The grain refinement of an as-cast Ti-46Al-8.5Nb-0.2W (atom fraction in %)alloy by the cyclic heat treatments was studied. The heat treatment scheme included a tempering at1250℃ and cyclic tempering at 1000 and 1200...The grain refinement of an as-cast Ti-46Al-8.5Nb-0.2W (atom fraction in %)alloy by the cyclic heat treatments was studied. The heat treatment scheme included a tempering at1250℃ and cyclic tempering at 1000 and 1200℃ three times after solution treatment at thetemperature above α phase transus followed by immediate fan cooling. The fine and homogeneousnear-γ microstructure can be obtained by this heat treatment, which causes the breakdown of as-castmicro-structure and prevents the anomalous growing of original γ phase.展开更多
The microstructure and mechanical properties of fine grained uranium prepared by equal channel angular pressing(ECAP)and subsequent intermediate heat treatment were investigated systematically by the confocal laser sc...The microstructure and mechanical properties of fine grained uranium prepared by equal channel angular pressing(ECAP)and subsequent intermediate heat treatment were investigated systematically by the confocal laser scanning microscope(CLSM),electron backscatter diffraction(EBSD)and split Hopkinson pressure bar(SHPB).The results show that the initial coarse grained uranium was refined from about 1000 to 6.5μm prepared by ECAP at 3 passes and subsequent heat treatment,and the corresponding dynamic yield strength increased from 135 to 390 MPa.For the ECAPed uranium samples,the relationship between grain size and yield strength could be described by classical Hall−Petch relationship,and the fitting Hall−Petch relationship for the fine grained uranium samples prepared by ECAP was drawn.展开更多
9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable ...9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable coarse columnar grains in weld metal whieh ean severely compromise the toughness. A new post-weld heat treatment （PWHT） is developed in the present work. Unlike the conventional processes in which the post-weld heat treatment is carried out below Ac1 , the use of temperatures above the Ac1 of 9Cr-1Mo alloy is considered. The new PWHT at a temperature above Ac1 improves the toughness of 9Cr-1Mo weld metals effectively. The improvement in toughness is mainly due to refinement and homogenization of mierostruetures. Key words展开更多
To improve the strength-toughness of 13Cr4NiMo martensitic stainless steel(13-4MSS),a thermal cyclic heat treatment(TCHT)combined with the advantage of tempering was proposed.The microstructures were characterized by ...To improve the strength-toughness of 13Cr4NiMo martensitic stainless steel(13-4MSS),a thermal cyclic heat treatment(TCHT)combined with the advantage of tempering was proposed.The microstructures were characterized by scanning electron microscopy,X-ray diffraction and electron backscattered diffraction,and the mechanical behaviors in terms of tensile properties and impact toughness were analyzed in correlation with microstructural evolution.It was found that grains and the martensitic matrix were refined by TCHT through the cyclic quenching transformation and austenite recrystallization,which was conducive to more nucleation quantity of reversed austenite during tempering.Two-sphericalcap nucleation model was used to explain the effect of refined grains of TCHT on the nucleation of reversed austenite.Grain refinement by TCHT improved the brittle fracture stress to reduce the ductile-brittle transition temperature and thus improved the cryogenic impact toughness of 13-4MSS.Reversed austenite distributed at the martensitic lath boundary enhances the crack arrest performance and increases the britle fracture stress.It is concluded that reasonable TCHT plus tempering process significantly improves the strength-toughness of 13-4MSS,reflecting the comprehensive effect of grain refinement and reversed austenite.展开更多
Grain refinement by cyclic heat treatment and deformation induced transformation technique of the refractory low-alloy steel and 12Cr1MoV was studied. Three cyclic heat treatments and a single-pass hot rolling process...Grain refinement by cyclic heat treatment and deformation induced transformation technique of the refractory low-alloy steel and 12Cr1MoV was studied. Three cyclic heat treatments and a single-pass hot rolling process by a Gleeble-1500 system were performed. The results show that the austenite grain sizes are affected by the cyclic quenching number, quencher, heating temperature before rolling, deforming tem- perature, strain and strain rate. The ferrite grain sizes are affected by the austenite grain refinement, deforming temperature, strain and the quenching cooling rate. The ferrite with grain size of around 3μm may be produced by the technique.展开更多
Two different Ti alloys were cast in a graphite mould using vacuum induction skull melting furnace. The first alloy was Ti-6Al-4V and the second was Ti-6Al-4V 0.5Si. Silicon as a grain refiner was added into Ti-6Al-4V...Two different Ti alloys were cast in a graphite mould using vacuum induction skull melting furnace. The first alloy was Ti-6Al-4V and the second was Ti-6Al-4V 0.5Si. Silicon as a grain refiner was added into Ti-6Al-4V alloy, and the effects of Si-addition on the microstructure and properties of the as-cast and swaged alloys were investigated. Hot swaging at 900 °C was performed on the cast samples and then two different thermal treatments were applied. The first treatment was done by heating the swaged samples at 1050 °C to produce fine lamella structure, while the second treatment was carried out at 1050 °C and then decreased the temperature to 800 °C for getting coarse lamella structure. An addition of 0.5% Si to Ti-6Al-4V alloy decreased the grain size of the as-cast sample from 627 to 337 μm. There was an increase in ultimate tensile strength of about 25 MPa for the as-cast Ti-6Al-4V 0.5Si alloy compared to Ti-6Al-4V due to the refinement effect caused by Si addition. A maximum ultimate tensile strength of 1380 MPa and a minimum corrosion rate （1.35×10 6 mm/a in Hank’s solution and 5.78×10 4 mm/a in NaCl solution） were reported for the heat treated fine lamella structure of Ti-6Al-4V 0.5Si alloy. The wear rate was decreased to about 50% by adding 0.5% Si at low sliding speeds and to about 73% at high sliding speeds.展开更多
基金This work was financially supported by the State Key Project for Fundamental Research Developing Plan (No. G2000067206-2)
文摘The grain refinement of an as-cast Ti-46Al-8.5Nb-0.2W (atom fraction in %)alloy by the cyclic heat treatments was studied. The heat treatment scheme included a tempering at1250℃ and cyclic tempering at 1000 and 1200℃ three times after solution treatment at thetemperature above α phase transus followed by immediate fan cooling. The fine and homogeneousnear-γ microstructure can be obtained by this heat treatment, which causes the breakdown of as-castmicro-structure and prevents the anomalous growing of original γ phase.
基金Project(51401187)supported by the National Natural Science Foundation of ChinaProjects(2014B0301046,2015B0301066)supported by the Science Development Fund of China Academy of Engineering Physics。
文摘The microstructure and mechanical properties of fine grained uranium prepared by equal channel angular pressing(ECAP)and subsequent intermediate heat treatment were investigated systematically by the confocal laser scanning microscope(CLSM),electron backscatter diffraction(EBSD)and split Hopkinson pressure bar(SHPB).The results show that the initial coarse grained uranium was refined from about 1000 to 6.5μm prepared by ECAP at 3 passes and subsequent heat treatment,and the corresponding dynamic yield strength increased from 135 to 390 MPa.For the ECAPed uranium samples,the relationship between grain size and yield strength could be described by classical Hall−Petch relationship,and the fitting Hall−Petch relationship for the fine grained uranium samples prepared by ECAP was drawn.
文摘9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable coarse columnar grains in weld metal whieh ean severely compromise the toughness. A new post-weld heat treatment （PWHT） is developed in the present work. Unlike the conventional processes in which the post-weld heat treatment is carried out below Ac1 , the use of temperatures above the Ac1 of 9Cr-1Mo alloy is considered. The new PWHT at a temperature above Ac1 improves the toughness of 9Cr-1Mo weld metals effectively. The improvement in toughness is mainly due to refinement and homogenization of mierostruetures. Key words
基金supported by Specific Research Project of Guangxi for Research Bases and Talents(Grant No.GuiKe AD19245145)Natural Science Foundation of Guangxi Province(Grant No.2018GXNSFBA281106).
文摘To improve the strength-toughness of 13Cr4NiMo martensitic stainless steel(13-4MSS),a thermal cyclic heat treatment(TCHT)combined with the advantage of tempering was proposed.The microstructures were characterized by scanning electron microscopy,X-ray diffraction and electron backscattered diffraction,and the mechanical behaviors in terms of tensile properties and impact toughness were analyzed in correlation with microstructural evolution.It was found that grains and the martensitic matrix were refined by TCHT through the cyclic quenching transformation and austenite recrystallization,which was conducive to more nucleation quantity of reversed austenite during tempering.Two-sphericalcap nucleation model was used to explain the effect of refined grains of TCHT on the nucleation of reversed austenite.Grain refinement by TCHT improved the brittle fracture stress to reduce the ductile-brittle transition temperature and thus improved the cryogenic impact toughness of 13-4MSS.Reversed austenite distributed at the martensitic lath boundary enhances the crack arrest performance and increases the britle fracture stress.It is concluded that reasonable TCHT plus tempering process significantly improves the strength-toughness of 13-4MSS,reflecting the comprehensive effect of grain refinement and reversed austenite.
文摘Grain refinement by cyclic heat treatment and deformation induced transformation technique of the refractory low-alloy steel and 12Cr1MoV was studied. Three cyclic heat treatments and a single-pass hot rolling process by a Gleeble-1500 system were performed. The results show that the austenite grain sizes are affected by the cyclic quenching number, quencher, heating temperature before rolling, deforming tem- perature, strain and strain rate. The ferrite grain sizes are affected by the austenite grain refinement, deforming temperature, strain and the quenching cooling rate. The ferrite with grain size of around 3μm may be produced by the technique.
文摘Two different Ti alloys were cast in a graphite mould using vacuum induction skull melting furnace. The first alloy was Ti-6Al-4V and the second was Ti-6Al-4V 0.5Si. Silicon as a grain refiner was added into Ti-6Al-4V alloy, and the effects of Si-addition on the microstructure and properties of the as-cast and swaged alloys were investigated. Hot swaging at 900 °C was performed on the cast samples and then two different thermal treatments were applied. The first treatment was done by heating the swaged samples at 1050 °C to produce fine lamella structure, while the second treatment was carried out at 1050 °C and then decreased the temperature to 800 °C for getting coarse lamella structure. An addition of 0.5% Si to Ti-6Al-4V alloy decreased the grain size of the as-cast sample from 627 to 337 μm. There was an increase in ultimate tensile strength of about 25 MPa for the as-cast Ti-6Al-4V 0.5Si alloy compared to Ti-6Al-4V due to the refinement effect caused by Si addition. A maximum ultimate tensile strength of 1380 MPa and a minimum corrosion rate （1.35×10 6 mm/a in Hank’s solution and 5.78×10 4 mm/a in NaCl solution） were reported for the heat treated fine lamella structure of Ti-6Al-4V 0.5Si alloy. The wear rate was decreased to about 50% by adding 0.5% Si at low sliding speeds and to about 73% at high sliding speeds.