Both the coarsening of Al2O3 nanoparticles and the growth of Cu nanograins of mechanically milled nanostructured Cu-5 vol.%Al2O3 composites with, and without, trace amounts of Ti during annealing at973 K for 1 h were ...Both the coarsening of Al2O3 nanoparticles and the growth of Cu nanograins of mechanically milled nanostructured Cu-5 vol.%Al2O3 composites with, and without, trace amounts of Ti during annealing at973 K for 1 h were investigated. It was found that doping with a small amount of Ti（e.g. 0.2 wt%） in a nanostructured Cu-5 vol.%Al2O3 composite effectively suppressed the coarsening of Al2O3 nanoparticles during exposure at this temperature. Further, the Ti addition also prevented the concomitant abnormal growth of the copper grains normally caused by the coarsening of the Al2O3 nanoparticles. Energy dispersive X-ray spectroscopy analysis of the Al2O3 nanoparticles in the annealed Cu-5 vol.%Al2 O3-0.2 wt%Ti sample suggested that the Ti atoms either diffused into the Al2O3 nanoparticles or segregated to the Cu/Al2O3 interfaces to form Ti-doped Al2O3 nanoparticles, which was more stable than Ti-free Al2O3 nanoparticles during annealing at high homologous temperatures.展开更多
基金supported financially by the China Scholarship Council (CSC)National Natural Science Foundation of China (Project No. 51271115)+1 种基金the Ministry of Science and Technology, China (Project No. 2012CB619600)the SJTU-UNSW Strategic Collaboration to conduct this investigation
文摘Both the coarsening of Al2O3 nanoparticles and the growth of Cu nanograins of mechanically milled nanostructured Cu-5 vol.%Al2O3 composites with, and without, trace amounts of Ti during annealing at973 K for 1 h were investigated. It was found that doping with a small amount of Ti（e.g. 0.2 wt%） in a nanostructured Cu-5 vol.%Al2O3 composite effectively suppressed the coarsening of Al2O3 nanoparticles during exposure at this temperature. Further, the Ti addition also prevented the concomitant abnormal growth of the copper grains normally caused by the coarsening of the Al2O3 nanoparticles. Energy dispersive X-ray spectroscopy analysis of the Al2O3 nanoparticles in the annealed Cu-5 vol.%Al2 O3-0.2 wt%Ti sample suggested that the Ti atoms either diffused into the Al2O3 nanoparticles or segregated to the Cu/Al2O3 interfaces to form Ti-doped Al2O3 nanoparticles, which was more stable than Ti-free Al2O3 nanoparticles during annealing at high homologous temperatures.