Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long li...Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long line, complex weather and geology features. In this paper, the welding cold cracking susceptibility of domestic X 70 pipeline steel adopted by the project, which is one of the most interesting questions of welding quality about petrol pipeline, was studied by means of oblique Y groove cracking test. The crack ratio of surface and section was tested under the conditions of different welding materials and preheat temperature .The thickness of plate steel was 14.7 mm and 10.3 mm . The results reveal that X 70 pipeline steel has good crack resistance. The research has important value for the construction of large scale pipeline engineering and the application of domestic X 70 pipeline steel.展开更多
Hydrogen induced cracking(HIC) behaviors of a high strength pipeline steel with three different microstructures, granular bainite & lath bainite(GB + LB), granular bainite & acicular ferrite(GB + AF), and qu...Hydrogen induced cracking(HIC) behaviors of a high strength pipeline steel with three different microstructures, granular bainite & lath bainite(GB + LB), granular bainite & acicular ferrite(GB + AF), and quasi-polygonal ferrite(QF), were studied by using corrosion experiment based on standard NACE TM0284. The HIC experiment was conducted in hydrogen sulfide(H_2S)-saturated solution. The experimental results show that the steel with GB + AF and QF microstructure present excellent corrosion resistance to HIC, whereas the phases of bainite lath and martensite/austenite in LB + GB microstructure are responsible for poor corrosion resistance. Compared with ferrite phase, the bainite microstructure exhibits higher strength and crack susceptibility of HIC. The AF + GB microstructure is believed to have the best combination of mechanical properties and resistance to HIC among the designed steels.展开更多
文摘Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long line, complex weather and geology features. In this paper, the welding cold cracking susceptibility of domestic X 70 pipeline steel adopted by the project, which is one of the most interesting questions of welding quality about petrol pipeline, was studied by means of oblique Y groove cracking test. The crack ratio of surface and section was tested under the conditions of different welding materials and preheat temperature .The thickness of plate steel was 14.7 mm and 10.3 mm . The results reveal that X 70 pipeline steel has good crack resistance. The research has important value for the construction of large scale pipeline engineering and the application of domestic X 70 pipeline steel.
基金supported by the National High Technology Research and Development Program of China(Grant No.2015AA03A501)the National Natural Science Foundation of China(Grant No.51274063)
文摘Hydrogen induced cracking(HIC) behaviors of a high strength pipeline steel with three different microstructures, granular bainite & lath bainite(GB + LB), granular bainite & acicular ferrite(GB + AF), and quasi-polygonal ferrite(QF), were studied by using corrosion experiment based on standard NACE TM0284. The HIC experiment was conducted in hydrogen sulfide(H_2S)-saturated solution. The experimental results show that the steel with GB + AF and QF microstructure present excellent corrosion resistance to HIC, whereas the phases of bainite lath and martensite/austenite in LB + GB microstructure are responsible for poor corrosion resistance. Compared with ferrite phase, the bainite microstructure exhibits higher strength and crack susceptibility of HIC. The AF + GB microstructure is believed to have the best combination of mechanical properties and resistance to HIC among the designed steels.