It was reported that hemispheric corrosion occurred in copper tubes in an acetic acid environment. When hemispheric corrosion occurred, corrosion could easily progress if water then flowed into the copper pipe, and co...It was reported that hemispheric corrosion occurred in copper tubes in an acetic acid environment. When hemispheric corrosion occurred, corrosion could easily progress if water then flowed into the copper pipe, and countermeasures were needed. Therefore, we studied the copper corrosion caused by acetic acid. The present work investigated the relationship between the corrosion form of copper and acetic acid concentration using phosphorous-deoxidized copper, and reported that hemispherical corrosion was observed at acetic acid concentrations of 0.01 to 1 vol.% (0.002 to 0.2 mol·L<sup>-1</sup>) in the immersion test. In this study, the effects of acetic acid and phosphate on copper corrosion were examined using oxygen-free copper in immersion tests. The results suggested that different concentrations of phosphate in acetic acid solutions and the presence or absence of acetic acid and phosphate affected the corrosion of copper, resulting in different corrosion forms and corrosion progress.展开更多
One novel metal-organic framework [Cu2（L）（μ3-OH）]n（1, H3L = [1,1＇：3＇,1＇＇-terphenyl]-4,4＇＇,5＇-tricarboxylic acid） has been synthesized and characterized by single-crystal powder X-ray diffraction, IR and...One novel metal-organic framework [Cu2（L）（μ3-OH）]n（1, H3L = [1,1＇：3＇,1＇＇-terphenyl]-4,4＇＇,5＇-tricarboxylic acid） has been synthesized and characterized by single-crystal powder X-ray diffraction, IR and thermogravimetric analyses. Complex 1 crystallizes in orthorhombic crystal system, space group Pbca with a = 21.573（19）, b = 5.404（5）, c = 33.78（3） ？, C21H（12）O7Cu2, Mr = 503.39, V = 3938（6） A^3, Z = 8, Dc = 1.698 g·cm^-3, μ = 2.202 mm^-1, F（000） = 2016, 1.531〈θ〈25.009°, λ（Mo Kα） = 0.71073 A, T = 293（2） K, the final R = 0.0448 and wR = 0.1002. The structure of complex 1 is a three-dimensional（3D） framework based on infinite rod-shaped secondary building units and can be simplified as kgd topology. The gas adsorption measurements for N2, CO2, H2O, CH3OH and CH3CH2OH have been done. Fortunately, the selective sorption of CO2 over N2 was found at 195 K.展开更多
The copper consumption by the Chinese cable industry amounted to 354×104 t in 2006, taking over 70 % of the total copper consumption in China in that year. At present, making copper rod directly from recovered sc...The copper consumption by the Chinese cable industry amounted to 354×104 t in 2006, taking over 70 % of the total copper consumption in China in that year. At present, making copper rod directly from recovered scrap copper and saving copper with aluminum have become topics of general interests in the Chinese cable industry. The quality of the copper conductors in the industry is declining, resulting in sharp decrease in the rate of qualified wire and cable products. More and more copper wires are drawn from the rods made directly from scrap copper. The manufacturers know well some of the wires or rods are unqualified products though, they continue to use or produce products not complying with standards in order to make profits. Now the consumption of copper-clad-aluminum and copper-clad-steel is growing gradually. In 2006, the consumption of copper-clad-aluminum in China amounted to ca. 5×104 t. But in some applications, neither the common understanding between buyer and supplier nor the results of feasibility study are achieved in the product orientation and technical/economic feasibility in terms of saving copper with aluminum. This paper presents the status-quo, problems arisen and suggestions in terms of making copper rod directly from recovered scrap copper and saving copper with aluminum, in a view to promote these two topics of general interests to go toward a virtuous circle.展开更多
文摘It was reported that hemispheric corrosion occurred in copper tubes in an acetic acid environment. When hemispheric corrosion occurred, corrosion could easily progress if water then flowed into the copper pipe, and countermeasures were needed. Therefore, we studied the copper corrosion caused by acetic acid. The present work investigated the relationship between the corrosion form of copper and acetic acid concentration using phosphorous-deoxidized copper, and reported that hemispherical corrosion was observed at acetic acid concentrations of 0.01 to 1 vol.% (0.002 to 0.2 mol·L<sup>-1</sup>) in the immersion test. In this study, the effects of acetic acid and phosphate on copper corrosion were examined using oxygen-free copper in immersion tests. The results suggested that different concentrations of phosphate in acetic acid solutions and the presence or absence of acetic acid and phosphate affected the corrosion of copper, resulting in different corrosion forms and corrosion progress.
基金Supported by the Natural Science Foundation of Shandong Province(No.ZR2016BL01)the Talent Introduction Project of Dezhou University(No.320116)
文摘One novel metal-organic framework [Cu2（L）（μ3-OH）]n（1, H3L = [1,1＇：3＇,1＇＇-terphenyl]-4,4＇＇,5＇-tricarboxylic acid） has been synthesized and characterized by single-crystal powder X-ray diffraction, IR and thermogravimetric analyses. Complex 1 crystallizes in orthorhombic crystal system, space group Pbca with a = 21.573（19）, b = 5.404（5）, c = 33.78（3） ？, C21H（12）O7Cu2, Mr = 503.39, V = 3938（6） A^3, Z = 8, Dc = 1.698 g·cm^-3, μ = 2.202 mm^-1, F（000） = 2016, 1.531〈θ〈25.009°, λ（Mo Kα） = 0.71073 A, T = 293（2） K, the final R = 0.0448 and wR = 0.1002. The structure of complex 1 is a three-dimensional（3D） framework based on infinite rod-shaped secondary building units and can be simplified as kgd topology. The gas adsorption measurements for N2, CO2, H2O, CH3OH and CH3CH2OH have been done. Fortunately, the selective sorption of CO2 over N2 was found at 195 K.
文摘The copper consumption by the Chinese cable industry amounted to 354×104 t in 2006, taking over 70 % of the total copper consumption in China in that year. At present, making copper rod directly from recovered scrap copper and saving copper with aluminum have become topics of general interests in the Chinese cable industry. The quality of the copper conductors in the industry is declining, resulting in sharp decrease in the rate of qualified wire and cable products. More and more copper wires are drawn from the rods made directly from scrap copper. The manufacturers know well some of the wires or rods are unqualified products though, they continue to use or produce products not complying with standards in order to make profits. Now the consumption of copper-clad-aluminum and copper-clad-steel is growing gradually. In 2006, the consumption of copper-clad-aluminum in China amounted to ca. 5×104 t. But in some applications, neither the common understanding between buyer and supplier nor the results of feasibility study are achieved in the product orientation and technical/economic feasibility in terms of saving copper with aluminum. This paper presents the status-quo, problems arisen and suggestions in terms of making copper rod directly from recovered scrap copper and saving copper with aluminum, in a view to promote these two topics of general interests to go toward a virtuous circle.