Synthesis of KNiF_3 with Lower Oxygen Content by Refluxing Method

The complex fluoride, KNiF3, with perovskite structure was synthesized by refluxing KF and Ni（NO3）2·6H20 in ethanediol. The samples were characterized by X-ray diffraction（XRD）, transmission electron microscopy（TEM）, X-ray photoelectron spectroscopy（XPS）, and ultraviolet-visible diffuse reflectance speetroseopy（UV-Vis DRS）. The results indicate that the mean diameter of KNiF3 particles is about 30-60 nm and the oxygen content in the samples is ≤5%. The prepared KNiF3 shows obvious absorption peaks at 400-830 nm.

Electrochemical investigation of the anode processes in LiF-NdF3 melt with low oxygen content

The oxidation of oxygen ions and the generation of an anode effect at a low oxygen content of 150 mg/kg were discussed in this paper.Cyclic voltammetry and square-wave voltammetry tests were conducted to explore the anodic processes of LiF-NdF_(3)melt after a lengthy period of pre-electrolysis purification at 1000℃(during which the oxygen content reduced from 413 to 150 mg/kg).The oxidation process of oxygen ions was found to have two stages:oxidation product adsorption and CO/CO_(2)gas evolution.The adsorption stage was controlled by diffusion,whereas the gas evolution was controlled by the electrochemical reaction.In comparison with oxygen content of 413 mg/kg,the decrease in the amplitude of the current at low oxygen content of 150 mg/kg was much gentler during the forward scanning process when the anode effect occurred.Fluorine-ion oxidation peaks that occurred at about 4.2 V vs.Li/Li+could be clearly observed in the reverse scanning processes,in which fluorine ions were oxidized and perfluorocarbons were produced,which resulted in an anode effect.

Study on Oxygen Content, Inclusions and Fatigue Properties of Bearing Steels Produced by Different Processes

The metallurgical properties and fatigue life of bearing steel processed by electric furnace (EAF), ladle refining (LF-VD), continous casting (CC) and electroslag remelting (ESR) have been investigated. The main results obtained are as follows: (1) Due to low oxygen content and dispersion inclusions in steel, the fatigue Life of LF-VD-IC or CC is three times as high as that of EAF steel; (2) The oxygen content in steel produced by CC process is about 9.0x10(-6), the carbon segregation (C/C(0)) is from 0.92 to 1.10 and the fatigue life of CC steel is equal to that of ladle refining ingot casting steel; (3) Although the amount of inclusion and oxygen in ESR steel is higher than that of LF-VD-IC or CC steel, the fatigue life of ESR steel is higher than that of the latter because of its fine and well dispersed inclusions.

Investigation on dependence of BiFeO_3 dielectric property on oxygen content

The influence of oxygen content on the dielectric property of BiFeO3 ceramics is studied by experiment and firstprinciples calculation. The experimental result demonstrates that the dielectric constant of BiFeO3 is strongly dependent on introduced oxygen and oxygen vacancies. By comparison with BiFeO3, the introduced oxygen and oxygen vacancies can lead to a reduction in dielectric constant of BiFeO5 at a lower frequency. The first-principles calculation also shows a similar result when photon energy is in a range of 2.0-4.1 eV. A likely explanation is that this oxygen content dependence may be ascribed to the distortion of Fe-O octahedron structure due to oxygen vacancies or excess oxygen ions in the crystal structure of BiFeO3.

Effect of oxygen content on dielectric characteristics of Cr-doped LaTiO_x

The ceramics La0.85Cr0.15TiOx and La0.7Cr0.3TiOx are prepared by conventional solid-state reaction method. The dielectric properties of Cr-doped La TiOx as a function of frequency（0.1 k Hz ≤ f ≤ 1 MHz） and temperature（77 K ≤ T ≤360 K） are studied. The blocks are then annealed in a flowing O2 or Ar/H2 to convert their oxygen content and the tests mentioned above are performed. The highly oxygenated samples exhibit extremely high low-frequency dielectric constants at room temperature（～10^6）. The results show that the oxygen stoichiometry could significantly influence the dielectric properties of Cr-doped LaTiOx.

Effects of oxygen content on the oxidation process of Si-containing steel during anisothermal heating

The oxidizing behavior of Si-containing steel was investigated in an O2 and N2 binary-component gas with oxygen contents ranging between 0.5 vol% and 4.0 vol% under anisothermal-oxidation conditions. A simultaneous thermal analyzer was employed to simulate the heating process of Si-containing steel in industrial reheating furnaces. The oxidation gas mixtures were introduced from the commencement of heating. The results show that the oxidizing rate remains constant in the isothermal holding process at high temperatures; therefore, the mass change versus time presents a linear law. A linear relation also exists between the oxidizing rate and the oxygen content. Using the linear regression equation, the oxidation rate at different oxygen contents can be predicted. In addition, the relationship between the total mass gain and the oxygen content is linear; thus, the total mass gain at oxygen contents between 0.5 vol%–4.0 vol% can be determined. These results enrich the theoretical studies of the oxidation process in Si-containing steels.

Influence of dissolved oxygen content on oxidative stability of linked polymer solution

The influence of dissolved oxygen content on the oxidative stability of a linked polymer solution (LPS) was studied by micro-filtration, dynamic light scattering and viscosity measurements. The results showed that at the same temperature, the degree of the oxidative degradation of the LPS increased and the rapidity of the oxidative degradation was accelerated with the increase of the dissolved oxygen content. Consequently, the size of linked polymer coils (LPCs) of the LPS became small, and the plugging capability of the LPS decreased. At a fixed content of dissolved oxygen, with increasing degradation temperature, almost the same results were observed, namely, an increased degree of oxidative degradation, accelerated rapidity of the oxidative degradation and decreased plugging capacity, with decreased oxidative stability of LPS. At 90 °C, in the presence of oxygen, LPS lost its plugging capability after having been degraded for a period of time. But at 40 °C, LPS with low dissolved oxygen content could be stable for a long time. The decreased plugging ability of LPS after oxidative degradation is mainly caused by the decreased size and number of the LPCs due to the breaking of hydrolyzed polyacrylamide (HPAM) molecule segments and the structural changing of HPAM molecules.

Effect of oxygen content on tensile strength of polymer-derived SiC fibers

Air-curing is usually applied to the polymer-derived SiC fibers and, as a result, oxygen is embedded to the material. An effective relationship between oxygen content of the SiC fibers and mass gain of their precursor fibers was established. Results also showed that oxygen content has a great influence on the mechanical properties and excellent tensile strength is usually obtained at the oxygen content of 12%～13%, similar to the density of SiC fibers. Oxygen content has a positive effect on the ceramic yield, and thus, is good to the density and tensile strength; while, oxygen content is also negative to volume content of SiC phase and crystallization of the SiC fibers, and thus, detrimental to the density and tensile strength. Both of the two effects result in the peak behavior of the tensile strength of SiC fibers.

Role of doping and oxygen content in superconductivity of La_2 CuO_(4+δ)

ＲｏｌｅｏｆｄｏｐｉｎｇａｎｄｏｘｙｇｅｎｃｏｎｔｅｎｔｉｎｓｕｐｅｒｃｏｎｄｕｃｔｉｖｉｔｙｏｆＬａ_２ＣｕＯ_（４＋δ）￥ＬｉＭｉｎｇ；ＨｕａｎｇＹｕｍｉｎｇ（ＳｃｈｏｏｌｏｆＣｈｅｍｉｓｔｒｙａｎｄＣｈｅｍｉｃａｌＥｎｇｉｎｅｅｒｉｎｇ，Ｓｏｕｔ...

Model Prediction and Optimal Control of Gas Oxygen Content for A Municipal Solid Waste Incineration Process

In the municipal solid waste incineration process,it is difficult to effectively control the gas oxygen content by setting the air flow according to artificial experience.To address this problem,this paper proposes an optimization control method of gas oxygen content based on model predictive control.First,a stochastic configuration network is utilized to establish a prediction model of gas oxygen content.Second,an improved differential evolution algorithm that is based on parameter adaptive and t-distribution strategy is employed to address the set value of air flow.Finally,model predictive control is combined with the event triggering strategy to reduce the amount of computation and the controller's frequent actions.The experimental results show that the optimization control method proposed in this paper obtains a smaller degree of fluctuation in the air flow set value,which can ensure the tracking control performance of the gas oxygen content while reducing the amount of calculation.

Adsorption of lead on multi-walled carbon nanotubes with different outer diameters and oxygen contents: Kinetics, isotherms and thermodynamics

The effects of different outer diameters and surface oxygen contents on the adsorption of heavy metals onto six types of multi-walled carbon nanotubes （MWCNTs） were investigated in an aqueous solution and lead was chosen as a model metal ion. The results indicated that the percentage removal and adsorption capacity of lead remarkably increased with decreasing outer diameter due to larger specific surface area （SSA）. The SSA-normalized maximum adsorption capacity （qJSSA） and SSA-normalized adsorption coefficient （KdSSA） were strongly positively correlated with surface oxygen content, implying that lead adsorption onto MWCNTs significantly increases with the rise of oxygen content and decreases with decreasing SSA. The calculated thermodynamic parameters indicated that adsorption of lead on MWCNTs was endothermic and spontaneous. When the oxygen content of MWCNTs increased from 2.0% to 5.9%, the standard free energy （AGt） became more negative, which implied that the oxygenated functional groups increased the adsorption affinity of MWCNTs for lead. Through calculation of enthalpy （△H0）, AGO and free energy of adsorption （Ea）, lead adsorption onto MWCNTs was recognized as a chemisorption process. The chemical interaction between lead and the phenolic groups of MWCNTs could be one of the main adsorption mechanisms due to highly positive correlations between the phenolic groups and Kd/SSA or qm/SSA.

Changes of Oxygen Content in Molten TiAl Alloys as a Function of Superheat during Vacuum Induction Melting

Experimental studies on the melting process of titanium aluminum alloy have been pursued from the viewpoint of contamination.TiAl alloys were prepared with vacuum induction melting （VIM） in calcia crucibles at 1873 K and 1923 K in order to determine the behavior of the oxygen content as a function of temperature,time and frequency of power.The experiment results showed that alloys were uncontaminated except for the increasing of oxygen content which was introduced from the reaction CaO（s）=Ca（in TiAl）＋O（in TiAl）,and the standard Gibbs energy of the reaction was determined to be △G0 =274000 102.8T（J/mol）.Oxygen content increased slowly with the melting time by about 50×10-6 wt pct/min,and decreased with induction melting frequency.Lower superheat and higher melting frequency can be used to reduce oxygen content increasing rate.

Influence of refining process and utilization of different slags on inclusions, titanium yield and total oxygen content of Ti-stabilized 321 stainless steel

Ti-stabilized 321 stainless steel was prepared using an electric arc furnace, argon oxygen decarburization (AOD) furnace, ladle furnace (LF), and continuous casting processes. In addition, the effect of refining process and utilization of different slags on the evolution of inclusions, titanium yield, and oxygen content was systematically investigated by experimental and thermodynamic analysis. The results reveal that the total oxygen content (TO) and inclusion density decreased during the refining process. The spherical CaO–SiO2–Al2O3–MgO inclusions existed in the 321 stainless steel after the AOD process. Moreover, prior to the Ti addition, the spherical CaO–Al2O3–MgO–SiO2 inclusions were observed during LF refining pro-cess. However, Ti addition resulted in multilayer CaO–Al2O3–MgO–TiOx inclusions. Two different samples were prepared by conventional CaO–Al2O3-based slag (Heat-1) and -TiO2-rich CaO–Al2O3-based slag (Heat-2). The statistical analysis revealed that the density of inclusions and the -TiOx content in CaO–Al2O3–MgO–TiOx inclusions found in Heat-2 sample are much lower than those in the Heat-1 sample. Furthermore, the TO content and Ti yield during the LF refining process were controlled by using -TiO2-rich calcium aluminate synthetic slag. These results were consistent with the ion–molecule coexist-ence theory and FactSage?7.2 software calculations. When -TiO2-rich CaO–Al2O3-based slag was used, the -TiO2 activity of the slag increased, and the equilibrium oxygen content significantly decreased from the AOD to LF processes. Therefore, the higher -TiO2 activity of slag and lower equilibrium oxygen content suppressed the undesirable reactions between Ti and O.

Effect of surface Nd-rich phase and oxygen content of melt-spun flakes on formation of coarse grains in hot-pressed Nd-Fe-B magnet

Nd-Fe-B hot-pressed(HP) magnet prepared from melt-spun MQU-F flakes features coarse grains(CG)with the average size of both 200 nm(CGS) and 700 nm(CGL) at flake boundary.The grain growth at the flake boundary of Nd2 Fe14B/α-Fe composite HP magnet before and after diffusion of low-melting-point Pr82Cu18 phase was investigated,revealing the indispensable role of surface RE-rich phase of meltspun flakes in the formation of CG in HP magnet.The dominant role of surface oxygen content of melt-spun flakes in the formation of CGL has been clarified with etching method.The HP magnet prepared from the etched flakes with dramatically decreased oxygen content exhibits the CG regions merely with homoge neous equiaxed CGS at flake boundary.Consequently,the coercivity(μ0 Hc) shows significant increase while remanent magnetization(μ0 Mr) inappreciable change.Further investigation with sieving method reveals the elimination of CGL via removal of the fine Nd-Fe-B flakes smaller than 54 μm due to their much higher oxygen content,confirming the dominant role of oxygen content in the formation of CGL.The quantitative analysis on the magnetic properties of the above HP magnets reveals the monotonic increase of coercivity(μ0 Hc) and negligible change of remanent magnetization(μ0 Mr) with decreased oxygen contents of Nd-Fe-B flakes.The maximum value of coercivity(μ0 Hc) increases from2.26 to 2.47 T as the oxygen content decreases from 0.1692 wt% to 0.079 wt%.

Oxygen content and magnetic properties of composites La_(0.75)Sr_(0.25)MnO_(3±δ) dcalcined at different temperatures

The effects of the calcination temperature on the oxygen content and magnetic properties of the nano- crystalline perovskite manganite Lao.75Sro.25MnO3±δ pre- pared by the sol-gel method were investigated. The highest temperatures at which the samples were calcined were 973, 1073, 1273, and 1473 K. The X-ray diffraction （XRD） analyses indicate that all the samples have only a single phase with the R3c perovskite structure. As the calcination temperature and calcination time increase, the oxygen content in the samples increases from being deficient to being in excess of that in the stoichiometric formula. The crystallite size also increases from 23 to 283 nm. Magnetic measurements indicate that the sample calcined at 1073 K has the highest Curie temperature. This is owing to the fact that the crystallite cores of this sample have stoichiometric oxygen content. The dependence of the Curie temperature and the saturation magnetization on the calcination tem- perature are successfully explained.

Oxygen content of high ferrotitanium prepared by thermite method with different melt separation temperatures

High ferrotitanium prepared directly by the thermite method has a disadvantageously high O content(≥10 wt%)because of the short slag-metal separation time.In this study,CaO and CaF2 are added to the melt to improve the basicity of the slag and melt separation under heat preservation is performed to strengthen slag-metal separation.The thermodynamics of the step-by-step reduction process of TiO2 in the Ti-Al-Fe-Si-O system whose composition is close to the alloy after melt separation were calculated.Samples of alloys and slags before and after melt separation were systematically analyzed.The result indicates that the reaction that TiO is reduced by Al to Ti is the limited step in the reduction process of TiO2.The O content of the alloys slightly decreases with temperature from 1873 to 2023 K,which agrees with the changes in the law of deoxidation limit.It is mainly attributed to the movement of chemical reactions in the alloy melt at different temperatures and slag-metal interfacial reaction.The addition of Al2 O3-CaO-CaF2 slag and high temperature promote the removal of Al2 O3 and titanium suboxides.The minimum contents of O and Al in the alloy reach 1.84 wt% and 3.26 wt%,respectively.

火电灵活性改造中大量补水除氧技术探讨

针对灵活性改造中常遇到的大量补水工况,探讨了真空热力除氧关键技术。结合凝汽器热力除氧一般原理和关键环节,对某300MW机组的实测结果进行了分析。分析结果表明,凝汽器在切缸运行工况可以胜任大量补水除氧的任务。相较于常规的凝汽器热力除氧,机组运行大量补水时喷淋除氧布置、管束流场规划、循环水运行、抽真空设备等方面需要进行一定程度的优化。

SPA-H钢低氧出钢的生产技术实践

针对生产SPA-H钢冶炼中低氧控制出钢技术开展研究,分析了相关热力学理论及低氧出钢必要性,确定了SPA-H钢合理低氧范围应为(198~333)×10^(-6)。为实现低氧控制开展了技术改进,合理控制转炉终渣成分,合理排产,实行灵活的溅渣护炉措施;改进冶炼制度,采用“一批料”模式或留少量料模式,改进氧枪工作参数,降低平均枪位,优化枪位控制,保证低枪位拉碳时间,终点温度按照1680℃控制,碳按照0.06%~0.11%控制;采用碳—氧修正模型、转炉质谱仪等辅助手段。改进后,平均终点氧含量降低,氧含量80%控制在选定合理范围,磷、硫、碳及锰含量控制水平均有提升。

Effect of overheating-induced minor addition on Zr-based metallic glasses

Melt treatment is well known to have an important influence on the properties of metallic glasses(MGs).However,for the MGs quenched from different melt temperatures with a quartz tube,the underlying physical origin responsible for the variation of properties remains poorly understood.In the present work,we systematically studied the influence of melt treatment on the thermal properties of a Zr50Cu36Al14 glass-forming alloy and unveiled the microscopic origins.Specifically,we quenched the melt at different temperatures ranging from 1.1Tl to 1.5Tl(Tl is the liquidus temperature)to obtain melt-spun MG ribbons and investigated the variation of thermal properties of the MGs upon heating.We found that glass transition temperature,Tg,increases by as much as 36 K,and the supercooled liquid region disappears in the curve of differential scanning calorimetry when the melt is quenched at a high temperature up to 1.5Tl.The careful chemical analyses indicate that the change in glass transition behavior originates from the incorporation of oxygen and silicon in the molten alloys.The incorporated oxygen and silicon can both enhance the interactions between atoms,which renders the cooperative rearrangements of atoms difficult,and thus enhances the kinetic stability of the MGs.