Experimental studies on phase equilibria and liquidus temperature in the PbO-ZnO-CaO-SiO2-＂Fe2O3＂ system,with the mass ratios of CaO/SiO2=1-1.6 and Fe/SiO2= 1.3-1.7,and 40% PbO and 8% ZnO,were carried out between 12...Experimental studies on phase equilibria and liquidus temperature in the PbO-ZnO-CaO-SiO2-＂Fe2O3＂ system,with the mass ratios of CaO/SiO2=1-1.6 and Fe/SiO2= 1.3-1.7,and 40% PbO and 8% ZnO,were carried out between 1273 and 1573 K.Slags were equilibrated at 1273 to 1573 K and cooled rapidly by quenching.The XRD and SEM-EDS results showed that the slag compositions are in the franklinite primary phase field.Calcium and lead silicates are formed between 1373 and 1473 K.The Ca/Pb silicate and magnetoplumbite phases are partially formed by an incongruent reaction.The experimental and thermodynamical results showed that the liquidus increased by increasing CaO/SiO2 mass ratio and decreasing Fe/SiO2 mass ratio.展开更多
Liquidus projection usually refers to a two-dimensional projection of ternary liquidus univariant lines at constant pressure. The algorithms used in Pandat for the calculation of liquidus projection with isothermal li...Liquidus projection usually refers to a two-dimensional projection of ternary liquidus univariant lines at constant pressure. The algorithms used in Pandat for the calculation of liquidus projection with isothermal lines and invariant reaction equations in a ternary system are presented. These algorithms have been extended to multicomponent liquidus projections and have also been implemented in Pandat. Some examples on ternary and quaternary liquidus projections are presented.展开更多
文摘Experimental studies on phase equilibria and liquidus temperature in the PbO-ZnO-CaO-SiO2-＂Fe2O3＂ system,with the mass ratios of CaO/SiO2=1-1.6 and Fe/SiO2= 1.3-1.7,and 40% PbO and 8% ZnO,were carried out between 1273 and 1573 K.Slags were equilibrated at 1273 to 1573 K and cooled rapidly by quenching.The XRD and SEM-EDS results showed that the slag compositions are in the franklinite primary phase field.Calcium and lead silicates are formed between 1373 and 1473 K.The Ca/Pb silicate and magnetoplumbite phases are partially formed by an incongruent reaction.The experimental and thermodynamical results showed that the liquidus increased by increasing CaO/SiO2 mass ratio and decreasing Fe/SiO2 mass ratio.
文摘Liquidus projection usually refers to a two-dimensional projection of ternary liquidus univariant lines at constant pressure. The algorithms used in Pandat for the calculation of liquidus projection with isothermal lines and invariant reaction equations in a ternary system are presented. These algorithms have been extended to multicomponent liquidus projections and have also been implemented in Pandat. Some examples on ternary and quaternary liquidus projections are presented.
基金financial support from industrial sponsors Aurubis AG(Germany)the Australian Research Council Linkage Program+5 种基金Boliden(Sweden)Metso Outotec Oyj(Finland)Nyrstar(Australia)Kazzinc LtdGlencore(Kazakhstan)Umicore NV(Belgium)are gratefully acknowledged。