We developed a fixation method and evaluate bone regrowth in the cavities of a Ф4 mm× 8 mm titanium（Ti）tube through porous hydroxyapatite（HAP）/β-tricalcium phosphate（β-TCP）composite filling（group A）,ch...We developed a fixation method and evaluate bone regrowth in the cavities of a Ф4 mm× 8 mm titanium（Ti）tube through porous hydroxyapatite（HAP）/β-tricalcium phosphate（β-TCP）composite filling（group A）,chitosan/calcium phosphate composite filling（group B）,and HAP particle modification（group C）.After 2 and 5 months of implantation in dog tibia defects,new bone formation in the three groups was studied by histology and histomorphometry.Group A displayed the most bone regenerated area in both 2 and 5 months post-operation.The chitosan/calcium phosphate composite in group B mostly degraded 2 months after implantation,leading to fibrous tissue invasion after 5 months.By contrast,less bone formation was observed in group C.These results indicated that filling the cavities of metalprostheses with a porous HAP/β-TCP composite can be used for stable long-term fixation in clinicalsettings.展开更多
Bone tissue scaffolds based on bioactive polymer–hydroxyapatite composites have caused infections that seriously limit their extended application. In this study, we proposed a practical ion substitution method to syn...Bone tissue scaffolds based on bioactive polymer–hydroxyapatite composites have caused infections that seriously limit their extended application. In this study, we proposed a practical ion substitution method to synthesize in situ silver phosphate on the surface of a two-level, threedimensional chitosan/nano-hydroxyapatite scaffold. A release test of silver ions in a phosphate buffered saline(PBS) solution was performed to demonstrate that silver ions were released continuously from the silver phosphate during the initial 6 days of the study. The antibacterial property and cytocompatibility of the scaffolds treated with different concentrations of silver nitrate solution were assessed by in vitro assays with Escherichia coli and MC3T3-E1, respectively. The ability of the silver-containing scaffolds to induce bacteriostasis was confirmed by the inhibition zone(15 mm) and high bactericidal rate([99 %). Cell proliferation, morphology and the alkaline phosphatase activity of MC3T3-E1 cultured on the scaffold with low silver phosphate contents were comparable with those cultured on control samples.展开更多
基金Funded by the Science and Technology Planning Project of Guangdong Province(2013B010402019)the Natural Science Foundation of Guangdong Province(2015A030310345)the Medical Scientific Research Foundation of Guangdong Province(A2015352)
文摘We developed a fixation method and evaluate bone regrowth in the cavities of a Ф4 mm× 8 mm titanium（Ti）tube through porous hydroxyapatite（HAP）/β-tricalcium phosphate（β-TCP）composite filling（group A）,chitosan/calcium phosphate composite filling（group B）,and HAP particle modification（group C）.After 2 and 5 months of implantation in dog tibia defects,new bone formation in the three groups was studied by histology and histomorphometry.Group A displayed the most bone regenerated area in both 2 and 5 months post-operation.The chitosan/calcium phosphate composite in group B mostly degraded 2 months after implantation,leading to fibrous tissue invasion after 5 months.By contrast,less bone formation was observed in group C.These results indicated that filling the cavities of metalprostheses with a porous HAP/β-TCP composite can be used for stable long-term fixation in clinicalsettings.
基金supported by the National Natural Science Foundation of China(51372142,51321091)the Fundamental Research Funds of Shandong University(2014QY003-09)
文摘Bone tissue scaffolds based on bioactive polymer–hydroxyapatite composites have caused infections that seriously limit their extended application. In this study, we proposed a practical ion substitution method to synthesize in situ silver phosphate on the surface of a two-level, threedimensional chitosan/nano-hydroxyapatite scaffold. A release test of silver ions in a phosphate buffered saline(PBS) solution was performed to demonstrate that silver ions were released continuously from the silver phosphate during the initial 6 days of the study. The antibacterial property and cytocompatibility of the scaffolds treated with different concentrations of silver nitrate solution were assessed by in vitro assays with Escherichia coli and MC3T3-E1, respectively. The ability of the silver-containing scaffolds to induce bacteriostasis was confirmed by the inhibition zone(15 mm) and high bactericidal rate([99 %). Cell proliferation, morphology and the alkaline phosphatase activity of MC3T3-E1 cultured on the scaffold with low silver phosphate contents were comparable with those cultured on control samples.