验结果进行了线性回归 。

古糖酯脂质体的制备及其包封率测定方法的研究

目的研究古糖酯脂质体的制备方法，并建立其包封率的测定方法、方法采用反相蒸发法制备古糖酯脂质体，运用正交实验确定最适的制备条件；采用高效凝胶渗透色谱法（HPGPC）测定古糖酯脂质体的包封率、结果采用反相蒸发法制备古糖酯脂质体的最适条件是：磷脂与胆固醇的摩尔比为4：1，古糖酯药物的加入量为1％，脂水相体积比为3：1，在此条件下制备的脂质体包封率可达39．13％。经负染色法观察古糖酯脂质体的形态为圆形或椭圆形，平均粒径为200nm。采用HPG-PC法可有效地分离古糖酯脂质体与游离药物，方法测定的线性范围为0．2～10．0g·L^-1，平均回收率为95．12％，RSD为1．83％（n=5）。结论反相蒸发法制备的古糖酯脂质体包封率高，粒径小，形态稳定。HPGPC方法简便、快捷，重现性好，适合于古糖酯脂质体包封率的测定。

正交试验法优化催情助孕液制备工艺

为了优化催情助孕液的水提醇沉工艺,采用正交试验法设计,用高效液相色谱法测定制剂中淫羊藿苷含量并以其为评价指标,考察了加水量、煎煮时间、煎煮次数、醇沉浓度、醇沉次数对制剂工艺的影响。结果表明:最佳制剂工艺为加10倍量水,煎煮3次,每次1h,乙醇醇沉浓度为75%,醇沉1次。用该工艺制备的催情助孕液淫羊藿苷含量为0.98892mg/mL,说明该优选工艺稳定可行。

“双掺”磨细矿渣粉和粉煤灰对混凝土抗硫酸盐侵蚀性能的影响研究

鉴于西部地区盐浸侵蚀严重的情况,采用干湿循环试验方法,通过测量分析混凝土试块质量和抗压强度变化,并根据试验数据探讨分析各因素对混凝土抗硫酸盐侵蚀性能影响程度,研究双掺磨细矿渣粉和粉煤灰对混凝土抗硫酸盐侵蚀性能的影响。

高性能化海砂混凝土配合比设计的正交试验研究

采用五因素、四水平的正交试验设计方法对高性能化海砂混凝土的配合比进行了试验,研究了水胶比、细骨料种类、掺合料掺量及种类和养护时间等不同试验因素对高性能化海砂混凝土强度的影响,分析了每个因素水平对高性能化海砂混凝土配合比的作用及各个水平之间的差异。结果表明,对混凝土强度的影响因素依次为水胶比、养护时间、细骨料的种类、掺合料掺量和种类。

大黄酚包合物的制备及其体外释药的研究

目的筛选制备大黄酚包合物的最佳工艺。方法采用正交试验设计以包封率和载药量为指标筛选最佳工艺条件,采用HPLC法测定其含量。结果大黄酚与β-环糊精的比例为1∶4,包合温度为40℃,包合时间为30 min,搅拌速度为200 r.min-1时包封率最高。结论大黄酚包合物制备工艺简单、方便,体外释放速度快。

应用毛细管电泳法分离测定6种取代苯化合物

采用毛细管电泳法对六种取代苯化合物进行了分离研究 ,考察了 3种电泳模式对分离的影响。环糊精的胶束毛细管电泳法可使各组分达到基线分离 ,正交设计法得到了最佳实验条件 ,在质量浓度为 30～ 30 0mg L的范围内 ,可进行定量分析 ,该方法已应用于废液中苯类化合物的测定。

利用当地材料配制高性能混凝土的试验研究

充分利用邯郸当地材料 ,采用正交设计方法配制高性能混凝土 ,分别考察各因素对混凝土工作性及各龄期抗压强度的影响 ,并与基准混凝土对比。试验研究证明 :利用邯郸当地原材料 ,配制高性能混凝土是完全可以实现的 ,并将获得良好的经济效益和社会效益。

废次烟叶中茄尼醇皂化工艺研究

目的:确定茄尼醇皂化的最佳工艺条件。方法:采用正交设计法,以反相高效液相色谱法测定各样品中茄尼醇含量,确立最优皂化条件。结果:最佳皂化工艺为物料比即茄尼醇和乙醇质量体积比为1:25,皂化温度45℃,茄尼醇和催化剂质量比为1:2,反应时间3 h。结论:本皂化方法成本低,条件温和、易控,值得推广。