Phosphate-coating was prepared for C/C composite using liquid-impregnation and different heat-treatment. The results show that the mass-loss rate of sample A with 1-2 ℃/min slow-cooling rate technology is 47%after ox...Phosphate-coating was prepared for C/C composite using liquid-impregnation and different heat-treatment. The results show that the mass-loss rate of sample A with 1-2 ℃/min slow-cooling rate technology is 47%after oxidation at 700 ℃ for 20 h, while that of sample B with air-fast-cooling one is only 0.98%. SEM images reveal that the coating of sample A is full of micro-holes, micro-cracks and many piece-like crystal particles, while that of sample B is integrated and compacted in glassy state with a few of micro-cracks. The coating of sample A is almost exhausted only in 8 h oxidized-test at 700 ℃, while that of sample B remains integrated after 8 h test at 700 ℃ and becomes loose due to much small pores generated after 20 h test at 700 ℃.展开更多
To further improve the oxidation-resistance of materials and reduce the cost of grid plates in grate-kiln, a new kind of heat-resistant grid plate was developed. The microstructure of this grid plate with a life more ...To further improve the oxidation-resistance of materials and reduce the cost of grid plates in grate-kiln, a new kind of heat-resistant grid plate was developed. The microstructure of this grid plate with a life more than 18 months was studied by XRD, SEM and EDS techniques. The results show that high hardness, high intensity and good impact property make the new kind of heat-resistant grid plate and its oxide film have a higher resistance to deformation and abrasion at 900-1000℃ Besides, small grain size is beneficial to form a complete protective oxide film. The oxide film composed of SiO2 layer, Cr2O3 layer and Fe2O3 layer is rather thin and bonds closely with the backing. The forming of the chemical stable nickel-rich layer increases the density of Cr2O3 layer.展开更多
The equipments and pipes serving at high temperature and pressure and the presence of hydrogen in the petrochemical industry are usually made of Cr-Mo steels.Cr9Mo pipes replacing Cr5Mo are widely used in many parts o...The equipments and pipes serving at high temperature and pressure and the presence of hydrogen in the petrochemical industry are usually made of Cr-Mo steels.Cr9Mo pipes replacing Cr5Mo are widely used in many parts of/with high-sulfur crude oil refining equipment to meet the more demanding high temperature anticorrosion and oxidation resistance requirements.The mechanical property,creep rupture property and high temperature oxidation-resistant property of domestic Cr9Mo steel are at the same level as the similar foreign products.Three years applications indicate that domestic Cr9Mo steel can fully meet the service requirements of petrochemical industries.Finally,this paper presents the material selection guidelines for the key oil refining devices processing of low sulfur/high acid crude oil.展开更多
基金Projects(09JJ4027)supported by the Natural Science Foundation of Hunan Province,ChinaProject(201206375003)supported by China Scholarship Council
文摘Phosphate-coating was prepared for C/C composite using liquid-impregnation and different heat-treatment. The results show that the mass-loss rate of sample A with 1-2 ℃/min slow-cooling rate technology is 47%after oxidation at 700 ℃ for 20 h, while that of sample B with air-fast-cooling one is only 0.98%. SEM images reveal that the coating of sample A is full of micro-holes, micro-cracks and many piece-like crystal particles, while that of sample B is integrated and compacted in glassy state with a few of micro-cracks. The coating of sample A is almost exhausted only in 8 h oxidized-test at 700 ℃, while that of sample B remains integrated after 8 h test at 700 ℃ and becomes loose due to much small pores generated after 20 h test at 700 ℃.
文摘To further improve the oxidation-resistance of materials and reduce the cost of grid plates in grate-kiln, a new kind of heat-resistant grid plate was developed. The microstructure of this grid plate with a life more than 18 months was studied by XRD, SEM and EDS techniques. The results show that high hardness, high intensity and good impact property make the new kind of heat-resistant grid plate and its oxide film have a higher resistance to deformation and abrasion at 900-1000℃ Besides, small grain size is beneficial to form a complete protective oxide film. The oxide film composed of SiO2 layer, Cr2O3 layer and Fe2O3 layer is rather thin and bonds closely with the backing. The forming of the chemical stable nickel-rich layer increases the density of Cr2O3 layer.
文摘The equipments and pipes serving at high temperature and pressure and the presence of hydrogen in the petrochemical industry are usually made of Cr-Mo steels.Cr9Mo pipes replacing Cr5Mo are widely used in many parts of/with high-sulfur crude oil refining equipment to meet the more demanding high temperature anticorrosion and oxidation resistance requirements.The mechanical property,creep rupture property and high temperature oxidation-resistant property of domestic Cr9Mo steel are at the same level as the similar foreign products.Three years applications indicate that domestic Cr9Mo steel can fully meet the service requirements of petrochemical industries.Finally,this paper presents the material selection guidelines for the key oil refining devices processing of low sulfur/high acid crude oil.