Al_(x)/HKUST-1(x=1/24,1/12,1/6,1/3),one of the bimetallic copper-based organic framework materials,was successfully prepared by the synthetic exchange method and characterized by X-ray diffraction(XRD),scanning electr...Al_(x)/HKUST-1(x=1/24,1/12,1/6,1/3),one of the bimetallic copper-based organic framework materials,was successfully prepared by the synthetic exchange method and characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),specific surface area(BET),thermogravimetric analysis(TG),infrared spectra(IR),X-ray photoelectron spectroscopy(XPS),and H_(2)-temperature programmed reduction(H_(2)-TPR).The findings indicated that Al_(x)/HKUST-1 maintained the octahedral morphology of its precursor(HKUST-1).The thermal stability and catalytic reduction ability of HKUST-1 skeleton were improved by doping aluminum(Al^(3+)).Al_(1/12)/HKUST-1 showed the best performance among all samples,with a nitric oxide(NO)conversion rate of 100%at 210℃(50℃lower than that of HKUST-1).The valence kind of Al,Cu,and O in Al_(1/12)/HKUST-1 did not change after the catalytic reaction,but the contents of Al,Cu,and O in different forms changed significantly.The catalytic process of the Al_(x)/HKUST-1 followed a Langmuir-Hinshelwood mechanism.展开更多
Monolith SCR catalysts coated with V2Os- WO3/TiO2 were prepared by varying binder and coating thickness. Comparing with a monolith extruded with 100% V2O5-WO3/TiO2 powder, a coated monolith with a catalyst-coating lay...Monolith SCR catalysts coated with V2Os- WO3/TiO2 were prepared by varying binder and coating thickness. Comparing with a monolith extruded with 100% V2O5-WO3/TiO2 powder, a coated monolith with a catalyst-coating layer of 260 μm in thickness exhibited the similar initial NOx reduction activity at 250℃. After 4 h abrasion （attrition） in an air stream containing 300 g. m^-3 fine sands （50-100μm） at a superficial gas velocity of 10m·s^-1, the catalyst still has the activity as a 100% molded monolith does in a 24-h activity test and it retains about 92% of its initial activity at 250℃. Estimation of the equivalent durable hours at a fly ash concentration of 1.0 g.m^-3 in flue gas and a gas velocity of 5 m.s^-1 demonstrated that this coated monolith catalyst is capable of resisting abrasion for 13 months without losing more than 8% of its initial activity. The result suggests the great potential of the coated monolith for application to de-NOx of flue gases with low fly ash concentrations from, such as glass and ceramics manufacturing processes.展开更多
基金financial supports from the Natural Science Foundation of Hunan Province,China(No.2020JJ4685)the Open Fund for Key Laboratory of Metallurgical Emission Reduction and Resources Utilization of Ministry of Education in Anhui University of Technology,China(No.JKF20-02)+2 种基金the Natural Science Foundation of Hunan Province,China(No.2019JJ40378)the Open Fund for State Environmental Protection Key Laboratory of Mineral Metallurgical Resources Utilization and Pollution Control in Wuhan University of Science and Technology,China(No.HB201908)the Scientific Technology Project of Strategic Emerging Industries and Major Achievement Transformation of Hunan Province,China(No.2017GK4010)。
文摘Al_(x)/HKUST-1(x=1/24,1/12,1/6,1/3),one of the bimetallic copper-based organic framework materials,was successfully prepared by the synthetic exchange method and characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),specific surface area(BET),thermogravimetric analysis(TG),infrared spectra(IR),X-ray photoelectron spectroscopy(XPS),and H_(2)-temperature programmed reduction(H_(2)-TPR).The findings indicated that Al_(x)/HKUST-1 maintained the octahedral morphology of its precursor(HKUST-1).The thermal stability and catalytic reduction ability of HKUST-1 skeleton were improved by doping aluminum(Al^(3+)).Al_(1/12)/HKUST-1 showed the best performance among all samples,with a nitric oxide(NO)conversion rate of 100%at 210℃(50℃lower than that of HKUST-1).The valence kind of Al,Cu,and O in Al_(1/12)/HKUST-1 did not change after the catalytic reaction,but the contents of Al,Cu,and O in different forms changed significantly.The catalytic process of the Al_(x)/HKUST-1 followed a Langmuir-Hinshelwood mechanism.
文摘Monolith SCR catalysts coated with V2Os- WO3/TiO2 were prepared by varying binder and coating thickness. Comparing with a monolith extruded with 100% V2O5-WO3/TiO2 powder, a coated monolith with a catalyst-coating layer of 260 μm in thickness exhibited the similar initial NOx reduction activity at 250℃. After 4 h abrasion （attrition） in an air stream containing 300 g. m^-3 fine sands （50-100μm） at a superficial gas velocity of 10m·s^-1, the catalyst still has the activity as a 100% molded monolith does in a 24-h activity test and it retains about 92% of its initial activity at 250℃. Estimation of the equivalent durable hours at a fly ash concentration of 1.0 g.m^-3 in flue gas and a gas velocity of 5 m.s^-1 demonstrated that this coated monolith catalyst is capable of resisting abrasion for 13 months without losing more than 8% of its initial activity. The result suggests the great potential of the coated monolith for application to de-NOx of flue gases with low fly ash concentrations from, such as glass and ceramics manufacturing processes.
