Wear behavior of high strength and high conductivity Cu alloys under dry sliding

In order to study the wear behavior of different kinds of contact wires,the dry sliding wear behaviors of Cu-Sn,Cu-Ag and Cu-Mg alloys prepared by up-drawn continuous casting and followed continuous extrusion were studied.The research was tested on a block-on-ring wear tester.The results indicate that the friction coefficient is remarkably influenced by the formation of a continuous tribofilm,which consists of oxidation film.The abrasion,adhesion,oxidation and plastic deformation are observed.Oxidation and abrasion wear mechanisms dominate at the lower sliding velocity and load.The combination of oxidation and adhesion play leading roles with the increasing load and velocity.Plastic deformation is detected under higher applied load and sliding velocities.

Dry sliding friction and wear behaviors of Mg_2B_2O_5 whisker reinforced 6061Al matrix composites

The friction and wear properties of Mg2B2O5 whisker reinforced 6061Al matrix composite fabricated via power ultrasonic-stir casting process were investigated using a ball-on-disk wear-testing machine against a GCr45 steel counterface under dry sliding conditions. The reinforcements include as-received Mg2B2O5 whiskers and Mg2B2O5 whiskers coated with CuO and ZnO. The volume fraction of the composites is 2%. The relationship between the wear rate and the coefficient of friction was discussed. The results indicate that the wear rate of the Mg2B2O5 whiskers coated with ZnO reinforced aluminum matrix composites is the lowest among the materials. As the applied load and sliding speed steadily increase the coefficients of friction and wear rates of the as-received matrix alloy and the fabricated composites decrease. As the applied load and sliding speed increase, the wear mechanisms of the composites shift from a mild to a severe regime.

Effect of individual and combined additions of Al-5Ti-B,Mn and Sn on sliding wear behavior of A356 alloy

The effect of grain refiner, Mn and Sn additions on the sliding wear behavior of A356 aluminum alloys was investigated. The microstructure and worn surfaces of the studied alloys were characterized by optical microscopy（OM）, scanning electron microscopy（SEM）, and transmission electron microscopy（TEM）. The experimental results indicate that the alloy refined by Al-5Ti-B alloy exhibits equiaxed α（Al） dendrites and performs better wear resistance compared with the alloy without the grain refiner. Moreover, the addition of Mn can change the β-Al5 Fe Si phase to α-Al（Mn,Fe）Si phase and reduce the possibility of crack formation, thus improving the wear resistance. Sn added to A356 aluminum alloy forms Mg2 Sn precipitates after heat treatment. Therefore, the unrealizable precipitation hardening Mg2 Si phase and the softening β-Sn phase can reduce the hardness of the alloy, and finally reduce the wear resistance.

Dry sliding wear behavior of cast Mg-11Y-5Gd-2Zn magnesium alloy

Dry sliding wear tests on as-cast and cast＋T6 Mg-11Y-5Gd-2Zn magnesium alloys were performed using a ball-on-plate configuration. The wear rates were measured within a load range of 3-15 N, sliding speed range of 0.03-0.24 m/s, test temperature range of 25-200 °C and at a constant sliding distance of 400 m. The wear tracks, worn surfaces and wear debris of the alloys were analyzed using scanning electron microscope （SEM）. The results show that the wear rate of the alloys increases almost linearly with increasing applied load and decreases with increasing sliding speed. The wear rate of the as-cast alloy is higher than that of the cast＋T6 alloy. The amount of Mg12Y1Zn1 phase, surface oxidation and retained wear debris affect the wear rate. The dominant wear mechanisms under the test condition are abrasion and plastic deformation.

Dry sliding wear behavior and mechanism of AM60B alloy at 25-200 ℃

Dry wear tests under atmospheric conditions at 25-200 °C and loads of 12.5-300 N were performed for AM60B alloy. The wear rate increases with increasing the load; the mild-to-severe wear transitions occur under the loads of 275 N at 25 °C, 150 N at 100 °C and 75 N at 200 °C, respectively. However, as the load is less than 50 N, the wear rate at 200 °C is lower than that at 25 °C or 100 °C. In mild wear regimes, the wear mechanisms can be classified into abrasive wear, oxidation wear and delamination wear. Delamination wear prevailed as the mild-to-severe wear transition starts to occur; the delamination occurs from the inside of matrix. Subsequently, plastic-extrusion wear as severe wear prevails accompanied with the transition. The thick and hard tribo-layer postpones the mild-to-severe wear transition due to restricting the occurrence of massive plastic deformation of worn surfaces.

Dry sliding wear behavior of rheocast hypereutectic Al-Si alloys with different Fe contents

The effect of iron content on wear behavior of hypereutectic Al?17Si?2Cu?1Ni alloy produced by rheocasting process was investigated. The dry sliding wear tests were carried out with a pin-on-disk wear tester. The results show that the wear rate of the rheocast alloy is lower than that of the alloy produced by conventional casting process under the same applied load. The fine particle-likeδ-Al4(Fe,Mn)Si2 and polygonalα-Al15(Fe,Mn)3Si2 phases help to improve the wear resistance of rheocast alloys. As the volume fraction of fine Fe-bearing compounds increases, the wear rate of the rheocast alloy decreases. Moreover, the wear rate of rheocast alloy increases with the increase of applied load from 50 to 200 N. For the rheocast alloy with 3% Fe, oxidation wear is the main mechanism at low applied load (50 N). At higher applied loads, a combination of delamination and oxidation wear is the dominant wear mechanism.

Microstructure and dry sliding wear behavior of cast Al-Mg_2Si in-situ metal matrix composite modified by Nd

The microstructure and dry sliding wear behav- ior of cast Al-18 wt% MgaSi in-situ metal matrix com- posite modified by Nd were investigated. Experimental results show that, after introducing a proper amount of Nd, both primary and eutectic Mg2Si in the Al-18 wt% Mg2Si composite are well modified. The morphology of primary Mg2Si is changed from irregular or dendritic to polyhedral shape, and its average particle size is signifi- cantly decreased. Moreover, the morphology of the eutectic MgzSi phase is altered from flake-like to very short fibrous or dot-like. The wear rates and friction coefficient of the composites with Nd are lower than those without Nd. Furthermore, the addition of 0.5 wt% Nd changes the wear mechanism of the composite from the combination of abrasive, adhesive, and delamination wear without Nd into a single mild abrasion wear with 0.5 wt% Nd.

Wear mechanism for spray deposited Al-Si/SiC_p composites under dry sliding condition

Al-Si/15%SiCp(volume fraction) composites with different silicon contents were fabricated by spray deposition technique, and typical microstructures of these composites were studied by optical microscopy(OM). Dry sliding wear tests were carried out using a block-on-ring wear machine to investigate the effect of applied load range of 10-220 N on the wear and friction behavior of these composites sliding against SAE 52100 grade bearing steel. Scanning electron microscopy(SEM) and energy-dispersive X-ray microanalysis(EDAX) were utilized to examine the morphologies of the worn surfaces in order to observe the wear characteristics and investigate the wear mechanism. The results show that the wear behavior of these composites is dependent on the silicon content in the matrix alloy and the applied load. Al-Si/15%SiCp composites with higher silicon content exhibit better wear resistance in the applied load range. Under lower loads, the major wear mechanisms are oxidation wear and abrasive wear for all tested composites. Under higher loads, severe adhesive wear becomes the main wear mechanisms for Al-7Si/15%SiCp and Al-13Si/15%SiCp composites, while Al-20Si/15%SiCp presents a compound wear mechanism, consisting of oxidation, abrasive wear and adhesion wear.

Dry sliding wear behavior of Al_2O_3 fiber and SiC particle reinforced aluminium based MMCs fabricated by squeeze casting method

Al2O3 fiber （Al2O3f） and SiC particle （SiCp） hybrid metal matrix composites （MMCs） were fabricated by squeeze casting method.The tests were carried out using a pin-on-disk friction and wear tester by sliding these pin specimens at a constant speed of 0.36 m/s （570 r/min） against a steel counter disk at room temperature,100 C and 150 C,respectively.To observe the wear characteristics and investigate the wear mechanism,the morphologies of the worn surfaces and specific wear rate were analyzed by using scanning electron microscope （SEM） and Arrhenius plots.Moreover,the effects of fiber orientation and hybrid ratio were discussed.

Dry sliding wear behavior of AA6061/ZrB_2 in-situ composite

The dry sliding wear behavior of AA6061/ZrB2 in-situ composite prepared by the reaction of inorganic salts K2ZrF6 and KBF4 with molten aluminum was investigated.An attempt was made to develop a mathematical model to predict the wear rate of AA6061/（0-10%） ZrB2 in-situ composites.Four-factor,five-level central composite rotatable design was used to minimize the number of experiments.The factors considered are sliding velocity,sliding distance,normal load and mass fraction of ZrB2 particles.The effect of these factors on the wear rate of the fabricated composite was analyzed and the predicted trends were discussed by observing the wear surface morphologies.The in-situ formed ZrB2 particles enhance the wear performance of the composite.The wear rate of the composite bears a proportional relationship with the sliding velocity,sliding distance and normal load.

Effect of SiC content on dry sliding wear, corrosion and corrosive wear of Al/SiC nanocomposites

The corrosion, corrosive wear and dry sliding wear of nanocomposites, are extremely complicated and involve various chemical, physical anbd mechanical factors. The aim of this work is to investigate the effects of nanosized SiC content on the hardness, dry sliding wear, corrosion and corrosive wear of Al/SiC nanocomposites synthesized by mechanical milling cold pressing and hot extrusion. The corrosion resistance of these composites in 3%NaCl solution was investigated by electrochemical polarization testing and their dry sliding as well as corrosive wear resistance in the same solution was evaluated using a pin-on-disc tester. The microstructures of the samples and their worn surfaces were examined using scanning electron microscopy. It was shown that the dry sliding wear and corrosion resistance of these nanocomposites were improved with the increase of SiC content. It was concluded that due to the lubrication effect of the solution, both the friction coefficient and frictional heat that might soften the material were reduced. In addition, the improved strength of the nanocomposites combined with their better corrosion resistance contributed to their increased corrosive wear resistance, compared with the base alloy. The prominent wear mechanism in the unreinforced alloy was adhesive wear, in the Al/SiC nanocomposites, the wear mechanism changed to abrasive.

Microstructure and dry sliding wear behavior of Cu-Sn alloy reinforced with multiwalled carbon nanotubes

Multiwalled carbon nanotubes （MWCNTs） reinforced Cu-Sn alloy based nanocomposite was developed by powder metallurgy route. The mass fraction of CNTs was varied from 0 to 2% in a step of 0.5%. The developed nanocomposites were subjected to density, hardness, electrical conductivity, and friction and wear tests. The results reveal that the density of nanocomposite decreases with the increase of the mass fraction of CNTs. A significant improvement in the hardness is noticed in the nanocomposite with the addition of CNTs. The developed nanocomposites show low coefficient of friction and improved wear resistance when compared with unreinforced alloy. At an applied load of 5 N, the coefficient of friction and wear loss of 2%CNTs reinforced Cu-Sn alloy nanocomposite decrease by 72% and 68%, respectively, compared with those of Cu-Sn alloy. The wear mechanisms of worn surfaces of the composites are reported. In addition, the electrical conductivity reduces with the increase of the content of CNTs.

Sliding wear behavior of magnetorheological fluid for brass with and without magnetic field

A pin-on-disc wear apparatus was used to carry out the tribological experiment of brass to investigate the effect of a magnetorheological （MR） fluid on the interfacial surface with and without magnetic field. A series of tests were performed at the loads of 20-100 N and rotating speeds of 127-425 r/min for 2 h. The friction coefficient and wear rate were monitored by the wear apparatus, while the microstructures of the worn surfaces were observed by scanning electron microscope （SEM）. In addition, the chemical composition of worn surfaces was analyzed by energy dispersive X-ray spectroscopy （EDS）. Test results show different friction and wear performance of the MR fluid with and without magnetic field. At the same time, the effects of various normal loads and rotating speeds on the tribological behavior were investigated. Through the investigation of the morphologies of the wom surfaces under the magnetic field, it is found that the MR particles are clearly evident on the wom surface and the plastic flow of ridges causes the lateral extrusion. This directly indicates that abrasive wear is the predominant wear mechanism observed with MR fluid.

Dry sliding wear behavior of Ti-6Al-4V alloy in air

The dry sliding wear properties of Ti-6Al-4V alloy sliding against GCr15 steel under different velocities(between 0.2 and 1.2 m/s)and applied loads(from 30 to 90 N)were tested using a pin on disk tester in air. The wear occurred on both surfaces of the tested couplings. The wear rate of the Ti-6Al-4V alloy ranged from 23.0 to 123.8 mg/km. The wear of Ti-6Al-4V samples was in severe wear. The wear rate of Ti-6Al-4V samples increased with the increasing of load and shows a minimum on the curves of wear rate versus sliding velocity. SEM morphologies of worn surfaces and debris were observed. Phases in the debris were analyzed by means of XRD spectra.

Experimental study ofcasing wear under impact-sliding conditions

Theoretical analysis and field monitoring show that lateral vibration has very important effect on casing wear in deep & ultra-deep well drilling. The wear mechanism of casing under impact-sliding work conditions has been investigated and many experiments have been completed with a newly developed full-scale casing wear test machine. Test results present that adhesion wear, contact fatigue, and grinding abrasion are the main wear mechanisms under impact-sliding test conditions. The friction coefficient and linear wear rate of the casing rise obviously with an increase in impact load. And the larger the impact load, the rougher the worn surface of the casing. The linear wear rate decreased slightly but the average friction coefficient increased slightly with an increase in impact frequency under an impact load of 2,500 N. Both the linear wear rate of the casing and the average friction coefficient increased substantially with an increase in impact frequency under an impact load of 4,000 N. Under lower impact load conditions, grinding abrasion and contact fatigue are the main mechanisms of casing wear; under higher impact load conditions, adhesion wear and contact fatigue are the main mechanisms of casing wear.

Fractal identification of wear debris group in sliding wear process

Fractal geometry was used to describe the distribution characteristics of wear debris group collected from pin-on-disc wear tester under dry friction conditions, and experimental study and theoretical analysis were made for the distribution features of wear debris group. It was found that the wear debris size distribution conforms to the fractal distribution law. Two numerical parameters, fractal dimension D and scale coefficient C, were defined with their geometric and tribological meanings and calculating methods given. It was discovered that these two parameters can be used to describe the variation law of wear status, which provide the basis for diagnosis and prognosis of tribological systems.

Effect of solidification process parameters on dry sliding wear behavior of AlNiBi alloy

As-cast samples of the Al-3wt.%Ni-lwt.%Bi alloy resulting from the horizontal directional solidification process were subjected to the micro-abrasive wear test.The effects of the solidification thermal and microstructural parameters,such as the growth and cooling rates and the cellular and primary dendritic spacings(VL and TR;λ1 and λc;respectively),were evaluated in the wear resistance of the investigated alloy.The tribological parameters analyzed were the wear volume and rate(Vw and Rw).The solidification experiments and the wear tests were carried out by means of a water-cooled horizontal directional solidification device and a rotary-fixed ball wear machine,respectively.The results show lower Vw and Rw values correspond to finer microstructures and the Vw dependence on λ1 is characterized by an experimental mathematical equation.A better distribution of Bi soft droplets and Al3Ni hard intermetallic particles is observed within the finer interdendritic region and,in consequence,the better wear resistance is achieved in as-cast samples with dendritic morphology rather than cellular morphology.A transition of wear mechanism from adhesive to abrasive is observed.

Microstructural characterization and dry sliding wear behavior of spark plasma sintered Cu-YSZ composites

In the present study, yttria stabilized zirconia （YSZ） reinforced Cu matrix composite specimens were produced by spark plasma sintering （SPS）. For comparison, pure Cu specimen was also produced in the same conditions. The effect of particles content on microstructure, relative density, electrical conductivity, and Vickers hardness was evaluated. The pin-on-disk test was also performed to determine dry sliding wear behavior of specimens under different wear conditions. After sliding wear tests, the worn surfaces were examined by field emission scanning electron microscopy （FE-SEM）. Microstructural study showed satisfactory distribution of reinforcement particles in copper matrix. The relative density up to 95%was obtained for all specimens. By increasing YSZ content from 0 to 5% （volume fraction）, the electrical conductivity of specimens decreased from 99.2%IACS to 65%IACS, correspondingly. The hardness of Cu-5%YSZ composite specimen was two times greater than that of pure copper. The volume loss and wear rate of pure Cu specimen were 1.48 mm^3 and 1.5±10^-3 mm^3/m under 50 N applied load and 1000 m sliding distance. However, for composite containing 5% YSZ particles, these values dropped to 0.97 mm^3 and 0.9±10^-3 mm^3/m, respectively. Moreover, the friction coefficient of specimens was changed from 0.6 to 0.4. The worn surface and debris observation indicate local plastic deformation and delamination as dominant wear mechanisms for pure copper, while oxidation and ploughing for composite specimen. Accordingly, it can be concluded that the Cu-YSZ composite could be a good candidate for the electrical contact applications in relays, contactors, switches and circuit breakers requiring good electrical and thermal conductivity and capability to resist wearing.

Influence of Heat Treatment on Microstructure and Sliding Wear Behavior of Fe-Al/WC Composite Coatings

An experimental study has been carried out to investigate the influence of heat treatment at 300 ℃,450 ℃,550 ℃,650 ℃ and 800 ℃ on the microstructure and sliding wear behavior of Fe Al/WC intermetallic composite coatings produced by high velocity arc spraying (HVAS) and cored wires. The result shows, the main phases in both as sprayed and heat treated Fe Al/WC composite coatings are iron aluminide intermetallics (Fe 3Al+FeAl) and α as well as a little oxide (Al 2O 3) and carbides (WC, W 2C, Fe 2W 2C and Fe 6W 6C). After heat treated at 450-650 ℃, dispersion strengthening of Fe 2W 2C and Fe 6W 6C will lead to a rise in microhardness of the coatings. The microhardness is likely to be the most important factor which influences the sliding wear behavior of the coatings. Increasing the microhardness through heat treatment will improve the sliding wear resistance of the Fe Al/WC composite coatings.

Structure and sliding wear behavior of 321 stainless steel/Al composite coating deposited by high velocity arc spraying technique

A typical 321 stainless steel/aluminum composite coating (321/Al coating) was prepared by high velocity arc spraying technique (HVAS) with 321 stainless steel wire as the anode and aluminum wire as the cathode. The traditional 321 stainless steel coating was also prepared for comparison. Tribological properties of the coatings were evaluated with the ring-block wear tester under different conditions. The structure and worn surface of the coatings were analyzed by scanning electron microscopy(SEM), X-ray diffractometry(XRD) and energy dispersion spectroscopy(EDS). The results show that, except for aluminum phase addition in the 321/Al coating, no other phases are created compared with the 321 coating. However, due to the addition of aluminum, the 321/Al coating forms a type of "ductile/hard phases inter-deposited" structure and performs quite different tribological behavior. Under the dry sliding condition, the anti-wear property of 321/Al coating is about 42% lower than that of 321 coating. But under the oil lubricated conditions with or without 32 h oil-dipping pretreatment, the anti-wear property of 321/Al coating is about 9% and 5% higher than that of 321 coating, respectively. The anti-wear mechanism of the composite coating is mainly relevant to the decrease of oxide impurities and the strengthening action resulted from the "ductile/hard phases inter-deposited" coating structure.