Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
The influence of cathodic pulse parameters was evaluated on plasma electrolytic oxidation(PEO)coatings grown on 7075 aluminum alloy in a silicate-based electrolyte containing potassium titanyl oxalate(PTO)using pulsed...The influence of cathodic pulse parameters was evaluated on plasma electrolytic oxidation(PEO)coatings grown on 7075 aluminum alloy in a silicate-based electrolyte containing potassium titanyl oxalate(PTO)using pulsed bipolar waveforms with various cathodic duty cycles and cathodic current densities.The coatings were characterized by SEM,EDS,and XRD.EIS was applied to investigate the electrochemical properties.It was observed that the increase of cathodic duty cycle and cathodic current density from 20%and 6 A/dm^(2) to 40%and 12 A/dm^(2) enhances the growth rate of the inner layer from 0.22 to 0.75μm/min.Adding PTO into the bath showed a fortifying effect on influence of the cathodic pulse and the mentioned change of cathodic pulse parameters,resulting in an increase of the inner layer growth rate from 0.25 to 1.10μm/min.Based on EDS analysis,Si and Ti were incorporated dominantly in the upper parts of the coatings.XRD technique merely detectedγ-Al_(2)O_(3),and there were no detectable peaks related to Ti and Si compounds.However,the EIS results confirmed that the incorporation of Ti^(4+)into alumina changed the electronic properties of the coating.The coatings obtained from the bath containing PTO using the bipolar waveforms with a cathodic duty cycle of 40%and current density values higher than 6 A/dm^(2) showed highly appropriate electrochemical behavior during 240 d of immersion due to an efficient repairing mechanism.Regarding the effects of studied parameters on the coating properties,the roles of cathodic pulse parameters and PTO in the PEO process were highlighted.展开更多
In order to improve the ability of ozone to catalyze the degradation of phenolic pollutants in wastewater,the CuO/Al2O3 catalysts was prepared by the impregnation precipitation method and an ozone catalytic oxidation ...In order to improve the ability of ozone to catalyze the degradation of phenolic pollutants in wastewater,the CuO/Al2O3 catalysts was prepared by the impregnation precipitation method and an ozone catalytic oxidation system was constructed.The actual phenolic sewage was used as the treatment object.And the reaction conditions of the system were optimized,and the treatment effect was determined,while the non-catalytic system was used as a control group.At the same time,the influence of salt and ammonia nitrogen related water quality on the system was studied.The optimal reaction conditions for the treatment of phenolic wastewater covered:a catalyst dosage of 30 g/L,an ozone flow rate of 0.3 m3/h,a pH value of 8.80,and a reaction time of 15 minutes.Under these conditions,the phenol and COD removal rates of the system reached 98.7%and 49.4%,respectively,which were by 31.3 percentage points and 16.2 percentage points higher than that of the ozonation system alone.The salt and ammonia nitrogen in the sewage can reduce the oxidation effect of the system.When the salinity reached 10%and the ammonia nitrogen content reached 13 000 mg/L,the removal rate of phenol could be reduced by about 20%.The results of this paper have a reference value for phenol wastewater treatment engineering.展开更多
The catalyst of CUOx/Al2O3 was prepared by the dipping-sedimentation method using y-Al2O3 as a supporter. CuO and Cu2O were loaded on the surface of Al2O3, characterized by X-ray diffraction （XRD） and X-ray photoele...The catalyst of CUOx/Al2O3 was prepared by the dipping-sedimentation method using y-Al2O3 as a supporter. CuO and Cu2O were loaded on the surface of Al2O3, characterized by X-ray diffraction （XRD） and X-ray photoelectron spectroscopy （XPS）. In the presence of CuOx/Al2O3, the microwave-induced chlorine dioxide （ClO2） catalytic oxidation process was conducted for the treatment of synthetic wastewater containing 100 mg/L phenol. The factors influencing phenol removal were investigated and the results showed that microwave-induced C102-CuOx/ml203 process could effectively degrade contaminants in a short reaction time with a low oxidant dosage, extensive pH range. Under a given condition （ClO2 concentration 80 mg/L, microwave power 50 W, contact time 5 latin, catalyst dosage 50 g/L, pH 9）, phenol removal percentage approached 92.24%, corresponding to 79.13% of CODcr removal. The removal of phenol by microwave-induced ClO2-CuOx/Al2O3 catalytic oxidation process was a complicated non-homogeneous solid/water reaction, which fitted pseudo-first-order by kinetics. Compared with traditional ClO2 oxidation, ClO2 catalytic oxidation and microwave-induced ClO2 oxidation, microwave-induced ClO2 catalytic oxidation system could significantly enhance the degradation efficiency. It provides an effective technology for the removal of phenol wastewater.展开更多
The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over Ni/Al2O3 catalyst on alumina support with different particle size. It is found that support particle size has significant influences ...The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over Ni/Al2O3 catalyst on alumina support with different particle size. It is found that support particle size has significant influences on physiochemical properties and catalytic activity of the resulting Ni/Al2O3 catalyst, but little influence on the selec-tivity. At a comparable amount of Ni loading, the catalytic activity of Ni/Al2O3 prepared with alumina support of smaller particle size is lower. The reduction behavior of the catalyst is a key factor in determining the catalytic activity of Ni/Al2O3 catalyst. The supported nickel catalyst 10.3Ni/Al2O3-3 improves the life span of the membrane by reducing fouling on the membrane surface compared to nano-sized nickel.展开更多
The influence of nano-A!2O3 additive on the adhesion between epoxy resin and steel substrate has been investigated. The results of tensile testing indicated that the adhesion strength was increased dramatically by add...The influence of nano-A!2O3 additive on the adhesion between epoxy resin and steel substrate has been investigated. The results of tensile testing indicated that the adhesion strength was increased dramatically by addition of Al2Os nanoparticles in epoxy resin compared with that of the unmodified resin. The highest adhesion strength was obtained with 1 wt% nano-A!2O3 added in epoxy adhesive, more than two times higher than that of the unmodified. Scanning electronic microscope (SEM) revealed that a boundary layer exists between epoxy and steel substrate, energy spectrum analysis indicates there is enrichment of the nano-A!2O3 particle. Those results confirmed that the nano-A12O3 additive was closely related to the change of interface morphology and the improvement of adhesion strength. The reason for adhesion improvement was also be discussed.展开更多
Organic substance such as solvent and resin's effect on luminescent capability of SrAl2O4:Eu2+ , Dy3+ phosphor was studied. Some organic solvents and resins were selected for experimentation. The results indicate ...Organic substance such as solvent and resin's effect on luminescent capability of SrAl2O4:Eu2+ , Dy3+ phosphor was studied. Some organic solvents and resins were selected for experimentation. The results indicate that those organic solvents will not have negative effect on the applied capability of SrAl2O4:Eu2+ , Dy3+ phosphor. Adopting the organic resins and covering method, the afterglow luminance of SrAl2O4:Eu2+ , Dy3+ phosphor was increased by 85.01% and 82.51%.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘The influence of cathodic pulse parameters was evaluated on plasma electrolytic oxidation(PEO)coatings grown on 7075 aluminum alloy in a silicate-based electrolyte containing potassium titanyl oxalate(PTO)using pulsed bipolar waveforms with various cathodic duty cycles and cathodic current densities.The coatings were characterized by SEM,EDS,and XRD.EIS was applied to investigate the electrochemical properties.It was observed that the increase of cathodic duty cycle and cathodic current density from 20%and 6 A/dm^(2) to 40%and 12 A/dm^(2) enhances the growth rate of the inner layer from 0.22 to 0.75μm/min.Adding PTO into the bath showed a fortifying effect on influence of the cathodic pulse and the mentioned change of cathodic pulse parameters,resulting in an increase of the inner layer growth rate from 0.25 to 1.10μm/min.Based on EDS analysis,Si and Ti were incorporated dominantly in the upper parts of the coatings.XRD technique merely detectedγ-Al_(2)O_(3),and there were no detectable peaks related to Ti and Si compounds.However,the EIS results confirmed that the incorporation of Ti^(4+)into alumina changed the electronic properties of the coating.The coatings obtained from the bath containing PTO using the bipolar waveforms with a cathodic duty cycle of 40%and current density values higher than 6 A/dm^(2) showed highly appropriate electrochemical behavior during 240 d of immersion due to an efficient repairing mechanism.Regarding the effects of studied parameters on the coating properties,the roles of cathodic pulse parameters and PTO in the PEO process were highlighted.
基金financially supported by the Ministry of Science and Technology of the People’s Republic of China [Grant No. 2017YFC1404605]
文摘In order to improve the ability of ozone to catalyze the degradation of phenolic pollutants in wastewater,the CuO/Al2O3 catalysts was prepared by the impregnation precipitation method and an ozone catalytic oxidation system was constructed.The actual phenolic sewage was used as the treatment object.And the reaction conditions of the system were optimized,and the treatment effect was determined,while the non-catalytic system was used as a control group.At the same time,the influence of salt and ammonia nitrogen related water quality on the system was studied.The optimal reaction conditions for the treatment of phenolic wastewater covered:a catalyst dosage of 30 g/L,an ozone flow rate of 0.3 m3/h,a pH value of 8.80,and a reaction time of 15 minutes.Under these conditions,the phenol and COD removal rates of the system reached 98.7%and 49.4%,respectively,which were by 31.3 percentage points and 16.2 percentage points higher than that of the ozonation system alone.The salt and ammonia nitrogen in the sewage can reduce the oxidation effect of the system.When the salinity reached 10%and the ammonia nitrogen content reached 13 000 mg/L,the removal rate of phenol could be reduced by about 20%.The results of this paper have a reference value for phenol wastewater treatment engineering.
基金Project supported by the National Nature Science Foundation of China(No.50678045).
文摘The catalyst of CUOx/Al2O3 was prepared by the dipping-sedimentation method using y-Al2O3 as a supporter. CuO and Cu2O were loaded on the surface of Al2O3, characterized by X-ray diffraction （XRD） and X-ray photoelectron spectroscopy （XPS）. In the presence of CuOx/Al2O3, the microwave-induced chlorine dioxide （ClO2） catalytic oxidation process was conducted for the treatment of synthetic wastewater containing 100 mg/L phenol. The factors influencing phenol removal were investigated and the results showed that microwave-induced C102-CuOx/ml203 process could effectively degrade contaminants in a short reaction time with a low oxidant dosage, extensive pH range. Under a given condition （ClO2 concentration 80 mg/L, microwave power 50 W, contact time 5 latin, catalyst dosage 50 g/L, pH 9）, phenol removal percentage approached 92.24%, corresponding to 79.13% of CODcr removal. The removal of phenol by microwave-induced ClO2-CuOx/Al2O3 catalytic oxidation process was a complicated non-homogeneous solid/water reaction, which fitted pseudo-first-order by kinetics. Compared with traditional ClO2 oxidation, ClO2 catalytic oxidation and microwave-induced ClO2 oxidation, microwave-induced ClO2 catalytic oxidation system could significantly enhance the degradation efficiency. It provides an effective technology for the removal of phenol wastewater.
基金Supported by the Special Funds for Major State Basic Research Program of China （No.2003CB615702）, the National Natural Science Foundation of China （No.20636020） and the Natural Science Foundation of Jiangsu Province （No.BK2006722）.
文摘The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over Ni/Al2O3 catalyst on alumina support with different particle size. It is found that support particle size has significant influences on physiochemical properties and catalytic activity of the resulting Ni/Al2O3 catalyst, but little influence on the selec-tivity. At a comparable amount of Ni loading, the catalytic activity of Ni/Al2O3 prepared with alumina support of smaller particle size is lower. The reduction behavior of the catalyst is a key factor in determining the catalytic activity of Ni/Al2O3 catalyst. The supported nickel catalyst 10.3Ni/Al2O3-3 improves the life span of the membrane by reducing fouling on the membrane surface compared to nano-sized nickel.
基金financially supported by the National Natural Science Foundation of China(No.50371077)
文摘The influence of nano-A!2O3 additive on the adhesion between epoxy resin and steel substrate has been investigated. The results of tensile testing indicated that the adhesion strength was increased dramatically by addition of Al2Os nanoparticles in epoxy resin compared with that of the unmodified resin. The highest adhesion strength was obtained with 1 wt% nano-A!2O3 added in epoxy adhesive, more than two times higher than that of the unmodified. Scanning electronic microscope (SEM) revealed that a boundary layer exists between epoxy and steel substrate, energy spectrum analysis indicates there is enrichment of the nano-A!2O3 particle. Those results confirmed that the nano-A12O3 additive was closely related to the change of interface morphology and the improvement of adhesion strength. The reason for adhesion improvement was also be discussed.
文摘Organic substance such as solvent and resin's effect on luminescent capability of SrAl2O4:Eu2+ , Dy3+ phosphor was studied. Some organic solvents and resins were selected for experimentation. The results indicate that those organic solvents will not have negative effect on the applied capability of SrAl2O4:Eu2+ , Dy3+ phosphor. Adopting the organic resins and covering method, the afterglow luminance of SrAl2O4:Eu2+ , Dy3+ phosphor was increased by 85.01% and 82.51%.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。