Weldingthermalcyclicsimulated techniquesisemployed in thestudy. By meansof analysismetalloscope, fracture morphology and impact toughness test of the sample, the effect ofweldingthermalcycle peak temperature and dualt...Weldingthermalcyclicsimulated techniquesisemployed in thestudy. By meansof analysismetalloscope, fracture morphology and impact toughness test of the sample, the effect ofweldingthermalcycle peak temperature and dualthermal cycle on the micro structure and toughnessoflow alloy high strength steel HQ100 isinvestigated.Inner fine martensitic andbainitic microstrctureisobservedby TEM.Theresultsshow that withtheincreaseof peaktem perature, grain sizesbecomelarger,theimpacttoughness drop down .Ifthermalcycleisim posed twiceand dualthermalcyclicpeaktemperatureis1275 ℃+ 750 ℃,theimpacttoughnessisatthelowest value.Alsotheimpacttoughnessagrees withthefracture morphology.展开更多
文摘Weldingthermalcyclicsimulated techniquesisemployed in thestudy. By meansof analysismetalloscope, fracture morphology and impact toughness test of the sample, the effect ofweldingthermalcycle peak temperature and dualthermal cycle on the micro structure and toughnessoflow alloy high strength steel HQ100 isinvestigated.Inner fine martensitic andbainitic microstrctureisobservedby TEM.Theresultsshow that withtheincreaseof peaktem perature, grain sizesbecomelarger,theimpacttoughness drop down .Ifthermalcycleisim posed twiceand dualthermalcyclicpeaktemperatureis1275 ℃+ 750 ℃,theimpacttoughnessisatthelowest value.Alsotheimpacttoughnessagrees withthefracture morphology.